Electrical heated tube processing technology good in plating quality and corrosion property

A treatment process, electric heating tube technology, applied in metal material coating process, manufacturing tools, metal processing equipment, etc., can solve the problems of welding scale on the metal surface, unusable, easy to rust on the surface of electrothermal light, etc., and achieve bright surface , Extended service life, and improved oxidation resistance

Inactive Publication Date: 2015-01-07
JIANGSU SHUNFA ELECTRIC HEATING MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The electric heating tube is a workpiece that has been working in a high-temperature and high-humidity environment for a long time. There is welding scale on the metal surface during manufacture. If the surface is not cleaned, it can be directly rolled and plated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1）

[0015] The specific steps of the electrothermal tube rolling treatment process of the present embodiment are as follows:

[0016] A. Treatment before rolling:

[0017] Put 50 pieces of electric heating tubes made by welding and forming process into 65°C white steel aqueous solution for 12 minutes, then soak them in concentrated nitric acid solution for 5 seconds, then rinse with clean water, and clean the surface. After treatment, the surface of the electric heating tube is white in appearance, and the welding scale can be brushed off with a toothbrush.

[0018] The white steel aqueous solution is made of 12% white steel and clean water in a mass ratio of 14:100. The composition of molten steel is 30wt% phosphoric acid, 10wt% nitric acid, 15wt% hydrochloric acid, and the rest is water. Concentrated nitric acid solution is prepared from 70% nitric acid and water in a mass ratio of 70:30.

[0019] B. Tumbler Treatment and Cleaning:

[0020] Put 400 pieces of electric heati...

Embodiment 2）

[0025] The specific steps of the electrothermal tube rolling treatment process of the present embodiment are as follows:

[0026] A. Treatment before rolling:

[0027] Put 50 pieces of electric heating tubes made by welding forming process into 50°C white steel aqueous solution for 6 minutes, then soak them in concentrated nitric acid solution for 5 seconds, then rinse with clean water, and clean the surface.

[0028] The white steel aqueous solution is made of white steel with a concentration of 12% and clean water in a mass ratio of 12:100. Concentrated nitric acid solution is prepared from 70% nitric acid and water at a mass ratio of 65:35.

[0029] B. Tumbler Treatment and Cleaning:

[0030] Put 400 pieces of electric heating tubes that have been treated before rolling into the rolling machine, add steel balls and clean water to completely cover the electric heating tubes. Add 160g of polishing agent and 80g of citric acid powder before tumbling, and tumbling for 12 m...

Embodiment 3）

[0035] The specific steps of the electrothermal tube rolling treatment process of the present embodiment are as follows:

[0036] A. Treatment before rolling:

[0037] Put 50 pieces of electric heating tubes made by welding forming process into 80°C white steel aqueous solution for 8 minutes, then soak them in concentrated nitric acid solution for 5 seconds, then rinse with clean water, and clean the surface.

[0038] The white steel aqueous solution is made of 12% white steel and clean water in a mass ratio of 16:100. Concentrated nitric acid solution is prepared from 70% nitric acid and water in a mass ratio of 75:25.

[0039] B. Tumbler Treatment and Cleaning:

[0040] Put 400 pieces of electric heating tubes that have been treated before rolling into the rolling machine, add steel balls and clean water to completely cover the electric heating tubes. Add 200g of polishing agent and 120g of citric acid powder before tumbling, and tumbling for 18 minutes. When tumbling i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an electrical heated tube barreling processing technology which comprises the following steps that A. an electrical heated tube is placed into a stainless steel water solution of 65 DEG C for soaking for 12 min first and then is placed into a concentrated nitric acid solution for soaking for 5 s, then washing is carried out, and the surface is cleared; B. the electrical heated tube subjected to before-barreling processing is subjected to barreling processing, then the electrical heated tube obtained after barreling is placed into a diluted citric acid solution with the concentration of 5% and the temperature of 80 DEG C for soaking for 5 min, and then washing is carried out; and C. the electrical heated tube is subjected to passivating treatment and spin drying; during passivating, the electrical heated tube is placed into a diluted nitric acid solution for soaking for 10 s and then is placed into a corrosion inhibition solution for soaking for 10 s, and then filtering and washing are carried out; and the corrosion inhibition solution is prepared by potassium iodide, benzotriazole and water according to the weight ratio of 0.1 : 60 : 100. According to the technology, welding scales, spots, splotches and rust on the surface of the electrical heated tube can be effectively removed, and the plating quality of the electrical heated tube is improved.

Description

[0001] This application is a divisional application, the application number of the original application: 201210481561.9, the application date: 2012-11-23, the name of the invention: electric heating tube rolling burnishing treatment process. technical field [0002] The invention relates to a method for chemically treating metal surfaces. Background technique [0003] Metal materials need to be tumbled before being plated. Rolling treatment is a process in which batches of parts and grinding media are rotated in a drum at a low speed, and the relative movement of parts and abrasives is used for finishing treatment. Wet machining grinding media commonly used in the tumbling process contain abrasives, chemical accelerators (brighteners) and water. Good rolling treatment can effectively guarantee the quality of plating and prevent metal materials from being corroded. The electric heating tube is a workpiece that has been working in a high-temperature and high-humidity environ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More