Zinc oxide mineral beneficiation collecting agent and preparation method of zinc oxide mineral beneficiation collecting agent

A collector and zinc oxide technology, which is applied in flotation, solid separation, etc., can solve the problems of high flotation cost, narrow selection range, and large reagent consumption, etc., to expand the selectivity range, improve the concentrate grade and recover The effect of improving the rate and sensitivity

Inactive Publication Date: 2014-01-15
SICHUAN JINGDA MINING TECH
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention overcomes the above-mentioned deficiencies and provides a fatty amine mixture collector and a preparation method thereof. The collector has low temperature resistance and good selectivity, and ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc oxide mineral beneficiation collecting agent and preparation method of zinc oxide mineral beneficiation collecting agent
  • Zinc oxide mineral beneficiation collecting agent and preparation method of zinc oxide mineral beneficiation collecting agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The weight component of a kind of zinc oxide ore dressing collector is:

[0022] Dodecyl amine 200g, hexadecyl amine 300g, octadecyl amine 450g, sodium dodecyl sulfonate 50g.

[0023] A preparation method of zinc oxide mineral dressing collector: dodecyl amine, hexadecyl amine, octadecyl amine and active agent are weighed according to the above ratio and poured into a heatable and stirred reaction kettle, and then poured into the weight Dissolve in 80-100g ethanol.

[0024] Slowly add 200g of water into the reaction kettle, heat to 130°C, then add 80g of sodium hydroxide and keep stirring for 2 to 3 hours, keep the temperature at 130°C during the stirring process, and the mass concentration of sodium hydroxide is 30%. After cooling, a paste-like mixture is formed to obtain a paste-like new collector product.

Embodiment 2

[0026] The weight component of a kind of zinc oxide ore dressing collector is:

[0027] Dodecylamine 250g, hexadecylamine 300g, octadecylamine 400g, sodium cetylsulfonate 50g.

[0028] A preparation method of zinc oxide mineral dressing collector: dodecyl amine, hexadecyl amine, stearyl amine and active agent are weighed in proportion and poured into a heatable and stirred reaction kettle, and then poured into a reaction kettle with a weight of Dissolve in 80-100g ethanol.

[0029] Slowly add 150-200g of water into the reaction kettle, when heated to 140°C, add 90g of sodium hydroxide and keep stirring for 2-3 hours, keep the temperature at 140°C during the stirring process, and the mass concentration of sodium hydroxide is 32% , and form a pasty mixture after cooling to obtain a pasty new collector product.

Embodiment 3

[0031] The weight component of a kind of zinc oxide ore dressing collector is:

[0032] Dodecyl amine 180g, hexadecyl amine 300g, octadecyl amine 450g, dodecyltrimethylammonium chloride 70g.

[0033] A preparation method of zinc oxide mineral dressing collector: dodecyl amine, hexadecyl amine, stearyl amine and active agent are weighed in proportion and poured into a heatable and stirred reaction kettle, and then poured into a reaction kettle with a weight of Dissolve in 80-100g ethanol.

[0034] Slowly add 150-200g of water into the reaction kettle, heat it to 150°C, then add 90g of sodium hydroxide and keep stirring for 2-3 hours, keep the temperature at 150°C during the stirring process, and the mass concentration of sodium hydroxide is 36% , and form a pasty mixture after cooling to obtain a pasty new collector product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a zinc oxide mineral beneficiation collecting agent and a preparation method of the zinc oxide mineral beneficiation collecting agent, in particular to a metal zinc oxide mineral beneficiation collecting agent and a preparation method of the metal zinc oxide mineral beneficiation collecting agent. The zinc oxide mineral beneficiation collecting agent comprises, by weight, 18%-25% of dodecanamine, 25%-30% of cetylamine, 38%-45% of octadecylamine and 4%-7% of active agent. The zinc oxide mineral beneficiation collecting agent is relatively resistant to low temperature and can be used without heating ore pulp, when the zinc oxide mineral beneficiation collecting agent is used under the condition that the temperature of the ore pulp is 15-25 degrees, compared with an original collecting agent, the zinc oxide mineral beneficiation collecting agent has the advantages that the obtained concentrate indexes are that the concentrate grade can be improved by 1.7%, the recovery rate can be improved by 5.76%, and the beneficiation cost can be greatly reduced. The zinc oxide mineral beneficiation collecting agent particularly has wide adaptation to high mud deep oxidation zinc oxide raw ore.

Description

technical field [0001] The invention relates to a zinc oxide mineral dressing collector and a preparation method thereof, and relates to a collector for metal zinc oxide mineral dressing and a preparation method thereof. Background technique [0002] There are many kinds of minerals contained in zinc oxide ore, the ore structure is complex, and the associated components are very unstable. The ore contains high clay, iron oxide minerals, soluble salts and other gangues and other reasons, and contains a large amount of clay and limonite. The flotation index of zinc oxide ore in my country is still low due to the high content of soluble salts and other reasons. [0003] At present, the flotation of zinc oxide ore mainly uses a single primary amine as a collector. With the change of ore properties, a single collector can no longer obtain ideal flotation indicators. The composite collector has a synergistic effect in the flotation process and can effectively improve the concentra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B03D1/018B03D101/02
Inventor 严志明汤小军周怡玫陈金花赵强徐国栋
Owner SICHUAN JINGDA MINING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap