Architectural water-resistant acrylate outer wall paint

A technology of acrylic and exterior wall coatings, which is applied in coatings and other directions, and can solve the problems of not being resistant to brushing, poor durability and anti-wear, long drying time, etc.

Inactive Publication Date: 2014-12-10
SUZHOU YUFAN NEW MATERIAL TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above technical problems, the present application provides a water-resistant acrylic exterior wall coating for buildings, which solves the technical problems of the existing water-resistant acrylic exterior wall coatings for buildings such as poor durability and abrasion resistance, long drying time, and inability to scrub.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of water-resistant acrylic ester exterior wall paint for building, its raw material ratio is as follows in parts by weight: 100 parts of acrylic resin solution; 20 parts of nitrocellulose; 5 parts of butyl acetate; 10 parts of methyl ethyl ketone; 30 parts of olefinic anhydride; 15 parts of n-butanol; 25 parts of ethylene glycol; 10 parts of titanium dioxide; 20 parts of calcium carbonate; 15 parts of pentaerythritol; 20 parts of deionized water; 25 parts of zinc naphthenate; 15 parts of cobalt naphthenate parts; 10 parts of acrylic acid.

[0016] Load nitrocellulose, butyl acetate, methyl ethyl ketone, maleic anhydride, n-butanol and ethylene glycol into a ball mill, mill for 30 min, then add titanium dioxide, calcium carbonate, pentaerythritol, deionized water and ring Zinc alkanoate, after ball milling for 30 minutes, add acrylic resin solution, continue ball milling for 4 hours, and finally, put all the remaining raw materials into the ball mill and mill for ...

Embodiment 2

[0019] A kind of water-resistant acrylic ester exterior wall paint for building, its raw material ratio by weight is as follows: 100 parts of acrylic resin solution; 30 parts of nitrocellulose; 15 parts of butyl acetate; 30 parts of methyl ethyl ketone; 40 parts of olefinic anhydride; 35 parts of butanol; 35 parts of ethylene glycol; 20 parts of titanium dioxide; 30 parts of calcium carbonate; 25 parts of pentaerythritol; 40 parts of deionized water; 35 parts of zinc naphthenate; 35 parts of cobalt naphthenate parts; 30 parts of acrylic acid.

[0020] Load nitrocellulose, butyl acetate, methyl ethyl ketone, maleic anhydride, n-butanol and ethylene glycol into a ball mill, mill for 30 min, then add titanium dioxide, calcium carbonate, pentaerythritol, deionized water and ring Zinc alkanoate, after ball milling for 30 minutes, add acrylic resin solution, continue ball milling for 5 hours, and finally, put all the remaining raw materials into a ball mill and ball mill for 30 minu...

Embodiment 3

[0023] A kind of water-resistant acrylic ester exterior wall paint for building, its raw material ratio by weight is as follows: 100 parts of acrylic resin solution; 25 parts of nitrocellulose; 10 parts of butyl acetate; 20 parts of methyl ethyl ketone; 35 parts of olefinic anhydride; 25 parts of butanol; 30 parts of ethylene glycol; 15 parts of titanium dioxide; 25 parts of calcium carbonate; 20 parts of pentaerythritol; 30 parts of deionized water; 30 parts of zinc naphthenate; 25 parts of cobalt naphthenate parts; 20 parts of acrylic acid.

[0024] Load nitrocellulose, butyl acetate, methyl ethyl ketone, maleic anhydride, n-butanol and ethylene glycol into a ball mill, mill for 30 min, then add titanium dioxide, calcium carbonate, pentaerythritol, deionized water and ring Zinc alkanoate, after ball milling for 30 minutes, add acrylic resin solution, continue ball milling for 4.5 hours, and finally, put all the remaining raw materials into the ball mill and ball mill for 30 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an architectural water-resistant acrylate outer wall paint which is prepared from the following raw materials in parts by weight: 100 parts of acrylic resin solution, 20-30 parts of nitrocellulose, 5-15 parts of butyl acetate, 10-30 parts of methyl ethyl ketone, 30-40 parts of maleic anhydride, 15-35 parts of n-butanol, 25-35 parts of ethylene glycol, 10-20 parts of tinting pigment, 20-30 parts of calcium carbonate, 15-25 parts of pentaerythritol, 20-40 parts of deionized water, 25-35 parts of mold preventive, 15-35 parts of cobalt naphthenate and 10-30 parts of acrylic acid. The product does not have any hard lump, and is in a uniform state while being stirred. The solid content is 50-60%, the surface drying time is 1-2 hours, and the solid drying time is 18-20 hours. The paint does not have the phenomenon of blistering or shedding after being immersed in water for 2-3 weeks, and does not have any abnormity after being immersed in alkaline water for 5-7 days. The scrubbing resistance of the coated film is 1500-2000 times; and the paint can be widely produced and continuously used instead of the existing materials.

Description

technical field [0001] The application belongs to the field of coatings, in particular to a water-resistant acrylic exterior wall coating for buildings. Background technique [0002] Paint, traditionally called paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, oil, or emulsion, with or without adding pigments, fillers, adding Corresponding additives, viscous liquid prepared with organic solvent or maleic anhydride. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called a coating film, also known as a paint film or a coating." The ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 戴晓宸
Owner SUZHOU YUFAN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products