Method for preparing kaolin intercalation compound

A technology of intercalation compound and kaolin, which is applied in the direction of silicon compounds, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of easy methanol release, long reaction cycle, unstable kaolin/methanol intercalation complex, etc., to achieve The effect of high intercalation rate and short preparation process time

Inactive Publication Date: 2015-11-25
CHINA UNIV OF GEOSCIENCES (WUHAN)
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The above method has successfully prepared the imidazolium ionic liquid intercalated kaolin complex, but there are many shortcomings: first, the reaction steps are more complicated, second, the reaction cycle is long, and third, the kaolin / methanol intercalation complex is not very stable. , Methanol is easy to come out in high temperature or high humidity environment. Fourth, it is difficult for the above method to insert the ionic liquid with a high melting point into the kaolin layer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing kaolin intercalation compound
  • Method for preparing kaolin intercalation compound
  • Method for preparing kaolin intercalation compound

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation process of kaolin intercalation compound of the present invention is as follows:

[0029] According to the ratio of monochloroacetic acid to 1-methylimidazole molar ratio of 1:1, put monochloroacetic acid to melt at 70-80°C, add 1-methylimidazole and react for 4-6 hours to obtain a reddish-brown viscous liquid ; Wash with absolute ethanol until the lower layer is a white solid and the upper layer is a colorless transparent liquid, the white solid is taken out and dried to obtain an ionic liquid 1-carboxymethyl-3-methylimidazolium chloride salt; set aside.

[0030] Mix kaolin: dimethyl sulfoxide: distilled water according to 15g: 60-80mL: 5-15mL, heat and stir at 25-75°C for 48-72 hours; centrifuge, wash and dry to obtain kaolin / dimethyl sulfoxide-based intercalation complex; the interlayer distance d(001) increases from 0.72nm to 1.12nm, and the intercalation rate is about 92%. It is ready for use.

[0031] The X-ray powder crystal diffraction pattern o...

Embodiment 1

[0033] Weigh 0.5 g of the spare kaolin / dimethyl sulfoxide intercalation complex and mix with 1 g of 1-carboxymethyl-3-methylimidazolium chloride salt, grind and mix with a mortar.

[0034] The ground mixture was placed in an autoclave, protected by nitrogen gas, and heated in a 210°C drying oven for 4 hours.

[0035] The reaction product was washed repeatedly with dimethyl sulfoxide to remove the residue of 1-carboxymethyl-3-methylimidazolium chloride salt, and then washed with absolute ethanol for 3-4 times and centrifuged.

[0036] The obtained reaction product was dried in a vacuum oven at 80°C.

[0037] The X-ray powder crystal diffraction pattern of kaolin / 1-carboxymethyl-3 methylimidazolium chloride salt intercalation complex in the present embodiment is as follows image 3 , it can be seen from the figure that the interlayer spacing of kaolin increases from 0.71nm to 1.36nm, and the diffraction peak intensity of the intercalation complex is relatively strong, indicatin...

Embodiment 2

[0039] Weigh 0.5 g of the spare kaolin / dimethyl sulfoxide intercalation complex and mix with 1.5 g of 1-carboxymethyl-3-methylimidazolium chloride salt, grind and mix with a mortar.

[0040] The ground mixture was placed in an autoclave, protected by nitrogen gas, and heated in a 210°C drying oven for 4 hours.

[0041] The reaction product was washed repeatedly with dimethyl sulfoxide to remove the residue of 1-carboxymethyl-3-methylimidazolium chloride salt, and then washed with absolute ethanol for 3-4 times and centrifuged.

[0042] The obtained reaction product was dried in a vacuum oven at 80°C.

[0043]The X-ray powder crystal diffraction pattern of the present embodiment kaolin / 1-carboxymethyl-3 methylimidazolium chloride salt intercalation complex is as follows Figure 4 , the (001) interlayer spacing is 1.35nm, and the intercalation rate reaches 84.00%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a kaolin intercalation compound. Kaolin, dimethyl sulfoxide and distilled water are mixed, and are heated and stirred for 48-72 hours at the temperature of 25 DEG C to 75 DEG C; centrifugal separation, washing and drying are carried out to obtain a kaolin / dimethyl sulfoxide intercalation compound; the obtained kaolin / dimethyl sulfoxide intercalation compound and 1-carboxymethyl-3 methylimidazole chlorine salt are mixed and heated in the environment of 190 DEG C to 210 DEG C under inert gas shielding, and cooling is carried out after heat preservation is carried out for 4-12 h; 1-carboxymethyl-3 methylimidazole chlorine salt is removed through washing of dimethyl sulfoxide, then washing is carried out through absolute ethyl alcohol, centrifugal separation and drying are carried out, and the kaolin / 1- carboxymethyl-3 methylimidazole chlorine salt intercalation compound is obtained. According to the method, imidazole ionic liquid can enter an interlayer of the kaolin in an intercalation mode only through a two-step method, and therefore the preparation process is short in time and high in intercalation efficiency.

Description

technical field [0001] The invention relates to the field of deep processing of kaolin materials, in particular to a preparation method of a kaolin intercalation compound. Background technique [0002] Kaolin is a common clay mineral, which is widely used in papermaking, coating, ceramics, building materials, refractory materials, petrochemical industry, agriculture, cutting-edge defense technology and other fields. The main component of kaolin in nature is kaolinite, which is a typical layered silicate mineral, and the interlayer distance d(001) is about 0.72nm. As a 1:1 layered clay mineral, kaolin is widely used in organic-inorganic composite materials. In recent years, the research on kaolin intercalation has been more active. The intercalation of kaolin with organic matter can significantly increase the interlayer spacing of kaolin, and make kaolin composite materials have the physical and chemical properties of kaolin and organic matter. Therefore, it is widely used i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/44
Inventor 朱小燕朱志超雷新荣严春杰陈洁渝吴红丹曾萍
Owner CHINA UNIV OF GEOSCIENCES (WUHAN)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com