A kind of feldspar waste concrete and preparation method thereof

A concrete and waste technology, applied in the field of feldspar waste concrete and its preparation, can solve the problems of waste pollution, less consumption, etc., and achieve the effects of good water resistance, improved compressive performance, and increased strength

Active Publication Date: 2017-07-04
JINAN HONGWANG CONCRETE CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN201310411979.7 adds 5 to 7% feldspar to the preparation of oil sludge sand foam concrete blocks, but since feldspar is not the main component, the amount used is small, which cannot solve the waste pollution caused by a large amount of feldspar waste piled up

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of feldspar waste concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of feldspar waste concrete of the present invention, each raw material weight part is made up of: feldspar waste 830, clay 165, cement 300, phenolic fiber 40, polyvinylidene chloride fiber 27, water 85 and admixture 5.0, admixture is made of carbonyl coke 7.1 parts of aldehyde superplasticizer, 5.9 parts of sodium metaaluminate accelerator, 9.02 parts of citric acid-chitosan adhesive and 10.0 parts of diatomite powder;

[0024] Preparation method of citric acid-chitosan adhesive: Dissolve citric acid in water at a mass ratio of 1:4, stir until a uniform solution is formed, then add chitosan with 20% mass of citric acid, and stir until chitosan Just dissolve completely, and store in a sealed container at 4-10°C.

[0025] P.O42.5 Ordinary Portland cement, the length of polyvinylidene chloride fiber is 8-10mm, and the length of phenolic fiber is 3-5mm.

[0026] The preparation steps are:

[0027] (1) Grinding: Weigh the feldspar waste, crush it until the particle ...

Embodiment 2

[0031] A kind of feldspar waste concrete of the present invention, each raw material weight part is made up of: feldspar waste material 800, clay 150, cement 280, phenolic fiber 35, polyvinylidene chloride fiber 25, water 80 and admixture 4.75, admixture is made of carbonyl coke Composed of 6.7 parts of aldehyde superplasticizer, 5.8 parts of sodium metaaluminate accelerator, 8.45 parts of citric acid-chitosan adhesive and 9.8 parts of diatomaceous earth powder;

[0032] The preparation method of the citric acid-chitosan adhesive is the same as in Example 1, P.O42.5 ordinary Portland cement, the length of the polyvinylidene chloride fiber is 8-10 mm, and the length of the phenolic fiber is 3-5 mm.

[0033] The preparation steps are the same as in Example 1.

Embodiment 3

[0035] A kind of feldspar waste concrete of the present invention, each raw material weight part is made up of: feldspar waste material 850, clay 180, cement 320, phenolic fiber 45, polyvinylidene chloride fiber 30, water 95 and admixture 5.25, admixture is made of carbonyl coke Composed of 7.5 parts of aldehyde superplasticizer, 6.1 parts of sodium metaaluminate accelerator, 9.55 parts of citric acid-chitosan adhesive and 10.2 parts of diatomaceous earth powder;

[0036] The preparation method of the citric acid-chitosan adhesive is the same as in Example 1, P.O42.5 ordinary Portland cement, the length of the polyvinylidene chloride fiber is 8-10 mm, and the length of the phenolic fiber is 3-5 mm.

[0037] The preparation steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a feldspar waste material concrete and a preparation method thereof. The feldspar waste material concrete comprises the following raw materials: feldspar waste material, clay, cement, phenolic fiber, polyvinylidene chloride fiber, water and an additive, and the additive is composed of a sulfonated acetone-formaldehyde high efficiency water reducer, a sodium meta aluminate accelerator, a citric acid-chitosan adhesive and diatomite powder. The method solves the utilization problem of feldspar waste material, source of the raw materials is stable and wide, production cost is reduced, resource is saved, environment can be protected; production process is simple and feasible, operation is convenient, a mixing material integrated with ceramic, glass and stone can be prepared after mixing and calcining clay and feldspar powder, and is crushed to be the sandstone material mixing material as a concrete frame, phenolic fiber, polyvinylidene chloride fiber and the additive are added, so that the concrete has the advantages of high intensity, antifreezing performance, fire resistance, and good water proofness, and is suitable for high mine workings, railway tunnel, diversion culvert and underground engineering construction with high concrete performance requirement.

Description

technical field [0001] The invention belongs to the technical field of concrete and waste recycling, and relates to a feldspar waste concrete and a preparation method thereof. Background technique [0002] Feldspar is the result of long-term movement of the earth's crust in nature. Feldspar has a high silica content, up to 67%, and high compressive strength. The basic structure of feldspar is tetrahedral, with structural stability and other characteristics. It is usually used in the manufacture of ceramics, glass, Abrasive material. Some feldspar deposits contain too many impurities and cannot be discarded as traditional ceramics, glass and other raw materials. A large number of feldspar wastes not only cause serious pollution to air, water and soil, but also occupy a large amount of farmland, causing waste. . Therefore, it is necessary to study how to use feldspar waste rationally and effectively to make feldspar waste "turn waste into treasure". [0003] In construction...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B18/12C04B14/10C04B16/06C04B24/38
CPCY02W30/91
Inventor 沈玉婷杨昊林王建袁惠星
Owner JINAN HONGWANG CONCRETE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap