The preparation method of lithium cobalt oxide

A technology for lithium cobalt oxide and cobalt salt, which is applied in the field of preparation of lithium cobalt oxide, can solve the problems of high energy consumption, difficult to control product morphology, and many processes, and achieves low energy consumption, regular and controllable morphology, and fewer processes. Effect

Active Publication Date: 2016-05-04
JIANGSU HUADONG INST OF LI ION BATTERY +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The whole process has disadvantages such as many steps, high energy consumption, and difficult to control the product shape.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • The preparation method of lithium cobalt oxide
  • The preparation method of lithium cobalt oxide
  • The preparation method of lithium cobalt oxide

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The embodiment of the present invention provides a preparation method of lithium cobaltate, which comprises the following steps:

[0016] S1, using a cobalt salt solution and an alkaline solution as reactants, and stirring while reacting in a controlled crystallization kettle with a buffer by a controlled crystallization method, to prepare spherical cobalt oxyhydroxide; and

[0017] S2, putting the spherical cobalt oxyhydroxide into a lithium hydroxide solution, and performing a hydrothermal reaction, so that lithium in the lithium hydroxide replaces hydrogen in the cobalt oxyhydroxide to generate spherical lithium cobaltate.

[0018] see figure 1 , The controlled crystallization kettle 100 includes a kettle body 10, a stirring device and a feeding device.

[0019] The stirring device 20 is used to stir the reactants accommodated in the kettle body 10 , and the stirring device includes a motor 22 , a stirring shaft 24 and a stirring paddle 26 . The motor 22 is connect...

Embodiment 1

[0045] 1) Add 4mol / L ammonia solution in a 4-liter controlled crystallization kettle as a buffer, mechanically stir vigorously, the stirring intensity is 1500 rpm, and slowly add 2mol / L cobalt chloride aqueous solution from both sides at the same time with a peristaltic pump And the sodium hydroxide aqueous solution of 4mol / L, feed rate is controlled at 0.5 milliliters per minute, obtains spherical cobalt oxyhydroxide.

[0046] 2) Take out the reaction product spherical cobalt oxyhydroxide in 1), repeatedly wash with deionized water and suction filter to preserve the obtained spherical cobalt oxyhydroxide;

[0047] 3) Mix 1 kg of the spherical cobalt oxyhydroxide obtained in 2) with an aqueous solution containing 400 g of saturated lithium hydroxide and put it into a high-pressure hydrothermal reaction kettle for hydrothermal reaction. The hydrothermal reaction kettle should be heated rapidly to 150°C and Insulated for 5 hours to obtain spherical lithium cobaltate;

[0048] 4...

Embodiment 2

[0052] 1) Add 8 mol / L ammonia solution into a 10-liter controlled crystallization kettle as a buffer, mechanically stir vigorously, the stirring intensity is 900 rpm, and slowly add 3 mol / L cobalt chloride aqueous solution from both sides at the same time with a peristaltic pump and the aqueous sodium hydroxide solution of 6mol / L, the feeding speed of two kinds of solutions all is controlled at 2 milliliters per minute, obtains spherical cobalt oxyhydroxide.

[0053] 2) Take out the reaction product spherical cobalt oxyhydroxide in 1), repeatedly wash with deionized water and suction filter to preserve the obtained spherical cobalt oxyhydroxide;

[0054] 3) Mix 3 kg of the spherical cobalt oxyhydroxide obtained in 2) with an aqueous solution containing 1 kg of saturated lithium hydroxide and put it into a high-pressure hydrothermal reaction kettle for hydrothermal reaction. The hydrothermal reaction kettle should be heated rapidly to 200°C and Insulated for 1 hour to obtain sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of lithium cobaltate, comprising: using a cobalt salt solution and an alkaline solution as reactants, and stirring while reacting in a controlled crystallization kettle with a buffer by a controlled crystallization method to prepare spherical cobalt oxyhydroxide and putting the spherical cobalt oxyhydroxide into lithium hydroxide solution, and performing a hydrothermal reaction in a hydrothermal reaction kettle, so that lithium in lithium hydroxide replaces hydrogen in cobalt oxyhydroxide to generate spherical lithium cobaltate.

Description

technical field [0001] The invention belongs to the field of lithium ion batteries, in particular to a preparation method of lithium cobaltate, in particular to a preparation method of low energy consumption lithium cobaltate. Background technique [0002] The rapid development of mobile electronic devices represented by smart phones, tablet computers, notebook computers, mobile tools, etc. is based on the development of lithium-ion battery preparation technology. Small mobile electronic devices have almost strict requirements on technical indicators such as battery safety, thermal stability and cycle life. It is precisely because of the high standards of battery safety and reliability that the positive electrode material lithium cobalt oxide, which plays a supporting role in the entire industry at the current stage, is difficult to be replaced in the foreseeable future. [0003] At present, the mature production process of industrialized lithium cobaltate is a solid-phase ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/525C01G51/00
CPCC01G51/42H01M4/525C01P2002/72C01P2004/03C01P2004/32C01P2004/61C01P2006/11H01M10/052Y02E60/10C01P2006/40H01M4/131H01M10/0525H01M2220/30
Inventor 方谋王要武何向明王莉尚玉明高剑郭建伟毛宗强
Owner JIANGSU HUADONG INST OF LI ION BATTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com