Manufacturing method and product of high surface strength offset printing paper

A technology of offset printing paper and high surface, applied in the field of offset printing paper, can solve the problems of low filler retention rate, retention affects the application effect of fillers, etc., so as to improve filler retention rate, protect ecological environment and resources Efficient utilization and good paper quality

Active Publication Date: 2015-11-25
DATANG INT HIGH ALUMINA COAL R & D CENT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the use of conventional paper-making fillers (such as calcium carbonate, talc, kaolin, etc.), due to the high density of the filler itself, it is easy to quickly settle to the bottom after being mixed with plant fibers, resulting in low filler retention. The particle size is far smaller than the fiber, and its own retention also greatly affects the application effect of the filler, which needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method and product of high surface strength offset printing paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation of embodiment 1 offset printing paper

[0028] 1. Preparation of surface sizing agent:

[0029] (1) Weigh the following components by mass percentage: 2.0% oxidized starch, 1.0% polyvinyl alcohol, 0.01% AKD, and the rest is water; (2) Fully mix and stir each component in water, Instantly.

[0030] 2. Preparation of offset printing paper

[0031] 1) Add porous calcium silicate with a mass percentage of 55% relative to the dry mixed wood pulp fiber to the mixed wood pulp fiber for mixing, adjust the slurry concentration to 10%, and process it in a refiner or PFI mill until the obtained Mixed pulp with a beating degree of 48°SR;

[0032] 2) Add cationic starch, AKD and polyacrylamide to the mixed slurry obtained in step 1) sequentially, the amount of cationic starch added is 15kg / ton of paper, the amount of AKD added is 2kg / ton of paper, and the amount of polyacrylamide added is 0.3kg / ton Paper;

[0033] 3) Use the slurry prepared in step 2) to make pa...

Embodiment 2

[0035] The preparation of embodiment 2 offset printing paper

[0036] 1. Preparation of surface sizing agent:

[0037] (1) Weigh the following components by mass percentage: 2.5% potato starch, 0.5% polyvinyl alcohol, 0.01% AKD, and the rest is water; (2) Fully mix and stir each component in water, Instantly.

[0038] 2. Preparation of offset printing paper

[0039] 1) Add porous calcium silicate with a mass percentage of 25% relative to the dry fiber to the wood pulp fiber for mixing, adjust the slurry concentration to 15%, and process it in a refiner or PFI mill until the beating degree is 48 °SR mixed slurry.

[0040] 2) Add cationic starch, AKD and polyacrylamide to the mixed slurry obtained in step 1) sequentially, the amount of cationic starch added is 10kg / ton of paper, the amount of AKD added is 0.5kg / ton of paper, and the amount of polyacrylamide added is 0.5kg / ton tons of paper.

[0041] 3) Use the slurry prepared in step 2) to make paper, press, and dry to obta...

Embodiment 3

[0043] Preparation of embodiment 3 offset printing paper

[0044] 1. Preparation of surface sizing agent:

[0045] (1) Weigh the following components by mass percentage: 1.5% cationic starch, 0.5% polyvinyl alcohol, 0.003% AKD, and the rest is water; (2) Fully mix and stir each component in water, Instantly.

[0046] 2. Preparation of offset printing paper

[0047] 1) Add porous calcium silicate with a mass percentage of 35% relative to the absolute dry fiber to the wood pulp fiber and mix, adjust the slurry concentration to 25%, and process it in a refiner or PFI mill until the degree of beating is 50 °SR mixed slurry.

[0048] 2) Add cationic starch, AKD and polyacrylamide to the mixed slurry obtained in step 1) sequentially, the amount of cationic starch added is 1kg / ton of paper, the amount of AKD added is 0.5kg / ton of paper, and the amount of polyacrylamide added is 0.1kg / ton tons of paper.

[0049] 3) Use the slurry prepared in step 2) to make paper, press, and dry to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a paper making method with pulp and a product of high-surface-intensity offset printing paper. The paper making method with the pulp comprises the steps that (1) multi-hole calcium silicate and mixed wood pulp fibers are subjected to mixing pulping, mixed pulp is obtained; (2) retention and drainage agents A, sizing agents and retention and drainage agents B are added into the mixed pulp in sequence, even stirring is carried out, papermaking pulp is obtained; (3) the papermaking pulp is subjected to papermaking, squeezing and drying, body paper is obtained; (4) surface sizing agents are used for carrying out surface sizing on the body paper, and the offset printing paper is obtained. The multi-hole calcium silicate is used as the papermaking padding, during a papermaking process, paper pulp / padding medium-high-concentration mixing pulping, CS / CPAM double-element retention and surface sizing agent formula improving and other measures are used, the padding retention rate is improved, paper intensity is effectively improved, and the waterproof performance, the oil resistance, the paper surface intensity, the tensile strength and other performance indexes of paper are obviously improved.

Description

technical field [0001] The invention relates to filled paper and a manufacturing method thereof, in particular to high-surface-strength offset printing paper filled with porous calcium silicate and a manufacturing method thereof, and belongs to the field of offset printing paper manufacturing. Background technique [0002] With the development of the publishing industry, the demand for offset printing paper is increasing. Offset printing has the characteristics of soft tones, low cost of plate making, large-format plates and fine lines of printing dots, etc., so offset printing paper has been greatly developed in recent years. [0003] Papermaking filler is the largest component of paper material except fiber. By adding filler, it can reduce the production cost of paper, improve the evenness, opacity and whiteness of the paper page, adjust the ink absorption of the paper, and increase the quality of the paper. printability etc. During the use of conventional paper-making f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H15/10D21H17/68D21H21/10D21H21/16
Inventor 张战军王成海孙俊民彭建军宋宝祥张权魏晓芬陈铃华高志军陈杨沈臻煌陈雪梅
Owner DATANG INT HIGH ALUMINA COAL R & D CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com