Water-soluble fluorine-containing modified N-NVP polymer and preparation method thereof

A technology of vinylpyrrolidone and water-soluble polymers, which is applied in the field of water-soluble polymer synthesis, can solve the problems of low product surface activity and high content of hydrocarbon side chain monomers, and achieve simple and easy operation of the product post-processing process, raw materials Easy to obtain, high conversion rate of monomer

Active Publication Date: 2014-03-26
SHANDONG UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hydrophobic association ability of vinylpyrrolidone polymers can be improved by traditionally using conventional hydrophobic segments to modify polymers, but the monomer content of the required hydrocarbon side chains is high, and the surface activity of the obtained products is not high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-soluble fluorine-containing modified N-NVP polymer and preparation method thereof
  • Water-soluble fluorine-containing modified N-NVP polymer and preparation method thereof
  • Water-soluble fluorine-containing modified N-NVP polymer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A preparation method of a water-soluble polymer containing fluorine-modified N-vinylpyrrolidone, the steps are as follows:

[0052] (1) Weigh 8.3g (0.07477mol) of N-vinylpyrrolidone (NVP) monomer, and measure 50mL of toluene, add it into a 100mL three-necked flask equipped with a nitrogen tube, a condenser tube and a stirring bar, and stir until completely dissolved;

[0053] (2) Weigh 0.09 g (0.225 mmol) of dodecafluoroheptyl methacrylate (DFMA), add it into a three-neck flask, fill it with nitrogen gas at room temperature, and fully stir until dissolved;

[0054] (3) Weigh 0.0839 g of azobisisobutyronitrile, add it to a three-neck flask, put it in a constant temperature water bath at 25°C, and blow nitrogen gas for 0.5 h;

[0055] (4) Raise the reaction temperature to 85°C and react for 8 hours to obtain a water-soluble polymer containing fluorine-modified N-vinylpyrrolidone.

[0056] Subsequent treatment: the water-soluble polymer of fluorine-modified N-vinylpyrrolid...

Embodiment 2

[0060] As described in Example 1, the difference is that the amount of N-vinylpyrrolidone monomer in step (1) is 11.1 g;

[0061] The feeding amount of monomer dodecafluoroheptyl methacrylate (DFMA) in step (2) is 0.2 g.

[0062] 10.012 g of water-soluble polymer powder containing fluorine-modified N-vinylpyrrolidone was obtained, and the yield was ≥88%. Molecular weight M w =(2.291±0.609)×10 5 g·mol -1 .

[0063] The water-soluble polymer containing fluorine-modified N-vinylpyrrolidone prepared in this example has high surface activity at room temperature, the concentration of its aqueous solution is 10 mg / mL, and the surface tension of the aqueous solution can be reduced to 33 mN / m.

Embodiment 3

[0065] As described in Example 1, the difference is that the amount of N-vinylpyrrolidone monomer in step (1) is 7.87g;

[0066] The feeding amount of monomer dodecafluoroheptyl methacrylate (DFMA) in step (2) is 0.2 g.

[0067] 6.983 g of water-soluble polymer powder containing fluorine-modified N-vinylpyrrolidone was obtained, and the yield was ≥86%. Molecular weight M w =(2.380±0.426)×10 5 g·mol -1 .

[0068] The water-soluble polymer containing fluorine-modified N-vinylpyrrolidone prepared in this example has high surface activity at room temperature, the concentration of its aqueous solution is 10 mg / mL, and the surface tension of the aqueous solution can be reduced to 33 mN / m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
surface tensionaaaaaaaaaa
surface tensionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-soluble fluorine-containing modified N-NVP polymer and a preparation method thereof. The preparation method comprises the step: N-NVP and DFMA are subjected to a polymeric reaction to obtain the compound shown as the formula (I). According to the invention, as a fluorine-containing hydrophobic alkyl side chain is introduced to the water-soluble N-NVP polymer, the N-NVP polymer has the advantages of excellent hydrophobic association property, high surface activity, and excellent salt, temperature and shear resistant properties, can serve as a macromolecular surfactant, and meanwhile has a high utilization potentiality in the fields of oil exploitation, paints, medicines, daily chemicals and the like.

Description

technical field [0001] The invention relates to a water-soluble polymer containing fluorine-modified N-vinylpyrrolidone and a preparation method thereof, in particular to a water-soluble polyN-vinylpyrrolidone (NVP) / dodecafluoroheptyl methacrylate (DFMA) A polymer and a preparation method thereof belong to the technical field of water-soluble polymer synthesis. Background technique [0002] Since polyvinylpyrrolidone and vinylpyrrolidone copolymers have many excellent physical and chemical properties, such as excellent solubility, low toxicity, film-forming properties, solubilization, complexation, physiological compatibility, surface activity and chemical stability etc. Therefore, it is widely used in medical and health care, cosmetics, food, beverage, brewing, papermaking, textile printing and dyeing, new materials, suspension and emulsion polymerization, dispersion stability and other fields, and has attracted more and more attention from scientific researchers. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F226/10C08F220/22C08F2/06
Inventor 谭业邦崔士红
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com