Composition of compound calcium sulfonate-based lubricating grease for improving high-temperature performance and preparation method thereof
A composite calcium sulfonate-based lubricating grease with high-temperature performance technology, applied in the field of lubricating grease, can solve problems such as short life, achieve the effects of prolonging retention, saving primary energy, and ensuring reliability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1:
[0031] 1) Component: overbased calcium sulfonate detergent (base value 320mgKOH / g): 200g (20.0%)
[0032]
[0033] 2) Production process: Put 200g (20.0%) of an overbased calcium sulfonate detergent with a base value of 320mgKOH / g into a small autoclave, add 10g (1%) of methanol to make calcium carbonate with a calcite structure, and stir quickly. Heat to 90~100℃, keep the temperature until the system materials gradually thicken, and gradually add 10g (1%) lithium hydroxide powder, 50g (5%) salicylic acid and twelve carbon to the system at 95~100℃. Dibasic acid 50g (5%), after a constant temperature reaction for 60 minutes, gradually increase the temperature, keep at 130~135℃ for 60 minutes, gradually increase the temperature to 220-222℃ for 5-10 minutes, adjust the consistency with polyolefin No. 8. The addition amount is 680g (68%), and the final grease obtained is 990g (methanol is volatilized during production, not in the components), and the working penetr...
Example Embodiment
[0034] Example 2:
[0035] 1) Component: overbased calcium sulfonate detergent (base value 320mgKOH / g): 350g (35%)
[0036]
[0037] 2) Production process: Put 350g (35.0%) of an overbased calcium sulfonate detergent with a base value of 320mgKOH / g into a small autoclave, add 30g (3%) of methanol to make calcium carbonate with calcite structure, and stir quickly. Heat to 90~100℃, keep the temperature until the system materials gradually thicken, and gradually add 20g (2%) lithium hydroxide powder, 80g (8%) salicylic acid and twelve carbon to the system at 95~100℃. Dibasic acid 100g (10%), after a constant temperature reaction for 60 minutes, gradually increase the temperature, keep the temperature at 130~135℃ for 60 minutes, gradually and slowly increase the temperature to 220-222℃ constant temperature for 5-10 minutes, adjust the consistency with polyolefin No. 8. The added amount is 420g (42%), and the final grease obtained is 970g (methanol is volatilized during production, not...
Example Embodiment
[0038] Example 3:
[0039] 1) Component: overbased calcium sulfonate detergent (base value 320mgKOH / g): 350g (35%)
[0040]
[0041] 2) Production process: Put 350g (35.0%) of an overbased calcium sulfonate detergent with a base value of 320mgKOH / g into a small autoclave, add 30g (3%) of methanol to make calcium carbonate with calcite structure, and stir quickly. Heat to 90~100℃, keep the temperature until the system materials gradually thicken, and gradually add 13g (1.3%) of lithium hydroxide powder, 80g (8%) of salicylic acid and hexadecane to the system at a temperature of 95~100℃. Dibasic acid 100g (10%), after a constant temperature reaction for 60 minutes, gradually increase the temperature, keep the temperature at 130~135℃ for 60 minutes, gradually and slowly increase the temperature to 220-222℃ constant temperature for 5-10 minutes, adjust the consistency with polyolefin No. 8. The added amount is 427g (42.7%), and the final grease obtained is 970g (methanol is volatilize...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap