A kind of preparation method of lead-acid battery negative plate

A lead-acid battery and negative plate technology, applied in the direction of lead-acid battery electrodes, battery electrodes, circuits, etc., to achieve the effects of increasing hydrogen evolution potential, reducing water consumption, and increasing capacity

Inactive Publication Date: 2015-10-28
HEBEI NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Data research shows that there is no report of adding zirconium compounds to the lead paste of the negative plate of the lead-acid battery and using industrial processes to make the negative plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of lead-acid battery negative plate
  • A kind of preparation method of lead-acid battery negative plate
  • A kind of preparation method of lead-acid battery negative plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Raw material preparation: Prepare 25g of lead powder, 0.1g of carbon black 1#, 0.1g of carbon black 2#, 0.1g of zirconium dioxide, 0.25g of barium sulfate, 0.05g of Norway lignin, 0.01g of fiber, concentration 1.4g / cm 3 3.20mL of sulfuric acid and 6mL of water.

[0026] (2) Preparation of lead paste: dry mix lead powder, carbon source, zirconium source and other solid materials, use a mortar to grind for 12 minutes, then quickly add distilled water mixed with fibers, stir for 4 minutes, slowly add dilute sulfuric acid, and add acid While stirring, stir for 5min.

[0027] (3) Plate making: apply the evenly mixed paste on the grid, cure at 25°C for 3 hours, and then dry at 80°C to make a negative plate. Then 1 negative plate and 1 regular positive plate make up a battery of about 0.2Ah.

[0028] (4) Formation: use a density of 1.05 g / cm 3 The sulfuric acid solution is charged and formed in multiple stages, the method is: first stand for 20 minutes, and then use 1m...

Embodiment 2

[0031] (1) Raw material preparation: Prepare 25g of lead powder, 0.15g of carbon black 1#, 0.1g of graphite, 0.1g of zirconium dioxide, 0.2g of barium sulfate, 0.05g of Norwegian lignin, 0.01g of fiber, and the concentration is 1.4g / cm 3 of 3.0 mL of sulfuric acid and 6 mL of water.

[0032] (2) Preparation of lead paste: Dry mix solid materials such as lead powder, carbon source, zirconium source, etc., use a mortar to grind for 10 minutes, then quickly add distilled water mixed with fibers, stir for 3 minutes, slowly add dilute sulfuric acid, and add acid While stirring, stir for 3min.

[0033] (3) Plate making: apply the evenly mixed paste on the grid, cure at 25°C for 3 hours, and then dry at 80°C to make a negative plate. Then 1 negative plate and 1 regular positive plate make up a battery of about 0.2Ah.

[0034] (4) Formation: use a density of 1.1 g / cm 3 The sulfuric acid solution was charged and formed in multiple stages, that is: firstly, it was left for 20 minut...

Embodiment 3

[0036] (1) Raw material preparation: prepare 25g of lead powder, 0.1g of carbon black 1#, 0.1g of carbon black 2#, 0.4g of zirconium nitrate, 0.25g of barium sulfate, 0.1g of Norway lignin, 0.03g of fiber, the concentration is 1.4g / cm 3 2.5mL of sulfuric acid and 5mL of water.

[0037] (2) Preparation of lead paste: dry-mix solid materials such as lead powder, carbon source, zirconium source, etc., use a mortar to grind for 12 minutes, then quickly add distilled water mixed with fibers, stir for 4 minutes, slowly add dilute sulfuric acid, and add acid While stirring, stir for 5min.

[0038] (3) Plate making: apply the evenly mixed paste on the grid, cure at 30°C for 3 hours, and then dry at 90°C to make a negative plate. Then 1 negative plate and 1 regular positive plate make up a battery of about 0.2Ah.

[0039] (4) Formation: use a density of 1.20 g / cm 3 The sulfuric acid solution is charged and formed in multiple stages, that is: first rest for 10 minutes, and then char...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a lead-acid storage battery negative plate. The preparation method comprises the following steps: (1) weighting lead powder, a carbon source, a zirconium source, barium sulfate, lignin, fibers, dilute sulphuric acid and distilled water which serve as raw materials in a mass ratio of 25:(0.1-0.3):(0.05-0.4):(0.1-0.25):(0.05-0.25):(0.005-0.02):(3-5):(4-7) for standby application; (2) preparing lead plaster; (3) plating; (4) forming. The preparation method has the advantages that a right amount of zirconium compound is added to a negative plate, so that the discharge capacity can be improved by 3-5%, meanwhile, the hydrogen evolution electric potential is remarkably negatively shifted, so that hydrogen is difficult to separate out, and the consumption of acid in a cyclic process is effectively reduced.

Description

technical field [0001] The invention relates to a preparation method of a lead-acid storage battery negative plate containing a zirconium additive, and belongs to the technical field of energy materials. Background technique [0002] Lead-acid batteries have the advantages of abundant raw materials, simple production process, mature technology, low price, and stable electrical performance. However, due to the low utilization rate of active materials, lead-acid batteries have low quality and specific energy. With the expansion of the application field of lead-acid batteries, people put forward higher requirements for their electrical properties, such as high rate charge and discharge, low temperature characteristics, high temperature resistance characteristics and service life. One of the most effective ways to solve these problems is to add an appropriate amount of additives to the active substance without changing the existing process conditions. Although there are many st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/16
CPCH01M4/20H01M4/628Y02E60/10
Inventor 丁克强刘璐刘丽坤赵永波李媛
Owner HEBEI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com