Solar battery backboard material with high weather resistance and preparation method thereof
A solar cell and weather resistance technology, applied in circuits, photovoltaic power generation, electrical components, etc., can solve the problems of inability to meet the needs of use, serious environmental pollution, and high manufacturing costs, and achieve excellent weather resistance, simple preparation process, and excellent environmental protection. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0014] Example 1: A high weather resistance solar cell backsheet material, comprising the following components in parts by weight: 48 parts of PET, 27 parts of PETG, 1.5 parts of glass powder, 13 parts of nanomaterials, 1.2 parts of ultraviolet absorbers, light stability GW-540 2.8 parts, anti-aging agent 1.5 parts, antioxidant 0.8 parts, stabilizer 3.5 parts. The ultraviolet absorber is a compound with a mass ratio of UV-317 and UV-326 of 1:1, and the antioxidant is a compound of antioxidant CA and antioxidant 264 with a mass ratio of 1:1. The stabilizer is polycarbodiimide, the nano material is nano titanium dioxide, and the anti-aging agent is a hindered amine anti-aging agent.
[0015] The above-mentioned preparation method of high weather resistance solar cell backsheet material includes the following steps: weigh the required raw materials according to the weight ratio and place them in a mixer, stir at 5500r / min for 8min, and the raw materials after stirring Dry at 75°C t...
Example Embodiment
[0016] Example 2: A high weather resistance solar cell back sheet material, including the following components in parts by weight: 45 parts of PET, 25 parts of PETG, 1 part of glass powder, 10 parts of nanomaterials, 0.8 parts of ultraviolet absorber, light stable 2.5 parts of GW-540, 1 part of antioxidant, 0.6 part of antioxidant, 3 parts of stabilizer. The ultraviolet absorber is UV-317, the antioxidant is a compound of antioxidant CA and antioxidant 264 with a mass ratio of 1:1, the stabilizer is carbonized iminophenyl ester, and the The nano material is nano calcium carbonate, and the anti-aging agent is benzophenone anti-aging agent.
[0017] The above-mentioned preparation method of high weather resistance solar cell backsheet material includes the following steps: weigh the required raw materials according to the weight ratio and place them in a mixer, stir at 5000r / min for 10min, and the raw materials after stirring Dry at 70°C to obtain premixed materials, and fill in i...
Example Embodiment
[0018] Example 3: A high weather resistance solar cell back sheet material, including the following components in parts by weight: 50 parts PET, 30 parts PETG, 2 parts glass powder, 15 parts nanomaterials, 1.5 parts UV absorber, and light stability 3 parts of GW-540, 2 parts of anti-aging agent, 1 part of antioxidant, 4 parts of stabilizer. The ultraviolet absorber is UV-326, the antioxidant is a compound of antioxidant CA and antioxidant 264 in a mass ratio of 1:1, and the stabilizer is polycarbodiimide. The nano material is a mixture of nano titanium dioxide, nano alumina, and nano calcium carbonate, and the anti-aging agent is a hindered amine anti-aging agent.
[0019] The above-mentioned preparation method of high weather resistance solar cell back sheet material includes the following steps: weigh the required raw materials according to the weight ratio and place them in a mixer, stir at 6000r / min for 5 minutes, and the raw materials after stirring Dry at 80°C to obtain pr...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap