Artificial quartzite plate and manufacturing method thereof

A technology of artificial quartz stone and quartz stone, which is applied in the field of artificial quartz stone plate and its manufacturing, can solve the problems of no antibacterial effect, single color and pattern, uneven density, etc., achieve wide use, long-lasting antibacterial effect, and manufacturing The effect of simple method

Inactive Publication Date: 2015-04-08
田忠和
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the artificial quartz stone produced by the prior art has defects such as uneven density, low hardness, easy powder formation, easy deformation, easy aging, easy coloring, single color and pattern, and no antibacterial effect, which limits its further development. The range of applications needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 30kg of 3-80 mesh quartz stone, 70kg of 325-mesh quartz powder, 5kg of cullet, 10kg of 30-50 mesh tourmaline, 3kg of 50-100 mesh sillimanite powder, 12kg of 100-200 mesh zirconium silicate powder, antioxidant 1222: 0.1kg, epoxy resin 10kg, silane coupling agent γ-methacryloxypropyltrimethoxysilane (KH570) 0.3kg, peroxy-2-ethylhexanoic acid tert-butyl ester 2kg, pigment 0.1 kg, the pigment is composed of titanium dioxide and blue water according to the mass ratio of 15:1; the above-mentioned components are uniformly mixed, and the mixed material is evenly spread on the plate-making mold, and then the plate-making mold is sent into the vacuum chamber , When the air pressure reaches -0.1MPa during vacuuming, vibrate for 2-3 minutes under a pressure of 2.5-3.5MPa to form, and then send it to a curing furnace for curing. The curing temperature is 85-95°C, and the time is 30-45 minutes. The cured plate is out of the oven. After demoulding, stacking and cooling, send it ...

Embodiment 2

[0023] Weigh 90kg of quartz stone of 3-80 mesh, 30kg of quartz powder of 325 mesh, 15kg of cullet, 3kg of tourmaline of 30-50 mesh, 12kg of sillimanite powder of 50-100 mesh, 3kg of zirconium silicate powder of 100-200 mesh, antioxidant 1098: 2kg, phenolic resin 5kg, silane coupling agent γ-aminopropyltriethoxysilane (KH550) 2kg, tert-butyl peroxybenzoate 0.3kg, pigment 1kg, described pigment is made of titanium dioxide, iron yellow powder, Iron red powder, iron black powder and blue water are composed according to the mass ratio of 312:6:25:1:28; the above-mentioned components are evenly mixed, and the mixed materials are evenly spread on the plate-making mold, and then the plate-making mold Send it into a vacuum chamber, when the air pressure reaches -0.1MPa during vacuuming, vibrate for 2-3 minutes under a pressure of 2.5-3.5MPa to form, and then send it to a curing oven for curing. The curing temperature is 85-95°C, and the curing time is 30-45 minutes. The finished boards...

Embodiment 3

[0025] Weigh 70kg of quartz stone of 3-80 mesh, 40kg of quartz powder of 325 mesh, 10kg of cullet, 5kg of tourmaline of 30-50 mesh, 5kg of sillimanite powder of 50-100 mesh, 5kg of zirconium silicate powder of 100-200 mesh, antioxidant 245: 1kg, polyurethane resin 8kg, silane coupling agent γ-glycidyl etheroxypropyl trimethoxysilane 1kg, benzoyl peroxide 0.5kg, pigment 0.5kg, the pigment is composed of titanium dioxide, iron yellow powder, iron black Powder, chrome green powder and blue water are composed according to the mass ratio of 980:1:2:3:118; the above-mentioned components are evenly mixed, and the mixed materials are evenly spread on the plate-making mold, and then the plate-making mold is sent to Put it into the vacuum chamber, when the air pressure reaches -0.1MPa during vacuuming, vibrate under the pressure of 2.5~3.5MPa for 2~3 minutes to form, and then send it to the curing furnace for curing. The curing temperature is 85~95℃, and the time is 30~45 minutes. After ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an artificial quartzite plate and a manufacturing method thereof. The artificial quartzite plate is composed of the following components in parts by weight: 30-90 parts of 3-80-mesh quartzite, 30-70 parts of 325-mesh quartz powder, 5-15 parts of cullet, 3-10 parts of 30-50-mesh tourmaline, 3-12 parts of 50-100-mesh sillimanite powder, 3-12 parts of 100-200-mesh zirconium silicate powder, 0.1-2 parts of antioxidant, 5-10 parts of unsaturated resin, 0.3-2 parts of silane coupling agent, 0.3-2 parts of curing agent and 0.1-1 part of pigment. The antioxidant is added to the raw materials, thereby enhancing the oxidation resistance and ultraviolet resistance of the artificial quartzite plate. The tourmaline is added to the raw materials to effectively enhance the antibacterial property of the artificial quartzite plate, and thus, the artificial quartzite plate has long antimicrobial effect. The sillimanite powder and zirconium silicate powder, which are favorable refractory materials with very high melting point and hardness, can enhance the refractory temperature of the artificial quartzite plate, prolong the refractory time and increase the compression strength.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, in particular to an artificial quartz stone plate and a manufacturing method thereof. Background technique [0002] As a substitute for natural stone, artificial quartz stone has incomparable advantages such as high strength, high hardness, high temperature resistance, corrosion resistance, anti-aging, easy cleaning, wear resistance, pure material, and no radiation. It is widely used in industrial production and people's daily life as a decorative material for floor tiles and walls. [0003] However, the artificial quartz stone produced by the prior art has defects such as uneven density, low hardness, easy powder formation, easy deformation, easy aging, easy coloring, single color and pattern, and no antibacterial effect, which limits its further development. The scope of application needs to be solved urgently. Contents of the invention [0004] The technical problem t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/10C04B26/12C04B26/16C04B26/04C04B22/08C04B14/06
Inventor 田忠和
Owner 田忠和
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com