Lightweight rubber material

A rubber material and light-weight technology, applied in the field of rubber, can solve the problems of poor cold resistance and unstable storage of raw rubber, and improve the resistance to tensile deformation, improve the resistance to flex cracking, and facilitate transportation and processing Effect

Inactive Publication Date: 2015-09-16
FUYANG ANGU BOILER PRESSURE VESSEL MFG
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of chloroprene rubber are electrical insulation performance, poor cold resistance, and raw rubber is unstable during storage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A light rubber material is characterized in that it is made up of the following raw materials in parts by weight:

[0018] Maleic anhydride 4, 8-10% sulfuric acid 0.6, accelerator MZ2, melamine 30, 37% formaldehyde solution 5, urea 10, microcrystalline cellulose 10, neoprene S40V 230, white beeswax 6, magnesium powder 5, Stannous octoate 0.7, polyurethane 2, Suzhou soil 20, light calcium carbonate 34, ditetradecyl alcohol ester 4, wood creosote 3, antioxidant DOD 3, sulfur 2, isopropanol 1.2.

[0019] A kind of preparation method of lightweight rubber material, comprises the following steps:

[0020] (1) Add microcrystalline cellulose to 3 times of water, add isopropanol and maleic anhydride, stir evenly, add 10% sulfuric acid, react in a water bath at 60°C for 7 hours, adjust the pH to neutral, evaporate under reduced pressure Water and isopropanol are removed to obtain acid anhydride cellulose;

[0021] (2) Mix white beeswax and ditetradecyl alcohol ester, heat and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
retention rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lightweight rubber material which is composed of the raw materials of, by weight, 3-4 parts of maleic anhydride, 0.2-0.6 parts of 8-10% sulfuric acid, 1-2 parts of an accelerator MZ, 26-30 parts of melamine, 5-8 parts of a 37% formaldehyde solution, 7-10 parts of urea, 6-10 parts of microcrystalline cellulose, 210-230 parts of chloroprene rubber S40V, 3-6 parts of white beeswax, 4-5 parts of magnesium enhancement powder, 0.7-1 parts of stannous octoate, 2-3 parts of polyurethane, 16-20 parts of Suzhou soil, 28-34 parts of light calcium carbonate, 4-7 parts of bitetradecenoic alcohol ester, 2-3 parts of wood creosote, 3-4 parts of an anti-aging agent DOD, 2-3 parts of sulfur, and 1-1.2 parts of isopropanol. According to the invention, with the crosslinking effect of maleic anhydride, microcrystalline cellulose forms a closer network structure in melamine resin formed by melamine, urea and formaldehyde, such that resin viscosity and tensile deformation resistance are well improved, and certain reinforcement and tackifying functions are performed in the rubber material. Therefore, flexure cracking resistance, hot-air aging resistance and stability are improved. The rubber finished product provided by the invention has the advantages of light weight, no toxic or harmful substance volatilization, easy transportation, and easy processing.

Description

technical field [0001] The invention mainly relates to the field of rubber, in particular to a lightweight rubber material. Background technique [0002] Chloroprene rubber is made of chloroprene as the main raw material through homopolymerization or copolymerization of a small amount of other monomers. Such as high tensile strength, excellent heat resistance, light resistance, aging resistance, and oil resistance are superior to natural rubber, styrene-butadiene rubber, and butadiene rubber. It has strong flame resistance and excellent flame retardancy resistance, high chemical stability and good water resistance. The disadvantage of chloroprene rubber is that it has poor electrical insulation performance and cold resistance, and the raw rubber is unstable during storage. Neoprene is widely used, such as used to make conveyor belts and transmission belts, sheathing materials for wires and cables, to make oil-resistant hoses, gaskets, and chemical-resistant equipment l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L1/10C08L75/04C08L61/30C08K13/02C08K3/26C08K5/47C08K3/34C08K5/098C08K5/05C08K3/06
Inventor 傅贵轩陈子育赵志刚刘云飞付丽丽张涛刘长征葛哲骏
Owner FUYANG ANGU BOILER PRESSURE VESSEL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com