High-durability concrete

A technology of durable concrete and mixed fibers, applied in the field of concrete, can solve the problems of complex service environment of concrete structures, inability of concrete durability to meet social requirements, low dosage and overall technical level, etc., and achieves good frost resistance and service life. Long, high-strength effects

Inactive Publication Date: 2015-03-04
WUWEI HENGJI COMML CONCRETE
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As far as concrete materials are concerned, although the total energy consumption per unit of production is very low, the huge amount used and the overall low level of technology put a lot of pressure on resources, energy and the environment as a whole
The service environment of concrete structures is often very complicated. The durability of the current concrete cannot meet the requirements of the society, and further research and development are needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The high durability concrete of the present invention, its raw material comprises the following components by weight: 100 parts of cement, 350 parts of river sand, 350 parts of crushed stone, 120 parts of water, 15 parts of fly ash, 80 parts of nano beads, natural 5 parts of zeolite superfine powder, 18 parts of alumina, 2 parts of sodium sulfate, 6 parts of diethanolamine, 1 part of sodium hydroxide, 1.6 parts of methyltrichlorosilane, 2 parts of ethanol, 6 parts of air-entraining agent, lignosulfonic acid 1 part of salt water reducer, 4 parts of polyvinyl alcohol, 5 parts of mixed fiber, 1.2 parts of sodium nitrite, 0.5 part of polyvinylpyrrolidone; the mixed fiber is carbon fiber, steel fiber, polypropylene fiber, polyvinyl alcohol fiber The combination of parts by weight is 1:5:7:3.

Embodiment 2

[0017] The high durability concrete of the present invention, its raw material comprises the following components by weight: 200 parts of cement, 150 parts of river sand, 700 parts of gravel, 50 parts of water, 35 parts of fly ash, 30 parts of nano beads, natural 35 parts of zeolite superfine powder, 10 parts of alumina, 5 parts of sodium sulfate, 3 parts of diethanolamine, 2.5 parts of sodium hydroxide, 1 part of methyltrichlorosilane, 5 parts of ethanol, 3 parts of air-entraining agent, lignosulfonic acid 2.8 parts of salt water reducer, 2 parts of polyvinyl alcohol, 20 parts of mixed fiber, 0.3 part of sodium nitrite, 1.6 parts of polyvinylpyrrolidone, 0.5 part of curing agent; the mixed fiber is carbon fiber, steel fiber, polypropylene fiber , The combination of polyvinyl alcohol fibers in a ratio of 1:2:3:6 by weight;

[0018] Wherein, the air-entraining agent is uniformly stirred by 30 parts by weight of sodium dodecylbenzene sulfonate, 30 parts by weight of stearic acid...

Embodiment 3

[0020] The high durability concrete of the present invention, its raw material comprises the following components by weight: 120 parts of cement, 263 parts of river sand, 400 parts of gravel, 95 parts of water, 19.3 parts of fly ash, 43 parts of nano beads, natural 11.6 parts of zeolite superfine powder, 15 parts of alumina, 3.9 parts of sodium sulfate, 5.46 parts of diethanolamine, 2.3 parts of sodium hydroxide, 1.4 parts of methyltrichlorosilane, 2.68 parts of ethanol, 4.9 parts of air-entraining agent, lignosulfonic acid 2.1 parts of salt water reducer, 3.2 parts of polyvinyl alcohol, 13.5 parts of mixed fiber, 0.94 part of sodium nitrite, 1.4 parts of polyvinylpyrrolidone, 1.2 parts of curing agent; the mixed fiber is carbon fiber, steel fiber, polypropylene fiber , The combination of polyvinyl alcohol fibers in a ratio of 1:4:6:5 by weight;

[0021] Wherein, the air-entraining agent is uniformly stirred by 55 parts by weight of sodium dodecylbenzene sulfonate, 20 parts by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-durability concrete which comprises the following raw materials: cement, river sand, macadam, water, fly ash, nano microbead, natural zeolite micropowder, aluminum oxide, sodium sulfate, diethanolamine, sodium hydroxide, methyl trichlorosilane, ethanol, an air entraining agent, a lignosulfonate water reducing agent, polyvinyl alcohol, mixed fiber, sodium nitrate and polyvinylpyrrolidone. The mixed fiber is the combination of carbon fiber, steel fiber, polypropylene fiber and polyvinyl alcohol fiber in a weight ratio of 1:(2-5):(3-7):(3-6). The high-durability concrete has the advantages of high strength, favorable water impermeability, favorable freezing resistance and favorable durability, and has long service life when being applied to hydrotechnics, harbors, roads and other projects.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a high-durability concrete. Background technique [0002] Concrete has also become the material of choice for roads, dams, and bridges, as industrial development and urbanization accelerate. With the proposal of high-performance concrete, the durability of concrete has attracted more and more attention from all aspects. The durability of concrete refers to the resistance of the concrete structure to climate, chemical corrosion, physical action or any other damage process. Its safety, usability and appearance. As far as concrete materials are concerned, although the total energy consumption per unit of production is very low, the huge consumption and the overall low technical level put a lot of pressure on resources, energy and the environment as a whole. The service environment of concrete structures is often very complicated. The durability of the current concrete cannot mee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B22/06C04B22/14C04B24/42C04B24/18
Inventor 倪友
Owner WUWEI HENGJI COMML CONCRETE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap