Hydrophilic and oleophobic filter material and preparation method thereof

A hydrophilic and oleophobic processing method technology, which is applied in the field of filter materials, can solve the problems that cannot be washed cleanly and hinder the popularization and application of fiber ball filter materials, etc., and achieve the effect of simple operation, good backwash regeneration performance, and fine fiber diameter

Inactive Publication Date: 2015-12-16
曾金华
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the extremely strong lipophilicity on the surface of the fiber ball filter material, it cannot be washed clean afte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A processing method for a hydrophilic and oleophobic filter material, comprising the steps of:

[0026] 1) Raw material preparation: prepare 90kg fiber silk and 10kg cotton seed hulls;

[0027] 2) Treatment of cottonseed hulls:

[0028] ①Crush cottonseed hulls: Add pure water according to the weight ratio of 1:8, process it with a high-speed shear emulsifier for 20 minutes at a speed of 8000r / min, and then process it with a high-pressure micro-jet ultrafine pulverization equipment at 25°C, with a processing pressure of 120MPa, the number of treatments is 4 times, and a paste-like slurry is obtained;

[0029] ②Drying: Dry the paste slurry obtained in step ①, and pass through a 100-mesh sieve to obtain powder;

[0030] 3) Bundle the fiber filaments, so that the fiber bundles are clamped and straightened;

[0031] 4) Use an ultrasonic welding head to melt the fiber bundles at intervals to form fusion points, add the cottonseed hull powder obtained in step 2) while melti...

Embodiment 2

[0034] A processing method for a hydrophilic and oleophobic filter material, comprising the steps of:

[0035] 1) Raw material preparation: prepare 95kg fiber filaments and 5kg cottonseed hulls;

[0036] 2) Treatment of cottonseed hulls:

[0037] ①Crush the cottonseed hulls: Add pure water according to the weight ratio of 1:10, and process it with a high-speed shear emulsifier for 10 minutes at a speed of 10,000r / min, and then process it with a high-pressure micro-jet ultrafine pulverization equipment at 25°C, and the processing pressure is 100MPa, the number of treatments is 2 times, and a paste-like slurry is obtained;

[0038] ②Drying: Dry the paste slurry obtained in step ①, and pass through a 100-mesh sieve to obtain powder;

[0039] 3) Bundle the fiber filaments, so that the fiber bundles are clamped and straightened;

[0040] 4) Use an ultrasonic welding head to melt the fiber bundles at intervals to form fusion points, add the cottonseed hull powder obtained in step...

Embodiment 3

[0043] A processing method for a hydrophilic and oleophobic filter material, comprising the steps of:

[0044] 1) Raw material preparation: prepare 92kg fiber filaments and 8kg cottonseed hulls;

[0045] 2) Treatment of cottonseed hulls:

[0046] ①Crush the cottonseed hulls: Add pure water according to the weight ratio of 1:10, process it with a high-speed shear emulsifier for 15 minutes at a speed of 12000r / min, and then process it with a high-pressure micro-jet ultrafine pulverization equipment at 25°C, with a processing pressure of 80MPa, the number of treatments is 3 times, and a paste-like slurry is obtained;

[0047] ②Drying: Dry the paste slurry obtained in step ①, and pass through a 100-mesh sieve to obtain powder;

[0048] 3) Bundle the fiber filaments, so that the fiber bundles are clamped and straightened;

[0049] 4) Use an ultrasonic welding head to melt the fiber bundles at intervals to form fusion points, add the cottonseed hull powder obtained in step 2) whi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hydrophilic and oleophobic filter material and a preparation method thereof. By effective technology, produced filaments are subjected to chemical modification and are added with plant composition, and thus, treating performance thereof is changed. Compared with common fiber balls, the hydrophilic and oleophobic filter material has the advantages that the modified fiber balls have small wire diameter and large specific surface area which is up to 2500m2/g. Owing to the characteristic of small wire diameter of the filaments, pores of filter layers after superposition of the filaments are small and the porosity of the filter layers after superposition is over 85%, and accordingly the filter material is superior to other filter materials in terms of interception of suspended matter.

Description

technical field [0001] The invention belongs to the technical field of filter materials, and in particular relates to a hydrophilic and oleophobic filter material and a processing method thereof. Background technique [0002] Plant fibers are formed by the development of different meristems. The fibers of xylem and phloem originate from the procambium or cambium. Some fibers can be generated by the basic meristem, the cells that will develop into fibers in the future, stop dividing horizontally very early, and only elongate longitudinally. Part of the fibers in the vascular bundle sheath can be generated from the procambium, and the other part can be formed from the basic meristem. [0003] Cotton fibers are elongated portions of epidermal cells on cotton ovules. Its development process is: when the cotton ovule is fertilized, the hair cells that produce fibers on the epidermis of the ovule elongate rapidly. Since then, the cell wall has gradually thickened, that is, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D39/04
Inventor 曾金华
Owner 曾金华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap