Antibacterial and mildew-resistant superfine-fiber synthetic leather, preparation method and products thereof

A microfiber, antibacterial and antifungal technology, applied in the direction of synthetic resin layered products, chemical instruments and methods, layered products, etc., can solve the problems of sterilization, long antibacterial response time, product discoloration, etc., and achieve high practical value , control production cost, good killing effect

Inactive Publication Date: 2013-08-28
JINJIANG MINGAO TEXTILE SCI & TECH
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, inorganic antibacterial agents also have the problem of long bactericidal and antibacterial response time, which may easily cause product discoloration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] PA / COPET type fixed island non-woven fabric, its unit weight is 240g / m 2 , its apparent density is 0.30g / m 3 ; 100 parts of water-based polyurethane slurry, the water-based polyurethane slurry is DG-3020, and its dry film 100% modulus is 20KG / cm 2 , solid content 20% by weight, its viscosity is 6Pa.s, 3 parts of sodium dodecylbenzenesulfonate, 2 parts of stearic acid amine and 50 parts of water, stir with high-speed mixer, make the density of mixed slurry be 300g / L; impregnate the non-woven fabric with the mixed slurry in the impregnation tank, the impregnation amount is 400-550g / m 2 , keep 30-60% of the cells; then solidify in the coagulation tank with an aqueous coagulation solution with a pH value of 5 and a temperature of 20°C, wash in the washing tank, and dry in an infrared drying oven to obtain the base fabric;

[0025] 10 parts of silver ion-loaded montmorillonite (Andimei, silver ion content is 0.2wt% of the carrier, Beijing Chonggao Nano Technology Co., Ltd...

Embodiment 2

[0044] PA / COPET type fixed island non-woven fabric, its unit weight is 400g / m 2 , its apparent density is 0.35 / m 3 ; 100 parts of water-based polyurethane slurry, the dry film of DG-3100 slurry 100% tensile strength is 100KG / cm 2 , solid content is 30% by weight, and its viscosity is 16Pa.s, adds 4 parts of foaming agents of sodium sulfosuccinate, 2 parts of foam stabilizer ammonium stearates, 150 parts of water and 3 parts of water-based colorants (Shanghai Si Lianhei G-55), and the high-speed mixer stirs evenly, so that the density of the mixed slurry is 550g / L;

[0045] 10 parts of silver ion-loaded montmorillonite (Andimei, silver ion content is 0.2wt% of the carrier, Beijing Chonggao Nano Technology Co., Ltd.) with a particle size of 100nm, sodium thiosulfate (Zibo Yiren Chemical Technology Co., Ltd.) 0.05 parts, fully wetted and dispersed in 100 parts of dimethylformamide (DMF solvent), stirred and ground. Add 0.06 parts of isopropyl tri-isooctanoyl-titanate (Nanjing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides an antibacterial and mildew-resistant superfine-fiber synthetic leather, a preparation method and products thereof. The antibacterial and mildew-resistant superfine-fiber synthetic leather comprises polyurethane resin and a composite antibacterial agent uniformly dispersed in the polyurethane. The preparation method comprises adding a foaming agent, a foam stabilizer, water and an aqueous coloring agent into an aqueous anionic polyurethane impregnated slurry, uniformly stirring by using a high-speed mixer to prepare into slurry, fully wetting and dispersing an inorganic antiseptic, an organic antiseptic, a compatibility treating agent and an anti-discoloration agent in dimethylformamide, stirring, grinding, adding the composite antibacterial agent with an adjusted viscosity into polyurethane synthetic leather molding slurry, uniformly mixing, and molding. The antibacterial and mildew-resistant superfine-fiber synthetic leather can be widely applied in shoes, sofa, clothes leather, case leather and leather for furniture and interior decoration.

Description

technical field [0001] The invention relates to a method for manufacturing superfine fiber synthetic leather, in particular to a method for preparing antimicrobial and mildew-proof superfine fiber synthetic leather. Background technique [0002] At present, polyurethane synthetic leather has been used in various fields of people's life, and there are various varieties. Among them, the high-grade microfiber synthetic leather has developed rapidly in recent years due to its advantages in physical properties and the appearance of imitation leather. The traditional wet production process of superfine fiber synthetic leather is to impregnate non-woven fabric with solvent-based polyurethane as the impregnating slurry, then solidify in DMF (dimethylformamide) aqueous solution, extract it from a hot toluene tank, wash and dry, Among them, a large amount of DMF and toluene are used, and the solvents that cannot be fully recovered are discharged in the form of gas and waste water, pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/00B32B27/18B32B27/40C08L75/04C08K9/12C08K5/47C08K3/30
Inventor 杨小波
Owner JINJIANG MINGAO TEXTILE SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap