Antibacterial monomer-containing repairing composite resin for dentistry and preparation method thereof

A dental restoration and composite resin technology, which is applied in dental preparations, dentistry, dental prosthesis, etc., can solve problems such as insufficient bonding strength and weak antibacterial ability of dental restoration composite resin, and achieve the effect of enhancing the bonding effect

Active Publication Date: 2014-03-12
JIANGSU UNIV OF SCI & TECH
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to provide a dental restoration composite resin containing antibacterial monomer methacryloyloxydodecylpyridine bromide. This antibacterial monomer can not only prevent the invasion of microorganisms at the interface, but also participate in polymerization and improve restoration The bonding strength between the material and the teeth, and effectively kill the microorganisms at the bonding interface after polymerization and curing, so as to solve the problems of weak antibacterial ability and insufficient bonding strength of dental restoration composite resins in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The composite resin consists of 25% bisphenol A-glycidyl methacrylate, 1% urethane dimethacrylate, 15% triethylene glycol dimethacrylate, 1% methacryl Oxydodecylpyridine bromide, 56.5% silicon dioxide, 0.5% camphorquinone and 1% N,N-dimethylaminoethyl methacrylate.

[0018] The preparation method of above-mentioned composite resin comprises the following steps:

[0019] (1) Surface modification of silicon dioxide; adding silicon dioxide to a cyclohexane solution of γ-methacryloxypropyltrimethoxysilane (γ-methacryloxypropyltrimethoxysilane The amount of silane is 2% of the silica mass), stirred at room temperature in a magnetic stirrer for 5 hours, and then dried in a drying oven at 100°C for 2.5 hours;

[0020] (2) Stir and blend 1g of antibacterial monomer methacryloyloxydodecyl bromide and 56.5g of modified silicon dioxide in a solvent, and remove the solvent after ultrasonic vibration to disperse to obtain a uniformly dispersed composite filler;

[0021] (3) With 2...

Embodiment 2

[0025] Composite resin consists of 6% bisphenol A-glycidyl methacrylate, 4.5% urethane dimethacrylate, 5% triethylene glycol dimethacrylate, 3% methacryl Oxydodecylpyridine bromide, 80% silicon dioxide, 0.8% camphorquinone and 0.7% N,N-dimethylaminoethyl methacrylate.

[0026] The preparation method of above-mentioned composite resin comprises the following steps:

[0027] (1) Surface modification of silicon dioxide; adding silicon dioxide to a cyclohexane solution of γ-methacryloxypropyltrimethoxysilane (γ-methacryloxypropyltrimethoxysilane The amount of silane is 2% of the silica mass), stirred at room temperature in a magnetic stirrer for 6 hours, and then dried in a drying oven at 120 ° C for 2 hours;

[0028] (2) Stir and blend 3g of antibacterial monomer methacryloyloxydodecyl bromide and 80g of modified silicon dioxide in a solvent, and remove the solvent after ultrasonic vibration to disperse to obtain a uniformly dispersed composite filler;

[0029] (3) With 6g bisp...

Embodiment 3

[0033] Composite resin consists of 1% bisphenol A-glycidyl methacrylate, 20% urethane dimethacrylate, 4% triethylene glycol dimethacrylate, 10% methacryl Oxydodecylpyridine bromide, 63.5% silicon dioxide, 1% camphorquinone and 0.5% N,N-dimethylaminoethyl methacrylate.

[0034] The preparation method of above-mentioned composite resin comprises the following steps:

[0035] (1) Surface modification of silicon dioxide; adding silicon dioxide to a cyclohexane solution of γ-methacryloxypropyltrimethoxysilane (γ-methacryloxypropyltrimethoxysilane The amount of silane is 2% of the silica mass), stirred at room temperature in a magnetic stirrer for 7 hours, and then dried in a drying oven at 150 ° C for 1.5 hours;

[0036] (2) Stir and blend 10g of antibacterial monomer methacryloyloxydodecyl bromide and 63.5g of modified silicon dioxide in a solvent, and remove the solvent after ultrasonic vibration to disperse to obtain a uniformly dispersed composite filler;

[0037] (3) With 1g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
wavelengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses antibacterial monomer-containing repairing composite resin for dentistry and a preparation method thereof. The composite resin comprises 1-25% of bisphenol A-glycidyl methacrylate, 1-20% of carbamic acid ester dimethacrylate, 4-15% of triethylene glycol dimethacrylate, 1-10% of methylacryloyl oxygen dodecylpyridinium bromide, 55-80% of silicon dioxide, 0.5-1% of camphorquinone and 0.5-1% of N, N-dimethylamino ethyl methacrylate. The methylacryloyl oxygen dodecylpyridinium bromide in the composite resin is an antibacterial bonding monomer synthesized from antibacterial quaternary ammonium dodecylpyridine and polymerizable methylacryloyl groups and can be polymerized with other monomers, so that the composite resin has an antibacterial effect, and the bonding effect between the resin and teeth can be enhanced.

Description

technical field [0001] The invention relates to a dental restoration material, in particular to a dental restoration composite resin containing an antibacterial monomer and a preparation method thereof. Background technique [0002] The World Health Organization lists dental caries, cardiovascular and cerebrovascular diseases, and tumors together as the three major non-communicable diseases that need to be prevented and controlled in the 21st century. Caries is a bacterial disease, the main common disease of the oral cavity, and one of the most common diseases of human beings. It can be secondary to pulpitis and periapical periodontitis, and can even cause alveolar bone and jaw inflammation. If it is not treated in time, the lesion will continue to develop, forming cavities, and eventually the crown will be completely destroyed and disappeared. The final result of its development is tooth loss. [0003] Dental restoration materials have a history of hundreds of years, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/083A61K6/027C08F222/20C08F222/22C08F220/34C08F2/48C08K9/06C08K3/36
Inventor 高延敏王丹周超
Owner JIANGSU UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap