Complex-calcium-based tetrapolyurea lubricating grease and preparation method thereof
A technology of calcium-based tetrapolyurea grease and composite calcium-based grease, which is applied in lubricating compositions, petroleum industry, thickeners, etc., can solve the problems of poor comprehensive performance of calcium-based polyurea grease, and achieve excellent Comprehensive performance, avoid strong volatilization, overcome hardening effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0018] The present invention provides a preparation method of complex calcium-based tetrapolyurea grease, which comprises the following steps:
[0019] (1) In the presence of lubricating base oil, the calcium hydroxide, higher fatty acid and dibasic aromatic acid are contacted and reacted, and the mixture obtained after the reaction is heated and dehydrated, and then the temperature is lowered to 70-80°C to obtain a complex calcium-based grease ;
[0020] (2) Add diisocyanate and diamine successively to the compound calcium-based grease, mix and contact for at least 5 minutes, then add monoamine, heat up to 100-120°C for contact reaction, and heat up the resulting mixture for refining , Wherein the molar ratio of the amount of diisocyanate, diamine and monoamine is (1.9-2.1):1:(1.9-2.1).
[0021] According to the method of the present invention, in step (1), the temperature of the grease obtained after dehydration is lowered to 70-80°C, and in step (2), the monoamine is added after ...
Embodiment 1
[0055] This example is used to illustrate the composite calcium-based tetrapolyurea grease of the present invention and its preparation method.
[0056] Raw material component: naphthenic oil (purchased from China National Offshore Oil Corporation, viscosity at 100°C is 12mm 2 / s): 835g; terephthalic acid: 30g; Ca(OH) 2 :22g; 12-hydroxystearic acid (purchased from Tongliao Weining Chemical Co., Ltd.): 60g; octadecylamine (purchased from ACROS company): 31.87g; ethylenediamine: 3.56g; 4,4'-two Phenylmethane diisocyanate (MDI): 29.58 g; tungsten disulfide: 8 g; selenium disulfide: 12 g; fluorinated graphite: 10 g; diisooctyl diphenylamine: 8 g; zinc naphthenate: 10 g.
[0057] Mix 500g of naphthenic oil with 60g of 12-hydroxystearic acid and 30g of terephthalic acid, stir evenly, heat to 80°C, add dropwise a lime milk solution containing 22g of calcium hydroxide, and quickly stir and saponify for 60 minutes. The temperature is raised to 105°C, and after the water is removed, the temp...
Embodiment 2
[0067] This example is used to illustrate the composite calcium-based tetrapolyurea grease of the present invention and its preparation method.
[0068] The composite calcium-based tetrapolyurea grease was prepared according to the method of Example 1, except that the same molar amount of isophthalic acid was used instead of terephthalic acid to obtain the composite calcium-based tetrapolyurea grease.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com