Impermeable white unsaturated polyester furniture coating

A furniture coating, unsaturated technology, applied in the direction of polyester coatings, coatings, etc., can solve problems such as dullness, poor hiding power, and affect the quality of topcoat coatings, and achieve uniform gloss

Inactive Publication Date: 2013-10-23
展辰新材料集团股份有限公司 +4
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the polyurethane sealing primer is not completely sealed or is pierced during polishing, it is easy to penetrate when it is coated with white unsaturated polyester furniture paint, and the penetration parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Formula: 50 parts of unsaturated polyester resin, 0.02 parts of polymerization inhibitor, 10 parts of talc powder, 20 parts of heavy calcium carbonate, 10 parts of titanium dioxide, 3 parts of zinc stearate, 2 parts of toluene, 2 parts of ethyl acetate, 0.5 parts of nitrocellulose; anti-settling agent: 0.3 parts of A200 fumed silica; defoamer: 0.3 parts of EFKA2720 non-organic silicon defoamer; leveling agent: 0.3 parts of EFKA3777 fluorine-modified acrylate leveling agent; dispersant : 0.3 parts of C-600 dispersant; stabilizer: 0.2 parts of DVP stabilizer.

[0037] Production method: put in unsaturated polyester resin → add toluene → add polymerization inhibitor → disperse uniformly at medium speed → add anti-sedimentation agent, defoamer, leveling agent, dispersant, nitrocellulose, stabilizer in sequence → disperse at medium speed 5 minutes → add titanium dioxide, talc powder, heavy calcium carbonate, zinc stearate → disperse at a medium speed for 30 minutes until the...

Embodiment 2

[0040] Formula: 40 parts of unsaturated polyester resin, 0.02 parts of polymerization inhibitor, 10 parts of titanium dioxide, 5 parts of talcum powder, 30 parts of heavy calcium carbonate, 3 parts of zinc stearate, 5 parts of toluene, 5 parts of ethyl acetate; Precipitating agent: 0.4 parts of A200 fumed silica; defoaming agent: 0.3 parts of EFKA2720 non-organic silicon defoaming agent; leveling agent: 0.3 parts of EFKA3777 fluorine-modified acrylate leveling agent; dispersing agent: C-600 dispersing agent 0.3 parts; 1.5 parts of nitrocellulose; stabilizer: 0.3 parts of DVP stabilizer.

[0041] Production method: with embodiment 1;

[0042] The appearance of the obtained unsaturated polyester furniture coating is: white viscous liquid.

Embodiment 3

[0044] Formula: 45 parts of unsaturated polyester resin, 8 parts of titanium dioxide, 0.02 parts of polymerization inhibitor, 10 parts of talcum powder, 25 parts of heavy calcium carbonate, 3 parts of zinc stearate, 2 parts of toluene, 3 parts of ethyl acetate; Anti-settling agent: 0.5 parts of A200 fumed silica; defoamer: 0.3 parts of EFKA2720 non-organic silicon defoamer; leveling agent: 0.2 parts of EFKA3777 fluorine-modified acrylate leveling agent; dispersant: C-600 dispersion 0.2 part of agent; 1 part of nitrocellulose; stabilizer: 0.3 part of DVP stabilizer.

[0045] Production method: with embodiment 1;

[0046] The appearance of the obtained unsaturated polyester furniture coating is: white viscous liquid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses impermeable white unsaturated polyester furniture coating. The impermeable white unsaturated polyester furniture coating comprises a main agent part A, a part B containing cobalt iso-octoate and a part C containing methyl ethyl ketone peroxide, wherein the part A comprises the following components in parts by weight: 40 to 50 parts of unsaturated polyester resin, 0.01 to 0.03 part of a polymerization inhibitor, 7 to 10 parts of titanium dioxide, 25 to 35 parts of an inorganic filler, 3 to 5 parts of zinc stearate, 4 to 10 parts of a solvent, 0.3 to 0.5 part of an anti-settling agent, 0.1 to 0.3 part of a defoaming agent, 0.2 to 0.5 part of a flatting agent, 0.1 to 0.3 part of a dispersing agent, 0.5 to 1.5 parts of nitrocotton and 0.1 to 0.3 part of a stabilizing agent. The impermeable white unsaturated polyester furniture coating adopts nitrocotton, so the technical problems that the coating is easy to permeate and the bar is exposed when a density board which is not closed is coated with the white unsaturated polyester furniture coating, and the rework rate of coating is reduced.

Description

technical field [0001] The invention relates to an unsaturated polyester furniture coating, in particular to an anti-permeation white unsaturated polyester furniture coating. Background technique [0002] Unsaturated polyester furniture coatings can be thickly coated at one time, with full paint film, good hardness, solvent resistance, filling and anti-collapse properties, and are widely used in the furniture industry. In particular, the current popular white panel furniture coating mainly uses unsaturated polyester furniture coatings as primers, and polyurethane white and other solid-color paints as topcoats. Now the panel furniture uses MDF as the base material, first spray a polyurethane sealing primer, and after polishing, apply a thick white unsaturated polyester furniture coating. If the polyurethane sealing primer is not completely sealed or is pierced during polishing, it is easy to penetrate when it is coated with white unsaturated polyester furniture paint, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/06C09D7/12
Inventor 陈寿生
Owner 展辰新材料集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap