Environment-friendly building board and preparation method thereof

A technology for building panels and environmental protection, applied in the field of environmentally friendly building panels and its preparation, can solve the problems that building panels cannot meet environmental protection and light weight, and achieve good performance, lower temperature and energy consumption, and low energy consumption.

Active Publication Date: 2014-09-03
GUANGDONG NO 1 CONSTRUCTION ENGINEERING CO LTD
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For this reason, the technical problem to be solved by the present invention lies in the fact that the building panels in the prior art cannot meet the performance requirements of environmental protection and light weight, and then provide an environmentally friendly building panel that can be used for outdoor wall insulation and indoor wall insulation. The above-mentioned boards have the properties of light weight, heat preservation and high strength, and can meet the environmental protection requirements of indoor construction at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly building board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0028] Cement 5kg, coal gangue 12kg, fly ash 4kg, paraffin 8kg, urea 7kg, sulfomethyl phenolic resin 8kg, glass fiber 6kg, bentonite 15kg, methylcellulose 3kg, mullite 5kg, medical stone 2kg, zeolite 5kg , sulfomethyl lignite 1kg, hydroxyethyl cellulose 15 and blowing agent 0.5kg.

[0029] The environmentally friendly building panels described in this example are prepared by the following steps:

[0030] (1) Get the blowing agent of described cement, coal gangue, fly ash, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and selected weight 1 / 4 according to the selected weight, mix well And sieve, set aside;

[0031] (2) Take the paraffin, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected parts by weight, mix well and heat to...

Embodiment 2

[0036] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0037] Cement 10kg, coal gangue 3kg, fly ash 15kg, paraffin 2kg, urea 13kg, sulfomethyl phenolic resin 4kg, glass fiber 14kg, bentonite 8kg, methylcellulose 9kg, mullite 1kg, medical stone 5kg, zeolite 2kg , sulfomethyl lignite 6kg, hydroxyethyl cellulose 4kg and blowing agent 1.5kg.

[0038] The environmentally friendly building panels described in this example are prepared by the following steps:

[0039] (1) Get described cement, coal gangue, fly ash, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and foamed 1 / 3 of selected parts by weight according to selected parts by weight agent, mixed and sieved, set aside;

[0040] (2) Take the paraffin, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected parts by weight, mix well a...

Embodiment 3

[0045] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0046] Cement 6kg, coal gangue 10kg, fly ash 7kg, paraffin 6kg, urea 9kg, sulfomethyl phenolic resin 7kg, glass fiber 9kg, bentonite 13kg, methylcellulose 5kg, mullite 4g, medical stone 3kg, zeolite 4kg , sulfomethyl lignite 2kg, hydroxyethyl cellulose 11kg and blowing agent 0.7kg.

[0047] The environmentally friendly building panels described in this example are prepared by the following steps:

[0048](1) get described cement, coal gangue, fly ash, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and the whipping agent of 30% of selected parts by weight according to the selected weight, mix Mix well and sieve, set aside;

[0049] (2) Take the paraffin wax, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected weight, mix and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of building materials and in particular relates to a lightweight, thermal-insulation and high-strength green environment-friendly building board and a preparation method thereof. The environment-friendly building board comprises the following components in parts by weight: 5-10 parts of cement, 3-12 parts of coal gangue, 4-15 parts of coal ash, 2-8 parts of paraffin, 7-13 parts of urea, 4-8 parts of sulfomethylated phenolic resin, 6-14 parts of glass fiber, 8-15 parts of bentonite, 3-9 parts of methyl cellulose, 1-5 parts of mullite, 2-5 parts of medical stone, 2-5 parts of zeolite, 1-6 parts of sulfonylmethyl lignite, 4-15 parts of hydroxyethyl cellulose, and 0.5-1.5 parts of a foaming agent. The environment-friendly building board disclosed by the invention has the advantages of lightweight, excellent thermal-insulation, fire-proof and high-strength performances, which are much higher than the requirements of national and industry standards.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a light-weight, heat-preserving and high-strength environment-friendly building board and a preparation method thereof. Background technique [0002] With the rapid development of social economy, more and more buildings have sprung up, showing high-level requirements for "building height, building form and building quality". Among them, building insulation is a measure to reduce the indoor heat dissipation of buildings to the outside. It plays an important role in creating a suitable indoor thermal environment and saving energy. It is also an important requirement and guarantee for building quality. [0003] According to the different construction locations, building environmental protection measures are mainly divided into two methods: the external structure of the building and the internal wall of the building. Among them, building insulation from the peripheral c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/00
Inventor 王茜南王永和
Owner GUANGDONG NO 1 CONSTRUCTION ENGINEERING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com