Coated aluminum substrate for drilling PCB (Printed Circuit Board) and preparation method of coated aluminum substrate
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of coated aluminum substrate and aluminum foil, which is applied in the field of PCB manufacturing, can solve the problems of easy loss of drill pins, low drilling efficiency, and low drilling accuracy, so as to prolong the life of drill pins, improve the quality of hole walls, and have good water solubility Effect
Active Publication Date: 2014-07-23
烟台柳鑫新材料科技有限公司
View PDF4 Cites 15 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a film-coated aluminum substrate for PCB drilling and its preparation method, aiming to solve the problems caused by the current aluminum foil for PCB drilling, such as low drilling accuracy and low drilling efficiency. , The problem of easy loss of drill needles
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] Take 40 parts by weight of polyurethane, acrylic ester, water-based phenolic resin, and water-based epoxy resin in 2 or more materials to form component A1, and then take 55 parts by weight of polyethylene oxide, polyethylene Two or more materials in glycol, glycerin, vinyl acetate, and polyvinyl alcohol form component A2, and then take 5 parts by weight of dimethylsiloxane and polyether additives, and the component Divide A1, A2 and additives into an emulsion, and roll-coat it on the surface of aluminum foil and dry it to obtain a finished product.
Embodiment 2
[0028] Take 50 parts by weight of polyurethane, acrylic acid ester, water-based phenolic resin, and water-based epoxy resin in 2 or more materials to form component A1, and then take 42 parts by weight of polyethylene oxide, polyethylene Two or more materials in glycol, glycerin, vinyl acetate, and polyvinyl alcohol form component A2, and then take 8 parts by weight of dimethylsiloxane and polyether additives, and the component Divide A1, A2 and additives into an emulsion, and roll-coat it on the surface of aluminum foil and dry it to obtain a finished product.
Embodiment 3
[0030] Take 35 parts by weight of isocyanate, polyester resin, water-based melamine resin, urea-formaldehyde resin, and acrylates to form component B1, and then take 60 parts by weight of polyethylene oxide , Polyethylene glycol, glycerin, vinyl acetate, polyvinyl alcohol in two or more materials to form component B2, and then take 5 parts by weight of dimethylsiloxane and polyether additives , Mix components B1, B2 and additives into an emulsion, and roll-coat it on the surface of aluminum foil and dry it to obtain a finished product.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a coated aluminum substrate for drilling a PCB (Printed Circuit Board) and a preparation method of the coated aluminum substrate. The method comprises the following steps: taking 40-50 parts by weight of two or more of polyurethane, acrylic ester, aqueous phenolic resin and aqueous epoxy resin to form a component A1, then taking 40-55 parts by weight of two or more of polyoxyethylene, polyethylene glycol, glycerin, vinyl acetate and polyving akohol to form a component A2, taking 5-8 parts by weight of accessory ingredient, mixing the component A1, the component A2 and the accessory ingredient to obtain emulsion, coating the surface of an aluminum foil with the emulsion in a roller coating manner to prepare finished product. By using the characteristics of the surface layer resin of the aluminum foil of low hardness, low melting point, strong cohesive property and excellent water solubility, the coated aluminum substrate for drilling the PCB is capable of improving the drilling precision of a drill point in the drilling process, effectively reducing the working temperature of the drill point, prolonging the service life of the drill point and improving the hole wall quality of the drill hole.
Description
technical field [0001] The invention relates to the technical field of PCB manufacturing, in particular to a film-coated aluminum substrate for PCB drilling and a preparation method thereof. Background technique [0002] At present, most of the PCB drilling holes are uncoated aluminum foil, or a single-function coated aluminum base cover. In the field of drilling, due to the side slip of the drill pin at the moment of contact with the aluminum foil, the deflection of the drill pin is serious, the accuracy of the hole position is low, the corresponding hole wall quality is poor, and the drill pin is also worn; Coated with a layer of resin, the drill needle goes into the drill smoothly without side slipping, but it is similar to ordinary aluminum sheets in terms of hole wall quality and drill wear. Therefore generally speaking, the drilling efficiency of existing cover plates is still relatively low. [0003] Therefore, the prior art still needs to be improved and developed....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more