Environment-friendly water-based antirust agent and preparation method thereof

A water-based rust inhibitor, an environmentally friendly technology, applied in the field of metal rust prevention, can solve the problems of short rust prevention time, high cost, large demand, etc., to improve wettability, improve adsorption capacity, and excellent rust prevention effect. Effect

Active Publication Date: 2013-11-20
上海宸蕴环保技术有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of use, the demand is huge, and the cost is high, and heavy metal agents are added, causing greater environmental pressure and safety hazards
[0005] In addition, there are some borate and carboxylate water-based anti-rust agents on the market. Because of their short anti-rust time, they often only have a short-term anti-rust effect.
[0006] Others, such as products that use sodium nitrite as a water-based antirust agent, although the antirust effect is relatively good, but sodium nitrite is carcinogenic and will pose serious health risks to personnel in various links of production, manufacturing and use. At present, many The country has banned the use of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly water-based antirust agent and preparation method thereof
  • Environment-friendly water-based antirust agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation method of 1# environment-friendly water-based antirust agent:

[0028] raw material

Dosage (kg)

Urea phosphate

99

Span-80 and Tween-80, 1:1 mixture

1

[0029] Add the above raw materials into water in sequence, mix and stir until uniform, and make 1# environment-friendly water-based antirust agent.

[0030] Take 50g of the above-mentioned 1# environment-friendly water-based rust inhibitor and dissolve it in 50g of distilled water.

[0031] Salt spray test according to SH / T0081, the result is: 7 days, grade 0.

[0032] Damp heat test according to GB / T2361, the result is: 10 days, grade 0.

Embodiment 2

[0034] The preparation method of 2# environment-friendly water-based antirust agent:

[0035] raw material

Dosage (kg)

Urea phosphate

1

Sodium dodecyl benzene sulfonate

2

sodium hydroxide

2

water

95

[0036] Add the above raw materials into water in sequence, mix and stir until uniform, and make 2# environment-friendly water-based antirust agent.

[0037] The above-mentioned 2# environment-friendly water-based antirust agent was tested for liquid phase corrosion according to the test method of GB / T11143-2008, and the result was: qualified.

Embodiment 3

[0039] The preparation method of 3# environment-friendly water-based antirust agent:

[0040] raw material

Dosage (kg)

Urea phosphate

50

TX-10

1.5

Potassium hydroxide

1.5

water

47

[0041] Add the above raw materials into water in sequence, mix and stir until uniform, and make 3# environment-friendly water-based antirust agent.

[0042] Take 20g of the above-mentioned 3# environment-friendly water-based rust inhibitor and dissolve it in 80g of distilled water.

[0043] Damp heat test according to GB / T2361, the result is: 72 hours, grade 0, in line with the relevant technical indicators of anti-rust oil.

[0044] According to the GB / T11143-2008 test method, the liquid phase corrosion test was carried out, and the result was: qualified.

[0045] 4. Embodiment four

[0046] The preparation method of 4# environment-friendly water-based antirust agent:

[0047] raw material

Dosage (kg)

Urea ph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an environment-friendly water-based antirust agent. The antirust agent is characterized by being prepared from the following raw materials according to weight percentage: 1-99% of urea phosphate, 0-5% of surfactant, 0-2% of sodium hydroxide or potassium hydroxide and the balance of water. The environment-friendly water-based antirust agent is prepared by sequentially adding the raw materials into water. The environment-friendly water-based antirust agent has excellent effects, can be used as a long-term antirust agent, can also be used as an excellent interprocess antirust agent after being added with water, and has the longest antirust time of three years, and furthermore, the antirust agent has the effects of energy conservation, emission reduction and environment protection.

Description

technical field [0001] The invention belongs to the technical field of metal antirust, and in particular relates to an environment-friendly water-based antirust agent and a preparation method thereof. Background technique [0002] Anti-rust oil is generally used for medium and long-term anti-rust of traditional metals, but anti-rust oil generally contains heavy metal ions such as barium and chromium. As we all know, heavy metal compounds cannot be excreted after entering the organism due to their insoluble characteristics, which will cause chronic poisoning . Therefore, some countries in Europe and the United States have imposed strict restrictions on its use. Although my country has not explicitly imposed relevant bans and restrictions on its use, from the perspective of environmental protection, health and safety, the restriction and non-use of such substances is an inevitable trend. [0003] At the same time, due to the current depletion of oil resources and rising oil ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/167C23F11/06
Inventor 张乃庆张光晖孟祥兵齐新然张天鹏
Owner 上海宸蕴环保技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products