Plastic bag production technology
A production process and technology of plastic bags, applied in the direction of bags, sacks, biological packaging, etc., can solve the problems of whether the equipment technology can meet the requirements, unclear production conditions, physical health threats, etc., to achieve low cost and enhance heat resistance. , the effect of accelerated degradation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1:
[0020] A kind of plastic bag production process of the present embodiment is characterized in that, its process steps are as follows:
[0021] (1) Screening of raw materials: the plastic particles are screened by an 80-mesh sieve, and the plastic particles are polylactic acid particles;
[0022] (2) Melting: Add the target particles screened in step (1) into the reactor, control the temperature at 175°C, and melt the target particles into a molten state under stirring conditions;
[0023] (3) Modification: add the modified material into the molten liquid in step (2), and mix evenly, the modified material is a mixture of magnesium-aluminum hydrotalcite, ammonium polyphosphate, and cobalt powder, and the mixing ratio is 2 :1:1, the content of the mixture is 2% of the melt;
[0024] (4) Film blowing: the mixed melt in step (3) is formed into a plastic film by a film blowing machine;
[0025] (5) Color printing: The pattern set according to the requirements...
Example Embodiment
[0028] Example 2 : the rest are the same as described in Example 1, except that step (1) is changed to a 150-mesh sieve, the content of the mixture in step (3) is 3% of the melt, and in step (1), the The plastic particles are polylactic acid particles.
Example Embodiment
[0029] Example 3: The rest are the same as described in Example 1, except that, in step (3), the content of the mixture is 5% of the melt, and in step (3), the modification condition is vacuum stirring.
[0030] Example 1 Example 2 Example 3 Complete melting time of plastic pellets 50min 35min 55min Complete degradation time of plastic bags 35d 28d 20d
[0031] Through the above three examples, there are three sets of data in the above table, it can be known that when the plastic particles are controlled at 120 mesh, the particle melting speed is the fastest, and when the modified material content is 5%, the complete degradation time of the plastic bag is the shortest.
[0032] The present invention completes the production process of the plastic bag through seven steps of screening, melting, modification, film blowing, color printing, slitting and bag making of the raw materials of the polylactic acid plastic particles, so that the pro...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap