Preparation method for milk protein composite fiber, milk protein composite fiber and application

A milk protein and composite fiber technology is applied in the preparation of milk protein composite fibers, milk protein composite fibers and application fields, which can solve the problems of high cost of chemical fibers and insufficient comfort, and achieves strong process operability and repeatability. Strong and dimensional stability

Active Publication Date: 2014-08-27
COSMO LADY (CHINA) HOLDINGS
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The problem to be solved by the present invention is that the present invention provides a kind of milk protein composite fiber with good skin affinity and low price, aiming at the problems of high cost of existing chemical fibers, insufficient comfort, and skin-friendly properties of plant fibers. Preparation method, milk protein composite fiber and application thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for milk protein composite fiber, milk protein composite fiber and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] see figure 1 , shows the flow chart of the milk protein composite fiber preparation method of the embodiment of the present invention, the method includes the following steps:

[0025] 1) Pretreatment of cotton fiber: add sodium hydroxide solution to cotton fiber, at room temperature, ultrasonically vibrate for 30-50s, filter and rinse;

[0026] 2) Reduction of cotton fibers: adding the cotton fibers treated in step 1) into the sodium periodate solution, stirring for 2-4 hours, filtering, and rinsing to obtain modified cotton fibers;

[0027] 3) Preparation of milk protein liquid: prepare sodium hydroxide solution, add olive oil to the sodium hydroxide solution, stir and mix at 30-50°C for 3-10 hours, then add milk, stir for 5-30 minutes, filter to remove solid matter to obtain milk protein liquid, and the amount of olive oil is 2 to 3 times of the weight of the sodium hydroxide solution;

[0028] 4) Add the modified cotton fiber prepared in step 2) to the milk protei...

Embodiment 2

[0040] The milk protein composite fiber preparation method, fiber and application provided in this example are basically the same as those in Example 1, except that:

[0041] 1) Pretreatment of cotton fibers: adding a sodium hydroxide solution with a concentration of 15% by weight into the cotton fibers, the sodium hydroxide solution will completely immerse the cotton fibers, at room temperature, ultrasonically vibrate for 30s, filter, and rinse with deionized water 3 times;

[0042] 2) Reduction of cotton fiber: immerse the cotton fiber treated in step 1) into a sodium periodate solution with a concentration of 0.05% by weight, under dark conditions, stir and react for 2h, filter, and rinse with deionized water for 5 times , to obtain modified cotton fiber;

[0043] 3) Preparation of milk protein liquid: prepare sodium hydroxide solution, add olive oil to the sodium hydroxide solution, stir and mix at 30°C for 3 hours, then add milk, stir for 5 minutes, filter to remove solids...

Embodiment 3

[0047] The milk protein composite fiber preparation method, fiber and application provided in this example are basically the same as those in Example 1 or 2, except that:

[0048] 1) Pretreatment of cotton fiber: adding a sodium hydroxide solution with a weight percentage concentration of 20% to the cotton fiber, the sodium hydroxide solution will completely immerse the cotton fiber, at room temperature, ultrasonically vibrate for 40s, filter, and rinse with deionized water 3 times;

[0049] 2) Reduction of cotton fiber: immerse the cotton fiber treated in step 1) into a sodium periodate solution with a concentration of 0.12% by weight, under dark conditions, stir and react for 3h, filter, and rinse with deionized water for 5 times , to obtain modified cotton fiber;

[0050] 3) Preparation of milk protein liquid: configure sodium hydroxide solution, add olive oil to the sodium hydroxide solution, stir and mix at 40°C for 8 hours, then add milk, stir for 20 minutes, filter to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A provided preparation method for milk protein composite fiber comprises the following steps: pre-treatment on cotton fiber, preparation of a reduction milk protein solution of cotton fiber, and preparation of milk protein composite fiber. The preparation method for the milk protein composite fiber is easily available in raw materials, compact in reaction steps, easily controllable in process and strong in technology maneuverability and repeatability. The invention also provides the milk protein composite fiber which comprises cotton fiber at the core and milk protein at the external surface of cotton fiber, and application of the milk protein composite fiber as a clothes material. When a garment made from the provided composite fiber is worn on a body, milk protein directly contacts skin, the skin-friendly property is better than that of conventional plant fiber, and also the garment has gloss of silk and is strong in sweat absorbing property, good in dimension stability and low in cost. According to the application of the milk protein composite fiber, the milk protein composite fiber is applicable to prepare intimate apparels, such as bras, underpants, small vests and summer clothes.

Description

technical field [0001] The invention relates to the field of textile industrial materials, in particular to a preparation method of milk protein composite fiber, milk protein composite fiber and application thereof. Background technique [0002] Nowadays, with the decrease of fossil fuels such as petroleum, the price has also risen accordingly, and the cost of synthetic fibers that completely rely on fossil fuels has also gradually increased, and the growth of quantity is greatly restricted. On the other hand, synthetic fibers also have their natural shortcomings. , such as poor skin affinity, and the comfort is inferior to natural fibers. Therefore, natural fibers have become the first choice for people to pursue a comfortable life. However, natural fibers such as silk are expensive, and the skin-friendly properties of cotton are not perfect. Therefore, natural functional textiles have gradually become the mainstream of the market. How to restructure or modify existing natu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/15D06M101/06
Inventor 李昌平沈玉姬莫惠西廖丽容
Owner COSMO LADY (CHINA) HOLDINGS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap