A technology of nitrile rubber and cis-butadiene rubber is applied in the field of nitrile rubber to achieve the effects of good wear resistance, excellent cold resistance and long service life

Inactive Publication Date: 2014-06-18
ANHUI SHENGDONG CHEM
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing seal materials include metallic materials, such as aluminum, lead, indium, stainless steel, etc., and non-metallic materials, such as rubber, plastic, ceramics, graphite, etc., but currently the most used non-metallic rubber materials, excellent sealing performance Inferiority depends to a large extent on the performance of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] A combination of high-strength and cold-resistant nitrile rubber and butadiene rubber, the raw materials of which comprise in parts by weight:

[0016] 67 parts of nitrile rubber, 35 parts of butadiene rubber, 2.6 parts of sulfur, 3 parts of zinc oxide, 1.15 parts of antioxidant OPPD, 1.2 parts of antioxidant MB, 4 parts of stearic acid, 65 parts of white carbon black, carbon black N33023 Parts, 0.9 parts of dioctyl oxalate, 0.9 parts of accelerator DBX, 0.3 parts of benzylamine, 1.1 parts of γ-aminopropyl triethoxysilane, 1.1 parts of processing aid WB212, 4 parts of light calcium carbonate Part, 35 parts of mixed gas carbon black, of which the content of acrylonitrile in nitrile rubber is 380%.

Example Embodiment

[0017] Example 2

[0018] A combination of high-strength cold-resistant nitrile rubber and butadiene rubber, the raw materials of which comprise by weight:

[0019] 70 parts of nitrile rubber, 26 parts of butadiene rubber, 2.5 parts of sulfur, 2.5 parts of zinc oxide, 1.2 parts of antioxidant OPPD, 0.85 parts of antioxidant MB, 6 parts of stearic acid, 67 parts of white carbon black, carbon black N33037 Parts, 0.8 parts of dioctyl oxalate, 1.1 parts of accelerator DBX, 0.35 parts of benzylamine, 1.1 parts of γ-aminopropyltriethoxysilane, 1.2 parts of processing aid WB212, 4 parts of light calcium carbonate The content of acrylonitrile in the nitrile rubber is 38.2%.

Example Embodiment

[0020] Example 3

[0021] A combination of high-strength cold-resistant nitrile rubber and butadiene rubber, the raw materials of which comprise by weight:

[0022] 67 parts of nitrile rubber, 38 parts of butadiene rubber, 3 parts of sulfur, 3 parts of zinc oxide, 1.1 parts of antioxidant OPPD, 0.7 parts of antioxidant MB, 5 parts of stearic acid, 68 parts of white carbon black, carbon black N33027 Parts, 0.85 parts of dioctyl oxalate, 1.12 parts of accelerator DBX, 0.35 parts of benzylamine, 1.1 parts of γ-aminopropyltriethoxysilane, 1.25 parts of processing aid WB212, 3.4 parts of light calcium carbonate The content of acrylonitrile in the nitrile rubber is 39%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composition of high-strength and cold-resistant butadiene-acrylonitrile rubber and butadiene rubber. The composition comprises the raw materials in parts by weight: 60-70 parts by weight of butadiene-acrylonitrile rubber, 20-40 parts by weight of butadiene rubber, 2-3 parts by weight of sulphur, 2-4 parts by weight of zinc oxide, 0.8-1.2 parts by weight of anti-aging agent OPPD, 0.4-1.3 parts by weight of anti-aging agent MB, 3-7 parts by weight of stearic acid, 50-70 parts by weight of white carbon black, 20-30 parts by weight of carbon black N330, 0.7-1 part by weight of dioctyl adipate, 0.8-1.2 parts by weight of accelerant DBX, 0.2-0.4 part by weight of benzyl amine, 0.8-1.2 parts by weight of gamma-aminopropyl triethoxysilane, 1.1-1.3 parts by weight of processing agent WB212, 3-4 parts by weight of light calcium carbonate and 20-40 parts by weight of mixed gas carbon black. In the invention, the composition of high-strength and cold-resistant butadiene-acrylonitrile rubber and butadiene rubber is excellent in cold resistance, good in wear resistance, and longer in service life.

Description

technical field [0001] The invention relates to the technical field of nitrile rubber, in particular to a composition of high-strength cold-resistant nitrile rubber and butadiene rubber. Background technique [0002] Sealing materials refer to materials that can withstand joint displacement to achieve airtightness and watertightness and are embedded in building joints. Early sealing materials are mainly fabrics, mineral fibers or felts. With the development of industrial technology, in order to meet the increasingly complex and diverse requirements of hydraulic and pneumatic seals, sealing materials have also developed rapidly, with more and more types and continuous improvement in physical and chemical properties. [0003] Existing seal materials include metallic materials, such as aluminum, lead, indium, stainless steel, etc., and non-metallic materials, such as rubber, plastic, ceramics, graphite, etc., but currently the most used non-metallic rubber materials, excellent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08L9/00C08K13/02C08K3/06C08K3/22C08K5/09C08K3/36C08K3/04C08K5/544C08K3/26C08K5/11
Inventor 刘建荣赵峰方光东
Owner ANHUI SHENGDONG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap