Wear-resistant manual surfacing electrode
A surfacing electrode and manual technology, applied in the direction of welding medium, manufacturing tools, welding equipment, etc., can solve the problems of mechanical inoperability, friction, damage of impact parts, wear resistance and corrosion resistance of the cladding layer, etc., and achieve arc light Soft, beautiful weld shape, excellent welding performance
Inactive Publication Date: 2014-03-26
QINGDAO HAIBAN PLASTIC IND & TRADE
View PDF0 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The existing surfacing welding electrodes mainly achieve the required hardness by adding tungsten carbide particles or increasing the carbon content, which has a problem, that is, the wear resistance and corrosion resistance of the cladding layer are prone to decline under high temperature conditions. , so that the friction and impact parts are damaged, and the machine cannot be used
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] A wear-resistant manual surfacing welding electrode, which consists of the following ingredients in parts by weight:
[0019] 10-20 parts of ferroboron;
[0020] 3-8 parts of silicon;
[0021] 2 to 6 parts of barium carbonate;
[0022] Charcoal 5-12 parts;
[0023] 4-9 parts of high-carbon ferrochrome;
[0024] 2 to 5 parts of nickel powder;
[0025] 3-8 parts of ferro-titanium;
[0026] 5-14 parts of cellulose;
[0027] 6-8 parts of microcrystalline graphite;
[0028] 10-12 parts of rutile.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention discloses a wear-resistant manual surfacing electrode. The wear-resistant manual surfacing electrode is composed of, by weight, 10-20 parts of ferroboron, 3-8 parts of silicon, 2-6 parts of barium carbonate, 5-12 parts of carbon, 4-9 parts of high carbon ferro-chrome, 2-5 parts of nickel powder, 3-8 parts of ferrotitanium, 5-14 parts of cellulose, 6-8 parts of amorphous graphite and 10-12 parts of rutile. Because a substrate of the surfacing electrode is made of cobalt, good wear resistance and good corrosion resistance can stilled be kept when the surfacing electrode works under the temperature of about 650DEG C; meanwhile, the surfacing electrode is good in welding operation performance and has the advantages that electric arcs are stable, arc light is soft, spatter is small, slag detachability is good, the appearance of weld joints is attractive and welding performance is good.
Description
technical field [0001] The invention belongs to the field of welding materials, in particular to an electrode, in particular to a wear-resistant manual surfacing electrode. Background technique [0002] Overlay welding is a welding process that deposits a layer of wear-resistant, corrosion-resistant, heat-resistant metal layers on the surface or edge of the workpiece. Surfacing welding can improve the service life of parts, use materials reasonably, improve product performance and reduce costs, and has significant economic benefits. In industrial production, welding technology such as surfacing welding is developing rapidly. Surfacing welding materials are divided into three categories: manual welding rods, welding wires, and strip welding strips. Among the hardfacing surfacing materials in my country, surfacing electrodes account for about 70%, surfacing welding wire accounts for about 25%, and welding strips account for about 5%. It can be seen that the surfacing electro...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K35/36
CPCB23K35/3053
Inventor 张雪燕
Owner QINGDAO HAIBAN PLASTIC IND & TRADE
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap