A kind of growth method and growth device of indium phosphide single crystal

A growth method and technology of indium phosphide, applied in the direction of single crystal growth, single crystal growth, crystal growth, etc., can solve the problems of high risk, reducing the dislocation density of indium phosphide single crystal, and large amount of red phosphorus, and achieve The effect of long service life, reduced risk and simplified equipment structure

Active Publication Date: 2017-09-19
威科赛乐微电子股份有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method adds sulfur as a dopant to reduce the dislocation density of indium phosphide single crystal, and this method uses a large amount of red phosphorus, and the excess phosphorus after crystal growth needs to be burned, which is extremely dangerous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of growth method and growth device of indium phosphide single crystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] use figure 1 In the growth device shown, the size of the pressure-resistant chamber 1 is 200mm in inner diameter; the insulation chamber 2 is a mullite insulation cotton insulation chamber with an inner diameter of 150mm and a thickness of 20mm; the insulation chamber cover 21 has a thickness of 20mm; the heater 3 has a rated power of 10kW The first crucible 4 is a quartz crucible with an inner diameter of 100 mm and a thickness of 5 mm; the second crucible 5 is a PBN crucible (pyrolytic boron nitride crucible) with an inner diameter (the diameter of the crucible after the crucible shoulders are finished) of 80 mm and a thickness of 5 mm. 5mm; the base 6 is a quartz base, which fits closely with the bottom of the second crucible 5 .

[0071] Place the quartz base 6 at the center of the bottom of the quartz crucible 4 , and place the pBN crucible 5 on the quartz base 6 . Make the dislocation density less than 2000cm -2 The direction indium phosphide single crystal see...

Embodiment 2

[0075] use figure 1 In the growth device shown, the pressure chamber 1 has an inner diameter of 250mm; the heat preservation chamber 2 is a mullite insulation cotton heat preservation chamber with an inner diameter of 200mm and a thickness of 20mm; the heat preservation chamber cover 21 has a thickness of 20mm; the heater 3 has a rated power of 15kW The first crucible 4 is a quartz crucible with an inner diameter of 150 mm and a thickness of 5 mm; the second crucible 5 is a PBN crucible (pyrolytic boron nitride crucible), and an inner diameter (the diameter of the crucible after the crucible puts the shoulders) is 110 mm. The thickness is 5mm; the base 6 is a quartz base, which closely fits with the bottom of the second crucible 5 .

[0076] Place the quartz base 6 at the center of the bottom of the quartz crucible 4 , and place the pBN crucible 5 on the quartz base 6 . Make the dislocation density less than 2000cm -2 The indium phosphide single crystal seed crystal in the ...

Embodiment 3

[0080] use figure 1 In the growth device shown, the pressure-resistant cavity 1 has an inner diameter of 300mm; the thermal insulation cavity 2 is a mullite thermal insulation cotton thermal insulation cavity with an inner diameter of 250mm and a thickness of 20mm; the thermal insulation cavity cover 21 has a thickness of 20mm; the heater 3 has a rated power of 20kW The first crucible 4 is a quartz crucible with an inner diameter of 200 mm and a thickness of 5 mm; the second crucible 5 is a PBN crucible (pyrolytic boron nitride crucible) with an inner diameter (the diameter of the crucible after the crucible shoulders are finished) of 160 mm and a thickness of 5 mm. 5mm; the base 6 is a quartz base, which fits closely with the bottom of the second crucible 5 .

[0081] Place the quartz base 6 at the center of the bottom of the quartz crucible 4 , and place the pBN crucible 5 on the quartz base 6 . Make the dislocation density less than 2000cm -2 The direction indium phosphi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for growing an indium phosphide single crystal, comprising the following steps: adopting a vertical gradient solidification method, heating an indium phosphide seed crystal, an indium phosphide polycrystal, diboron trioxide and red phosphorus, and performing crystallization growing to obtain an indium phosphide single crystal; the red phosphorus accounts for 0.05-0.1% of the total mass of the indium phosphide polycrystal, diboron trioxide and red phosphorus. The growth method provided by the invention can obtain indium phosphide single crystal with lower dislocation density without adding dopants such as iron or sulfur, which simplifies the process and saves cost, and the amount of red phosphorus used in the invention is small , which is only one tenth of the amount of red phosphorus used in the prior art, reducing the danger in production. The test results show that the average dislocation density of the indium phosphide single crystal obtained by the growth method provided by the invention is 2000-4000 / cm2, and the local dislocation density is below 500 / cm2. The invention also provides a growth device for indium phosphide single crystal.

Description

technical field [0001] The invention belongs to the technical field of crystal growth, and in particular relates to a growth method and a growth device of an indium phosphide single crystal. Background technique [0002] Indium phosphide (InP) is the earliest prepared III-V compound and one of the most important III-V semiconductor materials. At present, with the rapid development of optical fiber communication, high-speed electronic devices, high-efficiency solar cells and laser diodes, a series of superior characteristics of InP crystals can be brought into play, which has attracted more and more attention. [0003] At present, the growth methods of indium phosphide mainly include the LEC method and the VGF method. The LEC method is also called the liquid-sealed Czochralski method. This method has high equipment costs, high crystal stress, high dislocation density, and complex crystal growth process, which is not conducive to growing high-quality and large-sized single c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More