Method for preparing high-sensitivity surface enhanced raman scattering (SERS) substrate

A surface-enhanced Raman and high-sensitivity technology, applied in the field of analysis and detection, can solve problems that have not caused researchers, and achieve the effect of improving the probability of being located on a hot spot and high detection sensitivity

Inactive Publication Date: 2014-11-19
JILIN UNIV
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this phenomenon has not attracted widespread attention from researchers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-sensitivity surface enhanced raman scattering (SERS) substrate
  • Method for preparing high-sensitivity surface enhanced raman scattering (SERS) substrate
  • Method for preparing high-sensitivity surface enhanced raman scattering (SERS) substrate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Arranging colloidal balls with a diameter of 360nm on the surface of a silicon chip to form a single-layer colloidal ball array: (1) adding an equal volume of ethanol solution to an aqueous solution of polystyrene colloidal balls with a diameter of 360nm and a concentration of 10wt%, and ultrasonicating for 2h; ( 2) Cleaning the silicon wafers: Sonicate the silicon wafers in acetone, chloroform, ethanol and water for 5 minutes in sequence, and then wash the silicon wafers with a mixed solution of concentrated sulfuric acid (98wt%) and hydrogen peroxide (30wt%) (volume ratio 3:1) Wash at 80°C for 1 h, and finally rinse with deionized water and blow dry with nitrogen; (3) Assembly and transfer of polystyrene colloidal sphere monolayer film: first, add 200 mL of deionized water to a clean watch glass, and Add 20 μL of surfactant (1wt% sodium lauryl sulfate solution); secondly, place the volleyball silicon chip against the edge of the watch glass, so that it is partially imm...

Embodiment 2

[0038] The SERS test was carried out for the suspended nano-antenna with the thickness of the silver film ranging from 20 to 180nm. Figure 4 a shows the SERS spectra of suspended nanoantenna arrays with different silver film thicknesses, and the scale bar in the figure represents 20000 cps. The strongest SERS signal is the suspended nanoantenna structure covered with 95nm silver film. Figure 4 b shows the peak at 1091cm -1The relationship between the SERS intensity and the thickness of the silver film. As the silver film thickness increases from 20nm to 95nm, the SERS intensity increases continuously. However, when the silver film thickness increased from 120nm to 180nm, the SERS intensity decreased continuously.

Embodiment 3

[0040] The near-field distribution on the surface of suspended nanoantennas with different silver film thicknesses was simulated by finite time-domain difference method (Lumerical FDTD Solutions software). In order to make the model closer to the actual sample, each vertex of the triangle is truncated. According to geometrical calculations, for a sphere with a period of 360nm, the side length of each Ag triangle is 177.68nm, and the truncated side length is 10nm. At this time, the gap spacing is 20nm. Similarly, the Au triangle has a side length of 130nm and a truncated side length of 5nm. For the sake of simplicity, the silicon column is replaced by a cylinder with a diameter of 40nm and a height of 80nm. There is an air cavity with the same shape as the silver triangle directly below each suspended triangle, which is located in the silver film and has the same height as the thickness of the evaporated silver film. The refractive indices of Si, Ag, and Au are from the Palik...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a high-sensitivity surface enhanced raman scattering (SERS) substrate and belongs to the technical fields of analysis and detection. The method particularly comprises the step of constructing a suspended nanometer antenna structure array on a silicon substrate, wherein the vibration mode of a metal nanostructure can be controlled through the thickness of evaporation silver; the shape and the vibration mode of a suspended nanometer antenna can mutate with the increase of the thickness of an evaporation silver film; through the mutation, the strength of a hotspot is increased and the hotspot can be moved from the bottom of the nanometer antenna to the top of the nanometer antenna. On the basis, by means of the molecule confinement effect caused by the hydrophobicity of the surface of silver, the possibility that the hotspot comes into contact with a to-be-detected molecule is increased and the detection sensitivity of the SERS substrate is increased; the optimized suspended nanometer antenna structure array has high SERS sensitivity, the maximum SERS enhancement factor is 9.8*10<9> and the minimum detectable concentration is 10<-12>mol / L.

Description

technical field [0001] The invention belongs to the technical field of analysis and detection, and in particular relates to a method for preparing a high-sensitivity surface-enhanced Raman scattering (SERS) substrate. Background technique [0002] Optical nanoantenna is a metal nanostructure that can effectively capture electromagnetic waves at optical frequencies to achieve nanoscale electromagnetic field energy concentration and confinement. Optical nanoantennas usually use slits with very small spacing or tip structures with very small curvature radii to generate extremely small and extremely strong localized electric fields. Such sites are called "hot spots". Gold and silver nano bow tie structures (Nano Lett.2004,4,957; J.Phys.Chem.Lett.2013,4,496; Appl.Phys.Lett.2013,103,041903; Nano Lett.2012,12,796) as a typical The nanoantennas of the present invention generate hotspots by virtue of the tip-to-tip arrangement of two nanotriangular triangles that are very close to e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/65
Inventor 吕男马任平封雷徐大任王燕东刘凌霄
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com