Nanometer solvent-free epoxy antirust paint and preparation method thereof

A solvent-free, anti-rust paint technology, applied in the field of chemical coatings, can solve problems such as hindering development and application, and achieve the effects of excellent wear resistance, easy maintenance, and convenient construction

Active Publication Date: 2014-04-09
FOSHAN GAOMING FULITE CHEM CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, due to the irrationality of its formulation, the solvent-free antirust paint of the prior

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A kind of nanometer epoxy solvent-free epoxy antirust paint, it comprises each raw material component of following weight part:

[0053] Component A: 30 parts of E-44 epoxy resin;

[0054] 8 parts of reactive diluent propylene oxide butyl ether;

[0055] 16 parts of zinc phosphate;

[0056] 15 parts of mica powder;

[0057] 26 parts of nano-alumina;

[0058] 17 parts of iron oxide red powder;

[0059] 5-10 parts of aluminum tripolyphosphate;

[0060] Component B: 18 parts of curing agent modified alicyclic amine;

[0061] The preparation method of above-mentioned nano solvent-free epoxy antirust paint is:

[0062] Weigh each raw material component of formula quantity respectively, component A: E-44 epoxy resin, reactive diluent propylene oxide butyl ether, zinc phosphate, nano-alumina, iron oxide red powder and aluminum tripolyphosphate, and use high-speed Stir for 30-50 minutes at a speed of 500-1500 rev / min in the disperser; grind to a fineness below 40um with ...

Embodiment 2

[0064]A kind of nanometer epoxy solvent-free epoxy antirust paint, it comprises each raw material component of following weight part:

[0065] Component A: 30 parts of E-44 epoxy resin;

[0066] 8 parts of active diluent;

[0067] 16 parts of zinc phosphate;

[0068] 5 parts of mica powder;

[0069] 16 parts of nano-alumina;

[0070] 17 parts of iron oxide red powder;

[0071] 8 parts of aluminum tripolyphosphate;

[0072] Component B: 15 parts of curing agent modified alicyclic amine;

[0073] Weigh each raw material component of formula quantity respectively, component A: E-44 epoxy resin, reactive diluent propylene oxide butyl ether, zinc phosphate, nano-alumina, iron oxide red powder and aluminum tripolyphosphate, and use high-speed Stir for 30-50 minutes at a speed of 500-1500 rev / min in the disperser; grind to a fineness below 40um with a sand mill; filter and package the ground paint with component B: curing agent modified alicyclic amine.

Embodiment 3

[0075] A kind of nanometer epoxy solvent-free epoxy antirust paint, it comprises each raw material component of following weight part:

[0076] 40 parts of E-44 epoxy resin;

[0077] Propylene oxide butyl ether is 5 parts of active diluent;

[0078] 20 parts of zinc phosphate;

[0079] 20 parts of mica powder;

[0080] 30 parts of nano-alumina;

[0081] 10 parts of iron oxide red powder;

[0082] Component B: 15 parts of curing agent modified alicyclic amine;

[0083] Weigh each raw material component of formula quantity respectively, component A: E-44 epoxy resin, reactive diluent propylene oxide butyl ether, zinc phosphate, nano-alumina, iron oxide red powder and aluminum tripolyphosphate, and use high-speed Stir for 30-50 minutes at a speed of 500-1500 rev / min in the disperser; grind to a fineness below 40um with a sand mill; filter and package the ground paint with component B: curing agent modified amine fruit phenol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses nanometer solvent-free epoxy antirust paint and a preparation method thereof. The nanometer solvent-free epoxy antirust paint comprises the following raw material components in parts by weight: component A: 20-40 parts of E-44 epoxy resin, 5-15 parts of active diluent, 10-20 parts of zinc phosphate, 5-20 parts of mica powder, 10-20 parts of nanometer alumina, 10-20 parts of ferric oxide powder and 5-10 parts of aluminum triphosphate; component B: alicyclic amine or anacardol serving as a curing agent. The weight ratio of the component A to the component B is (6-8): 1. The nanometer solvent-free epoxy antirust paint disclosed by the invention is good in antirust property, environment-friendly, free of VOC emission, not harsh in construction conditions and low in requirements on base material, and the paint can be thickly coated once; the nanometer solvent-free epoxy antirust paint can be widely applied to a variety of fields, for example, bridge, guardrail steel structure, building material, machinery, etc.

Description

technical field [0001] The invention relates to an anti-corrosion coating, which belongs to the technical field of chemical coatings, in particular to a nano-solvent-free epoxy anti-rust paint and a preparation method thereof. Background technique [0002] Solvent-free epoxy liquid anti-corrosion paint / anti-corrosion coating is a high solids, room temperature curing (hardening) solvent-free epoxy anti-corrosion coating. It has the advantages of oil resistance, chemical resistance, wear resistance, impact resistance, and easy cleaning. It has strong adhesion to the substrate and is convenient for construction. It can be made into coatings of different thicknesses according to the needs of users. [0003] The above-mentioned anti-corrosion coating or anti-corrosion paint is a high-performance anti-corrosion coating, which has good chemical resistance, water resistance and good abrasion resistance. It is suitable for ships, ports, railway bridges, petroleum, chemical smelting,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D7/12C09D5/08
Inventor 严易舒尹华忠
Owner FOSHAN GAOMING FULITE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap