Low-temperature hot stamping hot melt adhesive for alumite and preparation method thereof

A hot melt adhesive, anodized aluminum technology, applied in the direction of adhesives, monocarboxylate copolymer adhesives, adhesive types, etc. problems, to achieve the effect of firm adhesion without falling off, stable and controllable production cost, and long-term storage stability

Active Publication Date: 2013-12-25
云南玉溪东魅包装材料有限公司
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the deficiencies in the prior art, the present invention aims to provide a low-temperature hot-stamping hot-melt adhesive and its preparation method, the anodized aluminum containing the hot-melt adhesive, I...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] In this example, the above-mentioned low-temperature hot-stamping hot-melt adhesive is used on the "Hongtashan" tipping paper produced by Yunnan Phoenix Paper Products Co., Ltd. The raw materials used are: 4.0 kg of vinyl chloride-vinyl acetate resin, 6.0 kg of terpene resin, butyl acrylate 4.0kg of ester, 1.0kg of 2-ethylhexyl acrylate, 1.0kg of nitrocellulose, 2.0kg of fumed silica, 50.0kg of ethyl acetate, 30.0kg of ethanol, and 2.0kg of propyl acetate.

[0030] Follow the steps below for production:

[0031] a. Add the weighed ethyl acetate, ethanol and propyl acetate into the container at room temperature and stir for 3 minutes at a stirring speed of 600r / min to obtain the mixed solution A;

[0032] b. Add the weighed vinyl chloride-vinyl acetate resin, terpene resin, butyl acrylate and 2-ethylhexyl acrylate into the mixed solution A in turn, stir for 120min, and the stirring speed is 600r / min to obtain the mixed solution B;

[0033] c. Add weighe...

Embodiment 2

[0037] In this example, the "Yuxi" tipping paper produced in Yunnan Yuxi tipping paper factory adopts the above-mentioned low-temperature stamping hot melt adhesive, and the raw materials used are: 1.0 kg of vinyl chloride-vinyl acetate resin, 3.0 kg of terpene resin, butyl acrylate 8.0 kg of ester, 2.0 kg of 2-ethylhexyl acrylate, 3.0 kg of nitrocellulose, 1.0 kg of fumed silica, 30.0 kg of ethyl acetate, 10.0 kg of ethanol, and 3.0 kg of propyl acetate.

[0038] Follow the steps below for production:

[0039] a. Add the weighed ethyl acetate, ethanol and propyl acetate into the container at room temperature and stir for 5 minutes at a stirring speed of 500r / min to obtain the mixed solution A;

[0040] b. Add the weighed vinyl chloride-vinyl acetate resin, terpene resin, butyl acrylate and 2-ethylhexyl acrylate into the mixed solution A in sequence, stir for 130min, and the stirring speed is 500r / min to obtain the mixed solution B;

[0041] c. Add weighed c...

Embodiment 3

[0045]In this example, the "Little Panda" tipping paper produced by Yunnan Qujing Qilinfu Brand Printing Co., Ltd. uses the above-mentioned low-temperature hot-stamping hot-melt adhesive, and the raw materials used are: 6.0 kg of vinyl chloride-vinyl acetate resin, 8.0 kg of terpene resin , 3.0 kg of butyl acrylate, 1.0 kg of 2-ethylhexyl acrylate, 5.0 kg of nitrocellulose, 4.0 kg of fumed silica, 70.0 kg of ethyl acetate, 50.0 kg of ethanol, and 5.0 kg of propyl acetate.

[0046] Follow the steps below for production:

[0047] a. Add the weighed ethyl acetate, ethanol and propyl acetate into the container at room temperature and stir for 4 minutes at a stirring speed of 700r / min to obtain the mixed solution A;

[0048] b. Add the weighed vinyl chloride-vinyl acetate resin, terpene resin, butyl acrylate and 2-ethylhexyl acrylate into the mixed solution A in sequence, stir for 100min, and the stirring speed is 700r / min to obtain the mixed solution B;

[0049] c. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides low-temperature hot stamping hot melt adhesive for alumite and a preparation method of the low-temperature hot stamping hot melt adhesive. In the existing alumite rotary gold stamping process, heat transfer hot stamping temperatures are all within the range of 120 DEG C to 200 DEG C, if the temperature of a gold stamping plate is too high, energy consumption in the gold stamping process is increased, alumite hot stamping foil or printing materials can deform by being heated, and then hot stamping is inaccurate. The low-temperature hot stamping hot melt adhesive is prepared from the following raw materials, by weight, 1-6 parts of chloroethylene-vinyl acetate resin, 1-10 parts of terpene resin, 1-10 parts of acrylic ester, 1-5 parts of nitrocellulose, 1-5 parts of fumed silica, 20-70 parts of ethyl acetate, 10-50 parts of ethyl alcohol and 1-5 parts of propyl acetate. The low-temperature hot stamping hot melt adhesive is low in softening temperature and high in adhesive power, heat transfer hot stamping temperatures are within the range of 85 DEG C to 100 DEG C, energy consumption can be remarkably reduced, the problems that the gold stamping foil or the printing materials easily deform by being heated by high-temperature hot stamping, so that waste caused by inaccurate hot stamping is generated are solved.

Description

technical field [0001] The invention relates to the field of hot-melt adhesives, in particular to a low-temperature stamping hot-melt adhesive for anodized aluminum and a preparation method thereof. Background technique [0002] Anodized aluminum is a new type of packaging material for vacuum aluminum plating. After a certain temperature and pressure, the pre-engraved patterns, lines and fonts on the hot stamping plate are transferred to the surface of the substrate, making it bright in color, strong in metal feeling, visually It has been widely used in hot stamping and decoration on the surface of paper products, plastic products, leather products, wood products and so on. [0003] Anodized aluminum is composed of a base film layer, a release layer, a colored layer, an aluminum-coated layer and a hot-melt adhesive layer. , and then coat the hot-melt adhesive layer. The hot-melt adhesive mainly plays the role of bonding. In anodized aluminum hot stamping, it is heated and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J127/06C09J131/04C09J11/08C09J11/06C09J11/04
Inventor 何宗修龚林陈诗阳杨正德
Owner 云南玉溪东魅包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap