A kind of fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent and preparation method thereof

A technology of phenyl hydrogen-containing silicone oil and cross-linking agent, which is applied in the field of fluorine-containing phenyl hydrogen-containing silicone oil cross-linking agent and its preparation, and can solve the problem that it is difficult to obtain completely transparent Products, phenylcyclosiloxane ring body stress, hydrogen-containing silicone oil cross-linking and other problems, to improve product quality and stability, high product yield, avoid residue effects

Inactive Publication Date: 2017-10-20
SOUTH CHINA UNIV OF TECH
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process cannot use alkaline catalysts, which will easily lead to hydrogen loss and crosslinking of hydrogen-containing silicone oil, and because phenyl cyclosiloxane is solid, it is incompatible with fluorine-containing cyclosiloxane, methyl cyclosiloxane, and hydrogen-containing silicone oil. soluble, and the stress of the phenylcyclosiloxane ring is large, it is difficult to completely open the ring under acidic conditions, and it is difficult to obtain a completely transparent product even if the reaction time is prolonged

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Under the condition of stirring (stirring speed is 80 rpm), add 200g of methyl silicone oil (molecular weight 800) with a viscosity of 5mPa.s, 200g of octaphenylcyclotetrasiloxane and 100g of a viscosity of 5mPa. s methyl fluorosilicone oil (molecular weight 730), then add 0.25g potassium hydroxide, stir for 10min and mix well; heat up to 150°C, stir at constant temperature for 8h, stop heating, cool to room temperature, add 20g concentrated sulfuric acid (mass concentration is 98% ) and 500g of hydrogen-containing silicone oil (molecular weight: 4800) with a hydrogen content of 1.6%, equilibrated at room temperature for 4h, added 80g of sodium carbonate for neutralization for 1h, and vacuum filtered to obtain a colorless and transparent fluorine-containing phenyl hydrogen-containing silicone oil. Weighing 950g, its yield is 95%. The silicone oil has a refractive index of 1.4644 at 25° C., a viscosity of 35 mPa.s, and a hydrogen content of 0.79%.

Embodiment 2

[0031] Under stirring conditions (stirring speed is 100 rpm), add 200g of methyl silicone oil (molecular weight 1300) with a viscosity of 10mPa.s, 200g of octaphenylcyclotetrasiloxane and 100g of a viscosity of 50mPa. s methyl fluorosilicone oil (molecular weight 3500), then add 0.5g potassium hydroxide, stir for 10min to mix; heat up to 160°C, stir at constant temperature for 7h, stop heating, cool to room temperature, add 50g concentrated sulfuric acid (mass concentration is 98% ) and 500g of hydrogen-containing silicone oil (molecular weight: 5000) with a hydrogen content of 0.6%, equilibrated at room temperature for 5 hours, added 100g of sodium carbonate to neutralize for 2 hours, and vacuum filtered to obtain a colorless and transparent fluorine-containing phenyl hydrogen-containing silicone oil. Weighing 955g, the yield is 95.5%. The silicone oil has a refractive index of 1.4641 at 25° C., a viscosity of 55 mPa.s, and a hydrogen content of 0.28%.

Embodiment 3

[0033] Under the condition of stirring (stirring speed is 120 rpm), add 150g of methyl silicone oil (molecular weight 3800) with a viscosity of 50mPa.s, 250g of octaphenylcyclotetrasiloxane and 100g of a viscosity of 100mPa.s in a 2L three-necked flask. s of methyl fluorosilicone oil (molecular weight 5500), then add 0.25g of lithium hydroxide, stir for 8min to mix; heat up to 180°C, stir at constant temperature for 5h, stop heating, cool to room temperature, add 18g of concentrated sulfuric acid (mass concentration is 98% ) and 100g of hydrogen-containing silicone oil (molecular weight: 4800) with a hydrogen content of 1.6%, equilibrated reaction at room temperature for 6h, added 54g of sodium bicarbonate for neutralization for 1.5h, and vacuum filtration to obtain a colorless and transparent fluorine-containing phenyl hydrogen-containing silicone oil. Weighing 952g, the yield was 95.2%. The silicone oil has a refractive index of 1.4932 at 25° C., a viscosity of 176 mPa.s, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of crosslinking agents, and discloses a fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent and a preparation method thereof. The method is to add an alkali catalyst to low-viscosity methyl silicone oil, phenylcyclosiloxane, and fluorosilicone oil, mix well, heat up and stir at a constant temperature, cool down, add acid catalyst and hydrogen-containing silicone oil in sequence, and balance the reaction. Subsequent treatment is carried out to obtain a colorless and transparent fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent. In the preparation method of the present invention, there is no need to add methylcyclosiloxane and end-capping agent, which simplifies the process and improves product quality and stability; the raw materials used do not contain chlorine and alkoxy groups, avoiding the introduction of chloride ions and alkane Oxygen residues; the present invention does not use any solvent, will not cause harm to the human body, and will not cause pollution to the environment; the yield of the crosslinking agent prepared by the present invention is high.

Description

technical field [0001] The invention belongs to the technical field of crosslinking agents, and relates to a fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent, in particular to a fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent and a preparation method thereof. The fluorine-containing phenyl hydrogen-containing silicone oil crosslinking agent specifically refers to a hydrogen-containing silicone oil crosslinking agent containing fluorine groups and phenyl co-modified. Background technique [0002] Phenyl silicone rubber is one of the main varieties of silicone rubber. It has good high and low temperature resistance, radiation resistance, etc., and is widely used in electronics, machinery, aerospace and other fields. Low phenyl silicone rubber has remarkable low temperature resistance and is also elastic at -110°C; high phenyl silicone rubber can be used for a long time at 350°C; under γ-ray irradiation, phenyl silico...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/44
Inventor 涂伟萍朱淮军戴子林
Owner SOUTH CHINA UNIV OF TECH