Composite porous fibers with core-shell structures and preparation method of dual-pore structure membrane

A composite fiber and porous fiber technology applied in the field of bioengineering to achieve high electrical conductivity, simple steps, and good practical value

Inactive Publication Date: 2014-02-12
JIAXING UNIV
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the combination of electrospinning technology and in-situ polymerization method has not been seen so far to prepare electroactive polylactic acid / polypyrrole composite micro / nanofiber double-pore structure with large voids interwoven by composite fibers with core-shell structure. Film related reports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite porous fibers with core-shell structures and preparation method of dual-pore structure membrane
  • Composite porous fibers with core-shell structures and preparation method of dual-pore structure membrane
  • Composite porous fibers with core-shell structures and preparation method of dual-pore structure membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0045] Preparation of polylactic acid / polyaniline composite micro / nanofiber dual-porous membrane with polyaniline as the shell and polylactic acid as the core, which is interwoven with composite porous fibers with a core-shell structure

[0046] Step 1 Preparation of polylactic acid spinning dope

[0047] First weigh a certain amount of dichloromethane and place it in a stoppered Erlenmeyer flask, then add a certain amount of PLLA slices into it, stir magnetically at room temperature for 5 hours, and prepare a spinning solution with a mass fraction of 12%.

[0048] Step 2 Preparation of polylactic acid hollow porous fibers and double-porous membranes by electrospinning

[0049] Pour the prepared solution into the solution reservoir (20mL syringe), use the flattened injection needle as the capillary for jetting fine flow, connect the positive pole of the high-voltage power supply, connect the receiver to the negative pole, and the amount of solution extruded is controlled by th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Long axisaaaaaaaaaa
Short axisaaaaaaaaaa
Film thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of high-conductivity hollow porous composite fibers which take a conductive polymer as a shell and a degradable polymer as a core and have core-shell structures, and a dual-pore structure membrane of the high-conductivity hollow porous composite fibers as well as an application of the dual-pore structure membrane in tissue engineering. The preparation method comprises the steps of preparing the degradable polymer, hollow fibers with porous surfaces and the dual-pore structure membrane through an electrostatic spinning method, preparing a degradable polymer / conductive high polymer, hollow porous composite fibers and a dual-pore structure membrane thereof through an in-situ polymerization method, and cleaning and drying to obtain the high-conductivity hollow porous composite fibers with the core-shell structures and the dual-pore structure membrane of the high-conductivity hollow porous composite fibers. The high-conductivity composite micron / nano-fiber dual-pore structure membrane prepared by the invention can be applied to nerve tissue engineering, has the advantages of high conductivity, high porosity, large pore size and good chemical stability, and has a practical value in nerve tissue engineering, and the preparation method of the membrane is simple and feasible.

Description

technical field [0001] The invention relates to the field of bioengineering, in particular to a high-conductivity composite porous fiber with a core-shell structure with a conductive polymer as the shell and a degradable polymer as the core and a preparation method for the double-pore structure membrane. Background technique [0002] In vitro and in vivo experiments have shown that electrically active biomaterials can stimulate the regeneration of bone cells and nerve cells (Biomaterial s2001; 22: 1055). So far, polypyrrole, polyaniline and other conductive polymers are widely studied as electroactive biomaterials that can be used as substrates. In particular, polypyrrole has shown potential in biomedical applications. Its unique electrical activity, conductivity and biocompatibility to mammalian cells make it ideal for nerve repair and guided nerve regeneration. Guide channel material (J.Biomed.Mater.Res.A 2000, 50:574-583). However, due to the fragility, rigidity and non...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/37D06M15/61D04H3/011D04H3/03D06M101/32
Inventor 俞巧珍
Owner JIAXING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com