Method for preparing nano cobalt ferrite

A technology of nano-cobalt and ferrite, which is applied in the direction of nanotechnology, nanotechnology, chemical instruments and methods, and can solve problems such as poor crystallization

Inactive Publication Date: 2014-07-02
LANZHOU UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

M.Rajendran et al. gave a method for co-precipitating iron salt and cobalt salt solution with NaOH and H2O2 mixed solution to prepare cobalt ferrite, but this method has poor crystallization at 20°C. See M.Rajendran, R.C. Pullar, A.K.Bhattacharya, D.Das S.N.Chintalapudi, C.K.Majumdar, Magnetic properties of nanocrystalline CoFe2O4 powders prepared at room temperature: variation with crystallitesize, Journal of Magnetism and Magnetic Materials, 232 (2001), 71–83

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing nano cobalt ferrite
  • Method for preparing nano cobalt ferrite
  • Method for preparing nano cobalt ferrite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) Weigh 0.1784g (0.00066mol) FeCl with a molar ratio of 2:1 3 .6H 2 O and 0.07815 g (0.00033 mol) CoCl 2 .6H 2 O, dissolved in 50ml of distilled water, fully stirred to dissolve, the metal ion concentration is 0.02M.

[0021] 2) Weigh 1.6g (0.04mol) NaOH and dissolve it in 20ml distilled water, the NaOH concentration is 2M. After stirring evenly, add N dropwise to it 2 h 4 .H 2 O (85% hydrazine hydrate) 10ml , N 2 h 4 .H 2 O concentration is 5.6 mol / L.

[0022] 3) at room temperature Down (20 o C) Stir rapidly under the condition, slowly drop the mixed solution of alkali and hydrazine hydrate prepared in step 2) into the solution of Fe and Co salts, and react for 2 hours.

[0023] 4) Fully wash the black precipitate produced by the reaction in step 3) with distilled water to a pH value of about 7, then wash with ethanol 2 to 3 times, and then dry naturally or in vacuum to obtain CoFe2O4 particles.

[0024] attached figure 1The X-ray diffraction spectrum...

Embodiment 2

[0026] 1) Weigh 0.1784g (0.00066mol) FeCl with a molar ratio of 2:1 3 .6H 2 O and 0.07815 g (0.00033 mol) CoCl 2 .6H 2 O, dissolved in 50ml of distilled water, fully stirred to dissolve, the metal ion concentration is 0.02M.

[0027] 2) Weigh 1.6g (0.04mol) NaOH and dissolve it in 20ml distilled water, the NaOH concentration is 2M. After stirring evenly, add N dropwise to it 2 h 4 .H 2 O (85% hydrazine hydrate) 10ml , N 2 h 4 .H 2 O concentration is 5.6 mol / L.

[0028] 3) at 40 o C Stir rapidly under water bath conditions, slowly add the mixed solution of alkali and hydrazine hydrate prepared in step 2) dropwise into the Fe and Co salt solution, and react for 2 hours.

[0029] 4) Fully wash the black precipitate produced by the reaction in step 3) with distilled water to a pH value of about 7, then wash with ethanol 2 to 3 times, and then dry naturally or in vacuum to obtain CoFe2O4 particles. The average particle size is 9nm, it is superparamagnetic at room tem...

Embodiment 3

[0032] 1) Weigh 0.1784g (0.00066mol) FeCl with a molar ratio of 2:1 3 .6H 2 O and 0.07815 g (0.00033 mol) CoCl 2 .6H 2 O, dissolved in 50ml of distilled water, fully stirred to dissolve, the metal ion concentration is 0.02M.

[0033] 2) Weighing 1.2g (0.03mol) NaOH was dissolved in 20ml of distilled water, the NaOH concentration was 1.5M. After stirring evenly, add N dropwise to it 2 h 4 .H 2 O (85% hydrazine hydrate) 14ml, N 2 h 4 .H 2 O concentration is 7mol / L.

[0034] 3) at 20 o C Stir rapidly under water bath conditions, and slowly drop the mixed solution of alkali and hydrazine hydrate prepared in step 2) into the solution of Fe and Co salts, and react for 3 hours.

[0035] 4) Fully wash the black precipitate produced by the reaction in step 3) with distilled water to a pH value of about 7, then wash with ethanol 2 to 3 times, and then dry naturally or in vacuum to obtain CoFe2O4 particles. The average particle size is 3nm, it is superparamagnetic at room ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-powder method capable of preparing spinel-structured nano-cobalt ferrite CoFe2O4 at relatively low temperature. The preparation method of the nano-cobalt ferrite CoFe2O4 with spinel structure of the present invention is: after weighing iron trichloride and cobalt dichloride in proportion, mix and prepare aqueous solution A, prepare NaOH or KOH alkali solution, stir to Add N2H4.H2O dropwise to obtain solution B; quickly stir the aqueous solution A obtained in step 1 at 20~40°C, and slowly add the mixed solution B prepared in step 2) into aqueous solution A to react to obtain black Precipitation of cobalt ferrite CoFe2O4 powder with spinel structure.

Description

technical field [0001] The invention relates to a preparation method of nano-cobalt ferrite powder, in particular to a nano-cobalt ferrite CoFe with spinel structure 2 o 4 method of preparation. Background technique [0002] Spinel-type cobalt ferrite is a magnetic material with excellent performance, which has many advantages such as high saturation magnetization, excellent corrosion resistance and wear resistance. It has been widely used in magnetic recording, magnetic elements and magnetic fluids. In addition, due to its high resistivity and significant magneto-optical Kerr effect, it has great application potential in wave-absorbing materials and new magneto-optical recording materials. See: [1] "Cobalt Ferrite Preparation and Research", Zhang Chao, Master's Degree Thesis of Henan University; [2] Cobalt Ferrite Micropowder Chemical Preparation Process and Its Absorbing Performance, Che Renchao, Li Yongqing, etc. , "Aerospace Materials Technology", 1999, No. 6; [3] Sy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/00B82Y30/00C04B35/26
Inventor 张旭东
Owner LANZHOU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com