Sealing ring

A sealing ring and nitrile rubber technology, which is applied in the field of sealing rings, can solve the problems that the self-lubricating performance, heat resistance, and aging resistance of the sealing ring cannot meet the use requirements, short service life, and prone to twisting and cracking. And the effect of reasonable formula, long service life and low cost

Inactive Publication Date: 2015-09-16
梁胜光
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional sealing ring is made of ordinary NBR as the main material, and its formula design often takes tear resistance, wear resistance and extrusion resistance as key considerations, and its use medium is not fully considered in the formula design process. The self-lubricating performance, heat resistance, aging resistance and other aspects of the sealing ring in the same working condition are far from meeting the requirements of use, so it is easy to twist and crack due to the increase of torque during assembly, and the service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of sealing ring described in the present embodiment 1 is made up of the raw material formula component of following mass percent: Comprise 120 parts of nitrile rubber, 90 parts of EPDM rubber, 60 parts of chloroprene rubber, 90 parts of butyl rubber, 25 parts of activated carbon, 10 parts of carbon fiber, 10 parts of graphite, 8 parts of dioctyl terephthalate, 6 parts of ethylene-vinyl acetate copolymer, 8 parts of dibutyl ester, 8 parts of chlorinated paraffin, 5 parts of dioctyl sebacate Ester, 12 parts of titanium dioxide, 12 parts of zinc chloride.

Embodiment 2

[0011] A kind of sealing ring described in the present embodiment 2 is made up of the raw material formula component of following mass percent: Comprise 130 parts of acrylonitrile-butadiene rubber, 100 parts of EPDM rubber, 80 parts of chloroprene rubber, 100 parts of butyl rubber, 30 parts of activated carbon, 12 parts of carbon fiber, 12 parts of graphite, 10 parts of dioctyl terephthalate, 8 parts of ethylene-vinyl acetate copolymer, 10 parts of dibutyl ester, 10 parts of chlorinated paraffin, 8 parts of dioctyl sebacate Ester, 15 parts of titanium dioxide, 15 parts of zinc chloride.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sealing ring. The sealing ring comprises the following raw material formula components in parts by weight: 120-130 parts of nitrile rubber, 90-100 parts of ethylene-propylene-diene monomer rubber, 60-80 parts of chloroprene rubber, 90-100 parts of butyl rubber, 25-30 parts of activated carbon, 10-12 parts of carbon fiber, 10-12 parts of graphite, 8-10 parts of dioctyl terephthalate, 6-8 parts of an ethylene-vinyl acetate copolymer, 8-10 parts of dibutyl ester, 8-10 parts of chlorinated paraffin, 5-8 parts of dioctyl sebacate, 12-15 parts of titanium dioxide and 12-15 parts of zinc chloride. The sealing ring has the beneficial effects that the strength is high, the compressive deformation is low, the high-low temperature resistances are excellent, the elongation is increased, the glue abrasion loss is low, the service life is long, the raw materials and the formula are reasonable, the cost is low, and the process is simple.

Description

technical field [0001] The invention relates to the technical field of sealing ring materials, in particular to a sealing ring. Background technique [0002] The traditional sealing ring is made of ordinary NBR as the main material, and its formula design often takes tear resistance, wear resistance and extrusion resistance as key considerations, and its use medium is not fully considered in the formula design process. The self-lubricating performance, heat resistance, aging resistance and other aspects of the sealing ring in the working condition are far from meeting the requirements of use. Therefore, it is easy to twist and crack due to the increase of torque during assembly, and the service life is short. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned shortcomings of the prior art and provide a sealing ring, which has high strength, low compression deformation, excellent high and low temperature resistance, im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L23/16C08L11/00C08L23/22C08L23/08C08K13/04C08K7/06C08K3/04C08K5/12C08K5/11C08K3/22C08K3/16
CPCC08L9/02C08L2201/08C08L2205/02C08L2205/035
Inventor 梁胜光
Owner 梁胜光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap