High-filling heatproof polypropylene composite material used for environmental protection wallpaper and preparation method thereof

A composite material, polypropylene technology, applied in the field of heat-resistant, environmentally friendly polypropylene composite materials for wallpaper, high filling, can solve the problems of temperature difference, difficult to process three-dimensional patterns, complex production process, etc., achieve low density, elongation at break, etc. High rate and good strength

Inactive Publication Date: 2014-07-30
HEFEI GENIUS NEW MATERIALS
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production process of this kind of wallpaper is complicated, and it still needs to use the plant fiber layer as the base layer. This kind of wallpaper is resistant to temperature difference, and it is not easy to process rich three-dimensional patterns.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Weigh 20 parts of dry polypropylene K8303 (Yangzi Petrochemical), 80 parts of calcium carbonate, 0.1 part of antioxidant 1010, 0.1 part of antioxidant DSTDP, lubricant EBS (N,N' -Ethylene bis stearamide) 0.2 parts, silicone powder 0.3 parts, coupling agent KH550 0.5 parts, put the above materials into the banburying room in turn, the temperature in the banburying room is 170°C, the speed is 40rpm, banburying 2min , and then put the uniformly mixed material into a twin-screw extruder, melt and extrude, and then water-cooled, and cut into particles with a length of 2mm by a pelletizer to obtain the final product. Among them, the processing temperature of the extruder is 180°C, 195°C, 210°C, 210°C, and 220°C from the feeding port to the die port in sequence, the speed of the main machine is 70rpm, and the vacuum degree is 0.3MPa.

Embodiment 2

[0033] Weigh 15 parts of dry copolymerized polypropylene T30S (Maoming Petrochemical), 85 parts of diatomite, 0.1 part of antioxidant 1010, 0.3 part of antioxidant 168, 0.2 part of lubricant EBS, and even The joint agent AC201 is 0.1 part, and the above materials are sequentially added into the banburying room, the temperature in the banburying room is 160°C, the rotation speed is 50rpm, and banburying is carried out for 4min. Melt extruded, then water-cooled, cut into particles with a length of 3 mm by a pelletizer to obtain the final product. Among them, the processing temperature of the extruder is 180°C, 195°C, 210°C, 210°C, 220°C from the feeding port to the die port in sequence, the main engine speed is 60rpm, and the vacuum degree is 0.3MPa.

Embodiment 3

[0035] Weigh 25 parts of dry polypropylene B8101 (Yanshan Petrochemical), 75 parts of calcium carbonate, 0.1 part of antioxidant 1010, 0.2 part of antioxidant 168, 0.1 part of lubricant EBS, coupling 0.2 parts of antistatic agent AC201, 0.5 parts of antistatic agent glycerol monostearyl (129), respectively add the above materials into the banburying room, the temperature in the banburying room is 170°C, the speed is 50rpm, banburying for 6min, and then mixing The uniformly refined material is put into a twin-screw extruder, melted and extruded, and then water-cooled, and cut into particles with a length of 2mm by a pelletizer to obtain the final product. Among them, the processing temperature of the extruder is 180°C, 195°C, 210°C, 210°C, 220°C from the feeding port to the die port in sequence, the main engine speed is 50rpm, and the vacuum degree is 0.3MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Heat distortion temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-filling heatproof polypropylene composite material used for environmental protection wallpaper and a preparation method thereof, the composite material is prepared by 15-40 parts of polypropylene, 60-85 parts of inorganic powder, 0.1-0.6 parts of coupling agent, 0.1-0.4 parts of anti-oxidant, 0.1-0.5 parts of lubricant and 0-2 parts of other auxiliary agents according to weight. The composite material has the advantages of high filler content, high applicable temperature and green environmental protection, can replace the plant fiber to produce the wallpaper, and reduces the tree felling; the composite material can prepare a lightweight, heatproof and environmental protection wallpaper base layer through film blowing; and the material preparation technology has the advantages of controllable process, low production cost and no secondary pollution.

Description

[0001] technical field [0002] The invention belongs to the technical field of polymer composite materials, and in particular relates to a high-filling, heat-resistant and environmentally friendly polypropylene composite material for wallpaper. [0003] technical background [0004] Wall decoration wallpaper is a commonly used wall decoration material for homes and hotels. At present, the widely used decorative wallpaper substrates are mainly divided into three categories: the first is the wallpaper substrate produced from paper pulp and wood pulp. Natural resources such as trees consume a lot of water in the papermaking process; the other is to apply a layer of polyvinyl chloride (PVC) emulsion on the paper surface of the base paper, and then prepare the wallpaper base layer by scraping and embossing. However, since the PVC material itself is hard and difficult to color, it is necessary to add a large amount of dioctyl phthalate (DOP) plasticizers and dyeing aids when ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/14C08K13/02C08K3/26C08K3/34B29B7/00B29B9/06
CPCC08L23/14B29B9/06B29C48/92B29C2948/9258B29C2948/92704C08K3/26C08K3/34C08K13/02C08K2003/265C08L2201/08C08L2203/14C08L2203/16C08L83/04
Inventor 杨桂生汪海姚晨光
Owner HEFEI GENIUS NEW MATERIALS
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com