Closestool high in strength and low in weight and preparation method thereof

A high-strength, lightweight technology, applied in the toilet field, can solve the problems of bacteria breeding, difficult handling, cracks, etc., and achieve the effects of strong release ability, improved immunity, and high mechanical strength.

Active Publication Date: 2015-11-11
广东澳丽泰陶瓷实业有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large volume and weight of the toilet, it is not easy to carry, and it is easily broken by bumps
Moreover, due to many factors such as the use environment and product quality, frequent contact with dirt and sewage can easily become a place where dirt and bacteria breed, which is directly related to people's health problems.
It is easy to emit an unpleasant smell when sucked in sewage, and it is difficult to clean
Over time, cracks and leaks will occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Body formula (parts by weight): 26 parts of illite, 15 parts of potash feldspar, 19 parts of montmorillonite, 21 parts of clay, 14 parts of sodalite, 10 parts of rutile, 22 parts of halloysite, 18 parts of allophane Parts, 6 parts of barium carbonate, 3 parts of garnet, 11 parts of calcined diatomaceous earth, 8 parts of turquoise, 7 parts of rectorite, 2 parts of additives;

[0028] Glaze formula (parts by weight): 12 parts of feldspar, 8 parts of kaolin, 5 parts of germanite, 13 parts of vermiculite, 14 parts of talc, 6 parts of tourmaline powder, 4 parts of nano silver powder.

[0029] Additive formula (parts by weight): 2 parts of sodium humate, 2 parts of water glass powder, 3 parts of sodium tripolyphosphate, 52 parts of carboxymethyl cellulose, 19 parts of starch.

[0030] The method for preparing the calcined diatomaceous earth is to take the diatomaceous earth into a sodium carbonate solution with a concentration of 18%, heat it to 75°C in a water bath, keep it for 2H...

Embodiment 2

[0038] Body formula (parts by weight): 24 parts of illite, 12 parts of potash feldspar, 18 parts of montmorillonite, 20 parts of clay, 13 parts of sodalite, 7 parts of rutile, 21 parts of halloysite, 17 parts of allophane Parts, 5 parts of barium carbonate, 2 parts of garnet, 9 parts of calcined diatomaceous earth, 5 parts of sea green stone, 6 parts of rectorite, 1 part of additive;

[0039] Glaze formula (parts by weight): 6 parts of feldspar, 7 parts of kaolin, 3 parts of germanite, 12 parts of vermiculite, 11 parts of talc, 4 parts of tourmaline powder, 3 parts of nano silver powder.

[0040] Additive formula (parts by weight): 1 part of sodium humate, 1 part of water glass powder, 2 parts of sodium tripolyphosphate, 45 parts of carboxymethyl cellulose, 18 parts of starch.

[0041] The method for preparing the calcined diatomaceous earth is to take the diatomaceous earth into a sodium carbonate solution with a concentration of 15%, heat it to 70°C in a water bath, keep it for 1.5...

Embodiment 3

[0049] Body formula (parts by weight): 29 parts of illite, 16 parts of potash feldspar, 23 parts of montmorillonite, 28 parts of clay, 15 parts of sodalite, 11 parts of rutile, 27 parts of halloysite, 20 parts of allophane Parts, 7 parts of barium carbonate, 4 parts of garnet, 13 parts of calcined diatomaceous earth, 9 parts of sea green stone, 10 parts of rectorite, 3 parts of additives;

[0050] Glaze formula (parts by weight): 13 parts of feldspar, 12 parts of kaolin, 9 parts of germanite, 17 parts of vermiculite, 15 parts of talc, 8 parts of tourmaline powder, 5 parts of nano silver powder.

[0051] Additive formula (parts by weight): 3 parts of sodium humate, 3 parts of water glass powder, 4 parts of sodium tripolyphosphate, 58 parts of carboxymethyl cellulose, 23 parts of starch.

[0052] The method for preparing the calcined diatomaceous earth is to take the diatomaceous earth into a sodium carbonate solution with a concentration of 20%, heat it to 80°C in a water bath, keep i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a closestool high in strength and low in weight and a preparation method thereof. A green body of the closestool comprises 24-29 parts of illite, 12-16 parts of potassium feldspar, 18-23 parts of montmorillonite, 20-28 parts of clay, 13-15 parts of sodalite, 7-11 parts of rutile, 21-27 parts of halloysite, 17-20 parts of allophane, 5-7 parts of barium carbonate, 2-4 parts of johnstonotite, 9-13 parts of calcined kieselguhr, 5-9 parts of glauconite, 6-10 parts of rectorite and 1-3 parts of addition agents; Glaze materials are composed of 6-13 parts of feldspar, 7-12 parts of kaolin, 3-9 parts of germanite, 12-17 parts of vermiculite, 11-15 parts of talcum, 4-8 parts of tourmaline powder and 3-5 parts of nano-silver-powder. The closestool high in strength and low in weight is low in weight, high in strength, low in water absorption and capable of releasing anions and resisting against bacteria.

Description

Technical field [0001] The present invention relates to the technical field of toilets, and more specifically, to a high-strength lightweight toilet and a preparation method thereof. Background technique [0002] The official name of the toilet is the toilet. It solves the problem of people's eating and drinking Lazard in and out. It is an essential household item. Due to the relatively large volume and weight of the toilet, it is not easy to handle and is susceptible to being bumped and broken. Moreover, due to various factors such as the use environment and product quality, frequent contact with sewage and sewage can easily become a place to hide dirt and breed bacteria, which is directly related to people's health problems. When the sewage is sucked in, it is easy to emit an unpleasant smell and is difficult to clean. Over time, cracks and water leakage will occur. Summary of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B41/86
Inventor 刘贵深刘伟群侯晓东黄灿森王冁
Owner 广东澳丽泰陶瓷实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com