A water-based nano-coating

A nano-coating, water-based technology, applied in the field of coatings and paints, can solve the problems of not effectively protecting the strength of the wall plastering bottom layer, affecting the beauty of the building, and the elasticity of the coating film is easy to age, so as to increase the reactive points, avoid natural oxidation, The effect of improving adsorption performance

Inactive Publication Date: 2015-11-25
HANGZHOU FUYANG FUCHUN COATING&DECORATING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main disadvantage of this kind of coating is that the elasticity of the coating film is easy to age, which leads to a decrease in the elongation rate, and cannot effectively protect the strength of the bottom layer of the wall, resulting in cracking and falling off of the wall surface, which not only affects the appearance of the building, but also cracks on the wall surface, causing the wall surface to crack and fall off. surface leaking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A water-based nano-coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A water-based nano-coating is characterized in that the coating is configured by A component and B component, wherein the formula of A component is as follows:

[0041] 60 parts of hydroxyl polyacrylate dispersion

[0042] 0.2 parts of leveling wetting agent

[0043] 12 parts polyacrylic acid

[0044] 20 parts polyisocyanate

[0045] 30 parts of crosslinking agent

[0046] Filling 10 parts

[0047] 1 part of N,N-dimethylethanolamine

[0048] Co-solvent 0.2 parts

[0049] 1 part antifreeze

[0050] Wetting agent 0.2 parts

[0051] 0.2 part of defoamer

[0052] Thickener 0.1 parts

[0053] Wetting agent 0.1 part

[0054] 1 part preservative

[0055] pH regulator

[0056] 25 parts of nano flame retardant compound;

[0057] The preparation method of described nano flame retardant composite agent is:

[0058] (1) The silicon hydroxyapatite, red phosphorus, attapulgite, hydrotalcite, montmorillonite, titanium dioxide, calcite, kaolin according to 25-35: 15-20: 10-...

Embodiment 2

[0067] A water-based nano-coating is characterized in that the coating is configured by A component and B component, wherein the formula of A component is as follows:

[0068] 80 parts of hydroxyl polyacrylate dispersion

[0069] 0.3 parts of leveling wetting agent

[0070] 25 parts polyacrylic acid

[0071] 30 parts polyisocyanate

[0072] 40 parts of crosslinking agent

[0073] Filling 15 parts

[0074] N,N-Dimethylethanolamine 2 parts

[0075] Co-solvent 0.5 parts

[0076] Antifreeze 2 parts

[0077] Wetting agent 0.5 parts

[0078] 0.5 part of defoamer

[0079] Thickener 0.3 part

[0080] Wetting agent 0.3 part

[0081] 2 parts preservative

[0082] pH regulator

[0083] 30 parts of nano flame retardant compound;

[0084] The preparation method of described nano flame retardant composite agent is:

[0085] (1) The silicon hydroxyapatite, red phosphorus, attapulgite, hydrotalcite, montmorillonite, titanium dioxide, calcite, kaolin according to 25-35: 15-20: 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous nano-coating. The aqueous nano-coating is characterized by being prepared from a component A and a component B, wherein the formula of the component A is as follows: 60-80 parts of hydroxyl polyacrylate dispersoid, 0.2-0.3 parts of leveling wetting agent, 12-25 parts of polyacrylic acid, and 20-30 parts of polyisocyanates; the component B comprises 6-9 parts of polyisocyanate curing agent; the aqueous nano-coating is prepared through the following steps: adding the component A to a container according to the formula, stirring at the middle speed, sequentially adding deionized water, the leveling wetting agent, a cosolvent, a defoaming agent and a thickening agent, dispersing for 20-30min at high speed, adding the water-dispersibility polyisocyanate curing agent according to the certain proportion, and fully stirring to obtain the aqueous nano-coating.

Description

technical field [0001] The invention belongs to the technical field of coatings and paints, in particular to a water-based nano coating. Background technique [0002] Any paint that uses water as a solvent or as a dispersion medium can be called a water-based paint. Water-based coatings include three types: water-soluble coatings, water-dilutable coatings, and water-dispersible coatings. Water-soluble coatings use water-soluble resins as film-forming materials, represented by polyvinyl alcohol and its various modified products. There are also water-soluble alkyd resins, water-soluble epoxy resins, and inorganic polymer water-based resins, etc.; water-dilutable coatings refer to coatings prepared after emulsified emulsions become films, which are solvent-based resins dissolved in organic solvents, and then re-emulsified. With the help of strong mechanical stirring, the resin is dispersed in water to form an emulsion, which is called a post-emulsification emulsion. The paint ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/06C09D5/18C09D7/12
Inventor 王福顺李凡
Owner HANGZHOU FUYANG FUCHUN COATING&DECORATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com