A kind of highly dispersed supported palladium/tungsten carbide catalyst and preparation method thereof

A tungsten carbide catalyst, supported palladium technology, applied in physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve the necessity and urgency of research and development of non-Pt catalysts due to increased cost, and the difficulty of evenly dispersing precious metals. , low utilization rate of catalysts, etc., to achieve the effects of rich Pd resources, simple and easy preparation process and low cost

Inactive Publication Date: 2017-04-12
DALIAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Traditional tungsten carbide-supported Pt-based catalysts, due to the large tungsten carbide particles and low specific surface area, the noble metal is not easy to disperse evenly, making the utilization rate of the catalyst low
The cost of Pt has further exacerbated the necessity and urgency of non-Pt catalyst research and development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of highly dispersed supported palladium/tungsten carbide catalyst and preparation method thereof
  • A kind of highly dispersed supported palladium/tungsten carbide catalyst and preparation method thereof
  • A kind of highly dispersed supported palladium/tungsten carbide catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1: 20% Pd / WC 10 (20% means that the mass content of the active component Pd is 20%, and 10 means 10nm SiO 2 template)

[0034] Weigh 2g of ammonium metatungstate, dissolve 2.62g of glucose in deionized water at 80°C, adjust the pH to 11 with NaOH, add 10nm SiO 2 Sol 5.3g (mass fraction 30%), stirred at 80°C for 3h; dried at 120°C for 5h to obtain a precursor solid. The above precursor solids were placed in a tube furnace, N 2 At 5°C min under atmosphere -1 The temperature was programmed to 550°C at a rate of 2°C min -1 The rate was programmed to raise the temperature to 900°C, react at a constant temperature for 3 hours, and cool naturally to obtain a precursor composite material. Put the above precursor composite material in 2M NaOH solution, stir at 40°C for 12h, filter, wash, vacuum dry at 80°C for 6h, and weigh to obtain highly dispersed tungsten carbide material WC 10 . Dissolve 0.5588g of sodium citrate in 50mL of deionized water, add chloropalladiu...

Embodiment 2

[0035] Example 2: 20% Pd / WC 20 (20% means that the mass content of the active component Pd is 20%, and 20 means 20nm SiO 2 template)

[0036] Weigh 2g of ammonium metatungstate, dissolve 2.62g of glucose in deionized water at 80°C, adjust the pH to 11 with NaOH, add 20nm SiO 2 Sol 4g (mass fraction 40%), stirred at 80°C for 3h; dried at 120°C for 5h to obtain a precursor solid. The above precursor solids were placed in a tube furnace, N 2 At 5°C min under atmosphere -1 The temperature was programmed to 550°C at a rate of 2°C min-1 The rate was programmed to raise the temperature to 900°C, react at a constant temperature for 3 hours, and cool naturally to obtain a precursor composite material. Put the above precursor composite material in 2M NaOH solution, stir at 40°C for 12h, filter, wash, vacuum dry at 80°C for 6h, and weigh to obtain highly dispersed tungsten carbide material WC 20 . Dissolve 0.5588g of sodium citrate in 50mL of deionized water, add chloropalladium ac...

Embodiment 3

[0037] Example 3: 20% Pd / WC 50 (20% means that the mass content of the active component Pd is 20%, and 50 means 50nm SiO 2 template)

[0038] Weigh 2g of ammonium metatungstate, dissolve 2.62g of glucose in deionized water at 80°C, adjust the pH to 11 with NaOH, add 50nm SiO 2 Sol 4g (mass fraction 40%), stirred at 80°C for 3h; dried at 120°C for 5h to obtain a precursor solid. The above precursor solids were placed in a tube furnace, N 2 At 5°C min under atmosphere -1 The temperature was programmed to 550°C at a rate of 2°C min -1 The rate was programmed to raise the temperature to 900°C, react at a constant temperature for 3 hours, and cool naturally to obtain a precursor composite material. Put the above precursor composite material in 2M NaOH solution, stir at 40°C for 12h, filter, wash, vacuum dry at 80°C for 6h, and weigh to obtain highly dispersed tungsten carbide material WC 50 . Dissolve 0.5588g of sodium citrate in 50mL of deionized water, add chloropalladium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-dispersion supported palladium / tungsten carbide catalyst and a preparation method thereof. The preparation method comprises precursor solution preparation, high temperature calcining, template etching, and dipping reduction loading with palladium. The prepared high-dispersion supported palladium / tungsten carbide can be used as an electrocatalyst and is a direct formic acid fuel cell anode electrocatalyst. The high-dispersion supported palladium / tungsten carbide catalyst has good stability, a narrow particle size dispersion range and a high catalyst utilization rate, prolongs a catalyst service life and reduces a fuel cell production cost. The preparation method solves the problem that the traditional preparation method has poor tungsten carbide dispersion effects and easily causes agglomeration so that specific surface area is reduced and a catalyst utilization rate is reduced.

Description

technical field [0001] The invention belongs to the field of energy materials and electrocatalysis, and relates to a highly dispersed and loaded palladium / tungsten carbide catalyst. The invention also relates to a preparation method of the highly dispersed supported palladium / tungsten carbide catalyst. Background technique [0002] In 1973, Levy and Boundart of Germany reported that tungsten carbide has Pt-like properties (Science.1973; 181:547-549), and tungsten carbide, as a potential catalytic material for replacing Pt group noble metals, has good electrical conductivity (10 5 S cm -1 at 20°C), and has catalytic activity for the electrooxidation reactions of hydrogen, alcohols, formic acid, etc., and its preparation and application research have attracted widespread attention. [0003] Tungsten carbide particles prepared by traditional preparation methods are easy to agglomerate, and the specific surface area (1-35m 2 g -1 ) is low, which is not conducive to the impro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/22H01M4/92
CPCY02E60/50
Inventor 李光兰谢洋洋陈思妹
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com