Environment-friendly medical polyacrylate pressure-sensitive adhesive

A technology of pressure-sensitive adhesives and polyacrylates, applied in the direction of adhesive additives, ester copolymer adhesives, adhesive types, etc., can solve problems such as difficult application, environmental and product pollution, and achieve small usage , reduce pollution, reduce the effect of consumption

Active Publication Date: 2016-01-06
四川厚生天佐药业有限公司
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main disadvantage of solvent-based polyacrylate pressure-sensitive adhesives is that the use of organic solvents in the formulation and manufacturing process will pollute the environment and prod

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] The environment-friendly medical polyacrylate pressure-sensitive adhesive is prepared by the aforementioned preparation method of the present invention, wherein in parts by weight, the soft monomer is 20 parts of ethyl acrylate, 15 parts of butyl acrylate, 10 parts of acrylate-2-ethyl Hexyl ester, its T g -70°C, the hard monomer is 10 parts of methyl methacrylate, 5 parts of methyl acrylate, the functional monomer is 3 parts of methacrylic acid, 2 parts of hydroxyethyl acrylate, 2 parts of acrylamide, and the initiator is 0.03 1 part of dibenzoyl peroxide, 0.02 part of dicumyl peroxide, 3 parts of glycerin rosin ester, 2 parts of pentaerythritol rosin ester, 5 parts of terpene resin, and 1 part of epoxy group-containing compound Propylene oxide, 0.5 parts of butylene oxide, the solvent is 20 parts of ethyl acetate, 5 parts of methanol, and 5 parts of isopropanol. After the preparation is completed, the properties of the product are tested.

Example Embodiment

[0029] Example 2

[0030] Environmentally friendly medical polyacrylate pressure-sensitive adhesives are prepared by the aforementioned preparation method of the present invention, wherein in parts by weight, the soft monomer is 20 parts of ethyl acrylate, 15 parts of isooctyl acrylate, 10 parts of acrylic acid-2- Ethylhexyl ester, its T g -68°C, the hard monomer is 10 parts of methyl methacrylate, 5 parts of styrene, the functional monomer is 3 parts of methacrylic acid, 2 parts of hydroxyethyl acrylate, 2 parts of maleic anhydride, and the initiator is 0.03 1 part of dibenzoyl peroxide, 0.02 part of tert-butyl peroxide benzoate, 5 parts of glycerin rosin ester, 5 parts of terpene resin for tackifying resin, 1 part of propylene oxide, 0.5 part of epoxy group-containing compound Butylene oxide, the solvent is 20 parts of ethyl acetate, 5 parts of methanol, and 5 parts of isopropanol. After the preparation is completed, the properties of the product are tested.

Example Embodiment

[0031] Example 3

[0032] Environmentally friendly medical polyacrylate pressure-sensitive adhesives are prepared by the aforementioned preparation method of the present invention, wherein in parts by weight, the soft monomer is 20 parts of butyl acrylate, 15 parts of isooctyl acrylate, 10 parts of acrylic acid-2- Ethylhexyl ester, its T g -66°C, the hard monomer is 5 parts of methyl methacrylate, 10 parts of styrene, the functional monomer is 2 parts of methacrylic acid, 3 parts of hydroxyethyl acrylate, 2 parts of acrylamide, and the initiator is 0.03 parts Dibenzoyl peroxide, 0.02 parts of dicumyl peroxide, 5 parts of glycerin rosin ester, 2 parts of pentaerythritol rosin ester, 3 parts of terpene resin, and 1 part of epoxy group-containing compound Propane, 0.5 parts of butylene oxide, the solvent is 20 parts of ethyl acetate, 5 parts of methanol, 5 parts of isopropanol. After the preparation is completed, the properties of the product are tested.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an environment-friendly medical polyacrylate pressure-sensitive adhesive. The pressure-sensitive adhesive is prepared from a soft monomer, a hard monomer, a functional monomer, tackifying resin, an initiator, a compound containing epoxy groups and solvent, wherein the glass-transition temperature of the soft monomer is minus 65 DEG C-70 DEG C. The soft monomer can be ethyl acrylate, or butyl acrylate, or iso-octyl acrylate, or 2-ethylhexyl acrylate or the like, the hard monomer can be methyl methacrylate, or methyl acrylate, or phenylethylene, or vinyl acetate, or acrylonitrile or the like, the compound containing epoxy groups can be epoxypropane, or epoxybutane, or diphenol propane epoxy resin, or tetraphenol epoxy resin, or naphthol linetype novolac epoxy, or vinylcyclohexene dioxide epoxy resin or the like, and the solvent can be ethyl acetate, or normal hexane, or heptane, or methyl alcohol, or isopropanol, or butanone or the like. The pressure-sensitive adhesive can be used in the medical and health field.

Description

technical field [0001] The invention relates to a medical pressure-sensitive adhesive, which belongs to the field of polymer materials. Background technique [0002] Pressure-sensitive adhesive is a kind of adhesive that can be bonded to the adherend under the light pressure of external force. With its unique performance and characteristics, it has become the product with the largest amount of use and the widest application range among adhesives. Its products are almost found in various fields such as packaging, automobiles, transportation, communications, electrical appliances, building materials, machinery, aviation, light industry, and hygiene. . Among them, polyacrylate pressure-sensitive adhesives are relatively cheap due to their simple formula, wide bonding range, good weather resistance, strong light resistance, excellent oil resistance, good water resistance, no phase separation and migration, and convenient operation. For reasons such as pressure-sensitive adhesi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J11/06C09J11/08C08F220/18C08F220/14C08F220/06C08F220/28C08F220/56C08F212/08C08F222/08C08F218/08
Inventor 任建华
Owner 四川厚生天佐药业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap