A laser-infocus arc double-sided symmetrical composite welding method

An -infocus, hybrid welding technology, applied in the field of laser-InFocus arc double-sided symmetrical hybrid welding, can solve the problems of high laser power requirements and high cost, and achieve the effects of improving welding quality, reducing equipment costs and reducing costs.

Active Publication Date: 2017-06-16
哈尔滨工大焊接科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve many problems such as high laser power requirement and high cost during laser-TIG double-sided welding of medium and thick plates, and proposes a laser-InFocus arc double-sided symmetrical composite welding method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A laser-infocus arc double-sided symmetrical composite welding method
  • A laser-infocus arc double-sided symmetrical composite welding method
  • A laser-infocus arc double-sided symmetrical composite welding method

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0025] Specific embodiment one: a kind of laser-InFocus electric arc double-sided symmetric composite welding method of the present embodiment, it is carried out according to the following steps:

[0026] Step 1: Process the workpiece to be welded into an I-shaped or Y-shaped groove, and grind and clean the processed groove and the surfaces on both sides, and fix the polished and cleaned workpiece to be welded on the welding fixture ;

[0027] Step 2: keep the laser beam and the InFocus arc welding torch on the same axis during the welding process, and the angle between the axis and the workpiece is 85° to 95°;

[0028] Step 3: Set the welding process parameters: the spot diameter is 0.1-0.5mm, the defocus is ﹣3-﹢3mm, the laser power is 500-5000W, the InFocus arc current is 50-1000A, and the welding speed is 50-900mm / min , both the laser and InFocus shielding gas use Ar gas, the laser shielding gas flow rate is 10-30L / min, and the InFocus shielding gas flow rate is 10-25L / min...

specific Embodiment approach 2

[0031] Specific embodiment two: the difference between this embodiment and specific embodiment one is: the hybrid welding is to use the laser and the InFocus electric arc to be welded in parallel with the direction of the welding seam, and the welding conditions are: the welding torch and the laser head are in the The same plane, and the plane is perpendicular to the direction of the weld, the laser head is located on the side of the workpiece with a relatively high melting point among the workpieces to be welded, and the focus of the laser beam is focused on the edge of the side of the workpiece with a relatively high melting point among the butt welded workpieces to be welded, The angle between the laser beam and the vertical direction is 5-30°; the welding torch of the InFocus arc is located on the side of the workpiece with a relatively low melting point among the workpieces to be welded, and the welding torch is placed at the center of the weld gap. Others are the same as ...

specific Embodiment approach 3

[0032] Embodiment 3: The difference between this embodiment and Embodiment 1 is that the angle between the axis and the workpiece in step 2 is 90°-95°. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a laser-InFocus electric arc double-face symmetric composite welding method, and relates to welding methods. The method comprises the steps of firstly, machining and grinding or cleaning a workpiece to be welded; secondly, adjusting the position of an InFocus welding gun and the position of a laser head; thirdly, setting welding parameters, wherein the diameter of light spots ranges from 0.1 mm to 0.5 mm, the defocusing amount ranges from -3mm to 3 mm, the laser power ranges from 500 W to 5000 W, the electric arc current of the InFocus welding gun ranges from 50 A to 1000 A, the welding speed ranges from 50 mm / min to 900 mm / min, Ar gas protection is carried out, the gas flow ranges from 10 L / min to 30 L / min, and the InFocus protection gas flow ranges from 10 L / min to 25 L / min; and fourthly, carrying out composite welding. The InFocus welding gun and a TIG welding machine are matched well, a dedicated power source is not needed, the equipment cost is reduced, the welding gun is reliable and durable, the interchangeability of the consumable is good, and due to the design of the InFocus welding gun, mechanization and automation are easily achieved.

Description

technical field [0001] The invention relates to a laser-InFocus arc double-sided symmetrical composite welding technology, which belongs to the field of material processing engineering. Background technique [0002] In welding production, how to improve product quality and welding productivity and reduce welding cost has always been an urgent problem to be solved. Due to the advantages of high power density, large penetration depth at the same heat input, narrow heat-affected zone, small welding deformation, and fast welding speed, lasers have been more and more widely used in welding production. However, laser welding also has some disadvantages, such as low energy conversion and utilization rate, high welding cost, especially difficult to weld aluminum alloy materials with high reflectivity and high thermal conductivity; the welding process is unstable, and to a large extent This limits the scope of application of laser welding technology. [0003] The use of laser fille...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/348
Inventor 杨雨禾雷正龙陈彦宾张可召李鹏
Owner 哈尔滨工大焊接科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com