Completely-biodegradable mulching film material and mulching film

A biodegradable and plastic film technology, applied in plant protection cover, climate change adaptation, etc., can solve the problems of poor heat resistance of plastic film, high cost, immature technology of complete biodegradation of aliphatic carbonate, etc., to reduce white pollution, increase The effect of crop yield

Inactive Publication Date: 2014-07-23
山东省意可曼科技有限公司
View PDF5 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The publication number is CN102311630, and the name is fully biodegradable aliphatic carbonate mulch and its preparation method. The raw materials used are fully biodegradable materials, which can replace traditional mulch and can achie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Weigh 60% of P3HB4HB (12% 4HB), 30% of PLA, 5% of tri-n-butyl citrate, 5% of zinc stearate, put them into a high-speed mixer and stir for 5 minutes, then put them into twin-screw extrusion Granulate in the machine and blow the film with a mulch machine.

Embodiment 2

[0024] Weigh 70% of PHBV (12% HV), 10% of PLA, 10% calcium carbonate, 5% tri-n-butyl citrate, and 5% paraffin into a high-speed mixer and stir for 5 minutes, then put into a twin-screw extruder Granulate in the machine.

Embodiment 3

[0026] 80% PHBH (15% 4HB, 10% PBAT, 8% epoxidized soybean oil, 2% talcum powder are weighed and dropped into a high-speed mixer and stirred for 5min, then dropped into a twin-screw extruder for granulation, Film blowing machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a completely-biodegradable mulching film material which contains one kind or several kinds of compounds which are selected from a group consisting of polyhydroxy alkanoates, polylactic acid, poly(butylene adipate-co-terephthalate), poly(butylene-scuccinate/adipate) and poly(butylene-scuccinate). By adopting the completely biodegradable mulching film material, the yield of crops can be greatly improved, the mulching film material can be completely biodegradable without residues of a mulching film, and the yield of crops can be continuously increased.

Description

【Technical field】 [0001] The invention relates to a mulch material, in particular to a completely biodegradable mulch material. 【Background technique】 [0002] Since the plastic film mulching cultivation technology was tested, applied and promoted in China, it has become an important technology for increasing agricultural production. However, since most of the current mulch films are polyethylene or polyvinyl chloride mulch films, their stability is extremely high, and the degradation process is quite slow, about 100 years; the fragments remaining in the soil cannot be degraded by soil microorganisms, nor can they be absorbed and utilized by crops. Especially the manufacture of ultra-thin plastic film, although the amount of plastic film per unit area can be relatively reduced and the cost can be reduced, but the thinner the plastic film, the easier it is to break. bring great difficulty. With the extensive use of plastic mulch, the accumulation of residual plastic mulch i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L67/02C08K5/11C08K5/098C08K3/26C08K5/1515C08K3/34A01G13/02
CPCY02A40/28
Inventor 钟路华蓝小平谭观岳孙西明
Owner 山东省意可曼科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap