Method for preparing nanosilver and finishing fabric

A nano-silver and fabric technology, applied in the processing of textile materials, liquid/gas/steam textile material processing, knitting, etc., can solve the problems of unsuitable textiles, prevent skin fungus and ringworm, simple process, and improve The effect of added value

Inactive Publication Date: 2015-12-09
钱景
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, permethrin is mainly used as a low-toxicity insecticide, and can be used to control various pests on cotton, vegetables, tea, and fruit trees. It is especially suitable for the control of hygiene pests, and is not suitable for textiles that are in contact with human skin for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Mix 100ml of 0.01g / L thymol solution with 1ml of 1g / L silver nitrate solution, stir at a constant speed for 10min at a temperature of 80°C to obtain a nano-silver colloid solution, and wash it repeatedly with ethanol and deionized water , centrifuged, and vacuum-dried at 80°C for 1 h to obtain silver nanoparticles.

[0017] Prepare a nano-silver solution with a concentration of 0.01-10g / L, and then immerse the fabric in it, the immersion time is 100min, two dipping and two rolling, the pressure is 1kg / m 2 , the liquid retention rate is 90%, pre-baked at 120°C for 3 minutes, baked at 180°C for 30 seconds, washed with water until neutral, and then dried at 30°C at low temperature; the fabric contains veil and bottom yarn, and the veil is 150D / 96F Double yarn made of polyester low stretch yarn DTY and PHA fiber blended, the blending ratio of face yarn DTY and PHA is 60%:40%, and the bottom yarn is 150D / 144F polyester low stretch yarn DTY. described therein.

Embodiment 2

[0019] Mix 50ml of 0.1g / L thymol solution with 1ml of 10g / L silver nitrate solution, stir at a uniform speed for 100min at a temperature of 50°C to obtain a nano-silver colloid solution, and wash it repeatedly with ethanol and deionized water , centrifuged, and vacuum-dried at 80°C for 12 hours to obtain silver nanoparticles.

[0020] Prepare a nano-silver solution with a concentration of 0.01-10g / L, and then immerse the fabric in it, the immersion time is 100min, two dipping and two rolling, the pressure is 1kg / m 2 , the liquid retention rate is 90%, pre-baked at 120°C for 3 minutes, baked at 180°C for 30 seconds, washed with water until neutral, and then dried at 30°C at low temperature; the fabric contains veil and bottom yarn, and the veil is 150D / 96F Double yarn made of polyester low stretch yarn DTY and PHA fiber blended, the blending ratio of face yarn DTY and PHA is 60%:40%, and the bottom yarn is 150D / 144F polyester low stretch yarn DTY. described therein.

Embodiment 3

[0022] The 1g / L thymol solution of 10ml was mixed with the silver nitrate solution of 1ml 50g / L, and stirred at a uniform speed for 300min at a temperature of 30°C to obtain a nano-silver colloid solution, which was repeatedly washed with ethanol and deionized water, After centrifugation and vacuum drying at 80°C for 24 hours, silver nanoparticles were obtained.

[0023] Prepare a nano-silver solution with a concentration of 0.01-10g / L, and then immerse the fabric in it, the immersion time is 100min, two dipping and two rolling, the pressure is 1kg / m 2 , the liquid retention rate is 90%, pre-baked at 120°C for 3 minutes, baked at 180°C for 30 seconds, washed with water until neutral, and then dried at 30°C at low temperature; the fabric contains veil and bottom yarn, and the veil is 150D / 96F Double yarn made of polyester low stretch yarn DTY and PHA fiber blended, the blending ratio of face yarn DTY and PHA is 60%:40%, and the bottom yarn is 150D / 144F polyester low stretch yar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Concentrationaaaaaaaaaa
Concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing nanosilver and finishing a fabric. The method comprises the steps: according to the volume ratio of 100:1-1:1, mixing a 0.01-1 g / L thymol solution with a 0.01-100 g / L silver nitrate solution, carrying out uniform-velocity stirring for 10-600 min under the condition of the temperature of 30 DEG C-80 DEG C, to obtain a nanosilver colloidal solution, repeatedly washing with ethanol and deionized water, centrifuging, carrying out drying treatment to obtain silver nanoparticles, then dipping the fabric into a nanosilver solution with the concentration of 0.01-10 g / L, and dipping for two times and rolling for two times. Thymol is used as a reductant and a stabilizer, and the method has the advantages of simple process, mild reaction, green environmental protection and the like. The prepared nanosilver is used in the textile field, can prepare the blended fabric having multiple efficacies of fragrance, corrosion prevention, sterilization, mite removal, dermatomycosis and tinea disease prevention, and greatly improves the added value of textiles.

Description

technical field [0001] The invention belongs to the field of textiles, in particular to a method for preparing nano silver and fabric finishing. Background technique [0002] Textiles are recognized as a medium for the growth of microorganisms such as bacteria and fungi. Microbial communities in nature widely exist in the surrounding environment, and can multiply rapidly once encountering suitable humidity, nutrients and temperature. Microorganisms growing on textiles not only affect the performance of textiles themselves, but also affect the health of users. Therefore, how to suppress or kill the microorganisms attached to textiles, especially the textile industry, is an urgent problem to be solved. [0003] Antibacterial textiles can increase the added value of products and meet people's needs for health and environmental protection. Therefore, they have attracted more and more attention from textile researchers and have great market potential. In the research field of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/83D06B3/18D06B15/00B22F9/24D04B1/04D04B21/04D06M101/32
Inventor 钱景赵兵
Owner 钱景
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com