Resin composition and application thereof

A resin composition and epoxy resin technology, applied in the field of copper clad laminates, can solve the problems of poor dimensional stability and heat resistance, improve heat resistance and dimensional stability, improve thermal expansion coefficient, and improve dimensional stability. Effects of sex and heat resistance

Active Publication Date: 2015-03-25
SHAANXI SHENGYI TECH
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a resin composition, which solves the problems of poor d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition and application thereof
  • Resin composition and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]Step 1: Weigh the following components according to parts by weight: 10 parts of epoxy soybean oil modified epoxy resin, 90 parts of DOPO-HQ modified phosphorus-containing epoxy resin, 15 parts of biphenyl type phenolic resin, nonyl 20 parts of phenol-modified benzoxazine, 70 parts of silicon dioxide, 50 parts of boehmite, 0.08 parts of diphenylimidazole, 60 parts of acetone, and 50 parts of ethylene glycol methyl ether; among them, silicon dioxide is spherical Silicon, mixed with 60 parts of silicon dioxide with an average particle size of 5 μm and 10 parts of silicon dioxide with an average particle size of 80 nm; boehmite is granular, with an average particle size of 2 μm;

[0037] Use KH560-ethanol solution with a volume concentration of 30%, the amount of KH560 is 2% of the mass of silica and boehmite, use dry spray to treat the surface of silica and boehmite in a kneader for 2 hours, then take it out for use ;

[0038] Step 2: using ethylene glycol methyl ether an...

Embodiment 2

[0042] Step 1: Take the following components in parts by weight: 30 parts of epoxy soybean oil modified epoxy resin, 70 parts of DOPO-HQ modified phosphorus-containing epoxy resin, 20 parts of biphenyl type phenolic resin, nonyl 5 parts of phenol-modified benzoxazine, 103 parts of silicon dioxide, 20 parts of boehmite, 0.15 parts of diphenylimidazole, 60 parts of acetone, and 50 parts of ethylene glycol methyl ether; among them, silicon dioxide is spherical Silicon, mixed with 100 parts of silicon dioxide with an average particle size of 5 μm and 3 parts of silicon dioxide with an average particle size of 80 nm; boehmite is granular, with an average particle size of 2 μm;

[0043] Use KH560-ethanol solution with a volume concentration of 30%, the amount of KH560 is 2% of the mass of silica and boehmite, use dry spray to treat the surface of silica and boehmite in a kneader for 2 hours, then take it out for use ;

[0044] Step 2: using ethylene glycol methyl ether and acetone ...

Embodiment 3

[0048] Step 1: Take the following components in parts by weight: 22 parts of epoxy soybean oil modified epoxy resin, 78 parts of DOPO-HQ modified phosphorus-containing epoxy resin, 18 parts of biphenyl phenolic resin, nonyl 15 parts of phenol-modified benzoxazine, 95 parts of silicon dioxide, 40 parts of boehmite, 0.1 part of diphenylimidazole, 60 parts of acetone, and 50 parts of ethylene glycol methyl ether; among them, silicon dioxide is spherical Silicon, mixed with 88 parts of silicon dioxide with an average particle size of 5 μm and 7 parts of silicon dioxide with an average particle size of 80 nm; boehmite is granular, with an average particle size of 2 μm;

[0049] Use KH560-ethanol solution with a volume concentration of 30%, the amount of KH560 is 2% of the mass of silica and boehmite, use dry spray to treat the surface of silica and boehmite in a kneader for 2 hours, then take it out for use ;

[0050] Step 2: using ethylene glycol methyl ether and acetone to disso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a resin composition. The resin composition is prepared from the following components in parts by weight: 10-30 parts of epoxy soybean oil modified epoxy resin, 70-90 parts of phosphorus modified phenolic epoxy resin, 15-20 parts of biphenyl type phenolic resin, 5-20 parts of nonyl phenol modified benzoxazine, 70-103 parts of silicon dioxide, 20-50 parts of boehmite, 0.08-0.85 part of diphenyl imidazole, 30-80 parts of acetone and 30-80 parts of ethylene glycol monomethyl ether. The resin composition is used for preparing a copper-clad plate. According to the resin composition, the problems that a copper-clad plate is poor in dimensional stability and heat resistance after being solidified by an existing adhesive resin system are solved; the heat resistance and dimensional stability of CEM-3 are improved; and the coefficient of thermal expansion of the plate is also improved, so that the production technology of the CEM-3 reaches the advanced level at home.

Description

technical field [0001] The invention belongs to the technical field of copper-clad laminates, in particular to a resin composition, and also relates to a copper-clad laminate made of the resin composition. Background technique [0002] With the rapid development of electronic integration technology and assembly technology, printed circuit board (Printed circuit board, PCB) manufacturers also have higher requirements for the dimensional stability and thermal expansion coefficient (Coefficient of Thermal Expansion, CTE) of CCL. Copper Clad Laminate (CCL) prepared by epoxy resin-based composite materials with phenolic resin as curing agent has good heat resistance, medium resistance, CAF (ion migration) resistance, etc., but there are some problems after curing. There are problems such as poor dimensional stability and high brittleness of the plate. However, although the epoxy resin-based composite material cured with dicyandiamide has good dimensional stability, it has poor h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/04C08L63/00C08G59/62C08G59/40C08K9/06C08K3/36C08K3/22B32B15/092B32B27/04
Inventor 吴雅惠武伟
Owner SHAANXI SHENGYI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap