High dispersion polyethylene coloring masterbatch

A technology for coloring masterbatch and polyethylene, applied in the field of plastic additives, can solve the problems of low dispersibility and weather resistance of masterbatch, and achieve the effects of improving resource utilization, improving wear resistance and anti-aging ability, and improving gloss.

Inactive Publication Date: 2014-09-24
BLUESTAR CHENGDU NEW MATERIALS
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention aims to solve the problem of low dispersibility and weather resistance of the color masterbatch in the prior art, and proposes a high-dispersion polyethylene color masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-dispersion polyethylene color masterbatch, comprising the following raw materials in parts by weight: 30 parts of low-density polyethylene, 10 parts of linear low-density polyethylene, 20 parts of rutile titanium dioxide, 2 parts of wetting agent NP-10, silicon oxide and 4 parts of alumina mixture, 0.5 part of white oil, 1 part of coupling agent, 2 parts of polyethylene wax, 0.1 part of antioxidant 1010, 1 part of calcium carbonate.

[0021] The coupling agent is a zirconium coupling agent or a tin coupling agent.

[0022] Its preparation method comprises the following steps:

[0023] A. Add rutile titanium dioxide and wetting agent NP-10 into the mixer, the mixer speed is 800r / min, after mixing for 4 minutes, add the mixture of coating agent silicon oxide and aluminum oxide, and continue mixing for 18 minutes;

[0024] B. Add low-density polyethylene, linear low-density polyethylene, dispersant polyethylene wax, antioxidant 1010, white oil, coupling agent, and ...

Embodiment 2

[0027] A high-dispersion polyethylene color masterbatch, comprising the following raw materials in parts by weight: 50 parts of low-density polyethylene, 20 parts of linear low-density polyethylene, 35 parts of rutile titanium dioxide, 6 parts of wetting agent NP-10, silicon oxide and 8 parts of alumina mixture, 1 part of white oil, 2 parts of coupling agent, 3 parts of polyethylene wax, 0.8 part of antioxidant 1010, 4 parts of calcium carbonate.

[0028] The ratio of the mixture of silicon oxide and aluminum oxide is 3:1.

[0029] The coupling agent is tin coupling agent.

[0030] The preparation method of this embodiment is the same as that of Example 1.

Embodiment 3

[0032] A high-dispersion polyethylene color masterbatch, comprising the following raw materials in parts by weight: 35 parts of low-density polyethylene, 12 parts of linear low-density polyethylene, 24 parts of rutile titanium dioxide, 3 parts of wetting agent NP-10, silicon oxide and 6 parts of alumina mixture, 0.8 parts of white oil, 1.2 parts of coupling agent, 2 parts of polyethylene wax, 0.5 parts of antioxidant 1010, 3 parts of calcium carbonate.

[0033] The coupling agent is titanate.

[0034] The ratio of the silicon oxide to aluminum oxide mixture is 2:1.

[0035] Its preparation method comprises the following steps:

[0036] A. Add rutile titanium dioxide and wetting agent NP-10 into the mixer, the mixer speed is 700r / min, after mixing for 5 minutes, add the mixture of coating agent silica and alumina, and continue mixing for 16 minutes;

[0037] B. Add low-density polyethylene, linear low-density polyethylene, dispersant polyethylene wax, antioxidant 1010, white ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high dispersion polyethylene coloring masterbatch, including the following raw materials by weight: 30-50 portions of low density polyethylene, 10-20 portions of linear low density polyethylene, 20-35 portions of rutile titanium dioxide, 102-8 portions of a wetting agent NP, 3-8 portions of a mixture of silica and alumina, 0.5-2 portions of white oil, 0.5-2 portions of a coupling agent, 1-3 portions of polyethylene wax, 0.1-1 portion of an antioxidant 1010 and 1-5 portions of calcium carbonate. The invention has the advantages of high dispersion and strong weatherability.

Description

technical field [0001] The invention relates to a color masterbatch, in particular to a high-dispersion polyethylene color masterbatch, which belongs to the technical field of plastic additives. Background technique [0002] The emergence of color masterbatch has brought an innovation to the plastic processing industry. Adding color masterbatch to process plastic products has good dispersibility and no pigment particle pollution during processing, which greatly protects the health of production line workers. However, with the continuous development of the color masterbatch industry, problems have also emerged. Since the color masterbatch is a high-concentration pigment concentrate, when the plastic product is required to be opaque and the proportion is large, the problem of poor dispersion also occurs, especially Color masterbatch for the production of film products. In addition, after long-term use of plastic products, they are easy to become brittle and yellow, which affe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L23/08C08K13/06C08K9/10C08K3/22C08K3/26C08J3/22
CPCC08K2003/2241C08L23/06C08L2205/025C08L2205/03C08L2207/066C08L2310/00C08L23/0815C08K13/06C08K9/10C08K2003/265
Inventor 阎昉邡林杉黄茜
Owner BLUESTAR CHENGDU NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com