Acrylate damping coating and preparation method thereof

An acrylic and damping coating technology, which is applied in the direction of anti-fouling/underwater coatings, coatings, etc., can solve the problems of damage to the health of construction workers, heavy environmental pollution, etc., and achieve hard coating, durability and stain resistance Good, the effect of improving the damping performance

Inactive Publication Date: 2015-10-21
郭小曼
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing damping coatings are mainly made of coal tar pitch, polyurethane, etc. with specific fillers added. Since this type of dam

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] The acrylic damping coating of the present invention is composed of the following ingredients in parts by weight: 20 parts of water, 1 part of water-based dispersant, 10 parts of calcium carbonate, 20 parts of talc, and flame retardant 7 parts, 0.5 parts of water-based defoamer, 50 parts of propionate emulsion, 0.1 part of thickener, 0.1 part of damping pigment and filler, and 0.5 part of film-forming aid.

[0016] The preparation process of the acrylic damping coating is as follows:

[0017] 1) Extract 20 parts of water and 50 parts of propionate emulsion according to the proportion by weight, put them into the reactor and mix, and stir evenly;

[0018] 2) Extract the mixture of step 1, extract 1 part of aqueous dispersant, 10 parts of calcium carbonate, 20 parts of talc, 7 parts of flame retardant, and 0.5 parts of aqueous defoamer according to the weight distribution ratio and add them to the emulsion mixture;

[0019] 3) The mixture of extraction step 2 is...

Example Embodiment

[0021] Example 2

[0022] The difference from Example 1 is that the acrylic damping coating is composed of the following ingredients in parts by weight: 35 parts of water, 3 parts of water-based dispersant, 18 parts of calcium carbonate, 35 parts of talc, and 11 parts of flame retardant. Parts, 2 parts of water-based defoamer, 110 parts of propionate emulsion, 1.5 parts of thickener, 3.3 parts of damping pigments and fillers, and 1.8 parts of film forming aids.

Example Embodiment

[0023] Example 3

[0024] The difference from Example 1 is that the acrylic damping coating is composed of the following ingredients in parts by weight: 30 parts of water, 2 parts of water-based dispersant, 14 parts of calcium carbonate, 30 parts of talc, and 9 parts of flame retardant. Parts, 1.5 parts of water-based defoamer, 80 parts of propionate emulsion, 1 part of thickener, 2 parts of damping pigments and fillers, and 1.2 parts of film forming aids.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acrylate damping coating and a preparation method thereof. The acrylate damping coating comprises, by weight, 20-35 parts of water, 1-3 parts of an aqueous disperser, 10-18 parts of calcium carbonate, 20-35 parts of talcum powder, 7-11 parts of a fire retardant, 0.5-2 parts of an aqueous antifoaming agent, 50-110 parts of a propionate emulsion, 0.1-1.5 parts of a thickener, 0.1-3.3 parts of a damping pigment filler and 0.5-1.8 parts of a film forming assistant. The propionate emulsion is adopted in the preparation process of the acrylate damping coating, so the damping performance of the coating in high and low temperature state is improved, and the coating also has the advantages of good noise reduction effect, non-toxicity, no peculiar smell, hard film, good gloss retention, good durability and good pollution resistance.

Description

technical field [0001] The invention relates to an acrylic damping paint and a preparation method thereof. Background technique [0002] Under the principle of developing the coatings industry based on economy, efficiency, ecology and energy, the global coatings market is developing towards water-based and solvent-free coatings that are more suitable for environmental protection. The development of water-based damping coatings is also the overall development trend of the composite coatings industry. [0003] Existing damping coatings are mainly made of coal tar pitch, polyurethane, etc. with specific fillers added. Since this type of damping coating contains a large amount of VOC, it causes serious environmental pollution. And seriously damage the health of construction workers. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide an acrylic damping paint with consistent color, no color difference, no peculiar smell...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/08C09D7/12
CPCC09D133/00C08K3/26C08K3/34C08K13/02C08K2003/265C09D5/16C09D7/40C09D7/61
Inventor 郭小曼
Owner 郭小曼
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap