Orange peel glass sheet and preparation method thereof

A glass plate and sheet technology, which is applied in the field of orange peel glass plate and its preparation, can solve the problems of no three-dimensional effect, cracks and bubbles, uneven color, etc., and achieve good transparency and color stability, Long acting time, the effect of improving softness

Active Publication Date: 2014-12-03
DONGGUAN IUIU HOUSEHOLD PROD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing glass sheets have the following disadvantages: the surface is rough, there are cracks and bubbles, the color is uneven, and there is no three-dimensional effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] A kind of orange peel glass plate sheet, comprises the raw material of following weight portion:

[0070] 60 parts of PVC resin

[0071] 30 parts plasticizer

[0072] Impact modifier 5 parts

[0073] 1 heat stabilizer

[0074] 1 part flame retardant

[0075] Anti-ultraviolet agent 0.1 parts

[0076] 0.01 parts of ultramarine blue toner;

[0077] Wherein, the plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 5:1;

[0078] The heat stabilizer is made of the following raw materials in parts by weight: 25 parts of nonanoic acid, 5 parts of lauric acid, 5 parts of barium hydroxide, 6 parts of zinc hydroxide, 10 parts of auxiliary stabilizer, 1.5 parts of antioxidant 1010, 2 parts of metal deactivator, 3 parts of anti-separation agent, and 4 parts of solvent; mixing and stirring the raw materials of the above-mentioned components to obtain the heat stabilizer;

[0079] Wherein, the auxiliary stabilizer is a mixture of phosphi...

Embodiment 2

[0101] A kind of orange peel glass plate sheet, comprises the raw material of following weight portion:

[0102] PVC resin 70 parts

[0103] 35 parts plasticizer

[0104] Impact modifier 8 parts

[0105] Heat stabilizer 1.5 parts

[0106] Flame retardant 2 parts

[0107] Anti-ultraviolet agent 0.12 parts

[0108] Ultramarine blue toner 0.012 parts;

[0109] Wherein, the plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 6:1;

[0110] The heat stabilizer is made of the following raw materials in parts by weight: 30 parts of nonanoic acid, 8 parts of lauric acid, 8 parts of barium hydroxide, 7 parts of zinc hydroxide, 15 parts of auxiliary stabilizer, 1.8 parts of antioxidant 1010, 2.5 parts of metal deactivator, 4 parts of anti-separation agent, and 5 parts of solvent; mixing and stirring the above-mentioned raw materials of each component to obtain the heat stabilizer;

[0111] Wherein, the auxiliary stabilizer is a mixture of ...

Embodiment 3

[0133] A kind of orange peel glass plate sheet, comprises the raw material of following weight portion:

[0134] PVC resin 80 parts

[0135] 40 parts plasticizer

[0136] Impact modifier 10 parts

[0137] 2 parts heat stabilizer

[0138] 3 parts flame retardant

[0139] Anti-ultraviolet agent 0.15 parts

[0140] Ultramarine blue toner 0.015 part;

[0141] Wherein, the plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 7:1;

[0142] The heat stabilizer is made of the following raw materials in parts by weight: 35 parts of nonanoic acid, 10 parts of lauric acid, 10 parts of barium hydroxide, 9 parts of zinc hydroxide, 20 parts of auxiliary stabilizer, 2 parts of antioxidant 1010, 3 parts of metal passivation agent, 5 parts of anti-separation agent, and 6 parts of solvent; mixing and stirring the above-mentioned raw materials of each component to obtain the heat stabilizer;

[0143] Wherein, the auxiliary stabilizer is a mixture o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of plastic sheets, and particularly relates to an orange peel glass sheet and a preparation method thereof. The orange peel glass sheet comprises the following raw materials in parts by weight: 60-100 parts of PVC resin, 30-50 parts of a plasticizer, 1-3 parts of a heat stabilizer, 1-5 parts of a fire retardant, 0.1-0.2 part of an anti-ultraviolet agent and 0.01-0.02 part of ultramarine pigment. The preparation method comprises the following steps of raw materials preparation; agitation at a high speed; primary plasticization; secondary plasticization; hierarchical filtering; calendaring and molding; cooling and rolling; laminating and embossing; and surface treatment. The sheet disclosed by the invention has the advantages of heat resistance, cold resistance, acid resistance, alkaline resistance, ageing resistance, stress resistance, smooth surface, no crack, no bubble, uniform color and luster and strong third dimension, is healthy and environmental friendly, and displays the orange peel effect. The preparation method disclosed by the invention is simple in process, convenient to operate and control, stable in quality and high in production efficiency, and large-scale industrial production can be achieved.

Description

technical field [0001] The invention relates to the technical field of plastic sheets, in particular to an orange peel glass sheet and a preparation method thereof. Background technique [0002] Traditional glass is bulky, difficult to handle, and fragile. Ultra-transparent glass sheets are made of polyvinyl chloride resin and additives. They are lightweight, environmentally friendly, crystal clear, beautiful and practical. Polyvinyl chloride resin is a non-crystalline, polar polymer with high softening temperature and melting temperature. Generally, it can be plasticized at 160~210°C. Due to the polar bonds between macromolecules, PVC Shows hard and brittle properties. Additives can be further divided into heat stabilizers, lubricants, processing modifiers, impact modifiers, fillers, anti-aging agents, anti-cold agents, colorants, etc. according to their functions. Therefore, during processing, it is necessary to carry out experimental processing modification and impact m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/02C08K5/12C08K5/1515C08K5/09C08K3/22C08K5/526B29C43/58
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com