Production method for scientific and technological ecological impregnated paper

A production method and a technology of impregnating paper, which are applied in papermaking, paper, paper coating, etc., can solve problems such as adverse effects on the ecological environment and forest resources, poor use effects of home decoration, and effects on surface aesthetics, and achieve the elimination of bottoming and carbonization. The effect of optimization of impregnation process parameters and shortening of curing time

Active Publication Date: 2016-01-06
DILONG NEW MATERIAL LINYI
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the natural characteristics of wood, there are some insurmountable defects in the veneer. The wood fibers only have tension in the direction of tree growth (longitudinal), and there is almost no tension in the horizontal direction, resulting in longitudinal cracking of the board during use.
Secondly, the sag on the surface of the wood fiber itself, in the process of pressing, will appear incompletely pressed locally, which is manifested as carbonization of the board surface, which affects the choice of color on the board surface. You can only choose light colors instead of dark colors, resulting in Choices are limited
Furthermore, due to the fact that the veneer's own scars and black lines are difficult to completely cover and the surface tension is limited, there will be bottom-through phenomenon and surface unevenness during the pressing process, which will have a great impact on the appearance of the surface and bring bad effects to home decoration.
In addition, in the production of veneer, a large amount of wood is used, which has a considerable adverse impact and waste on the country's ecological environment and forest resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A production method of scientific and technological ecological impregnated paper, it comprises the following steps:

[0021] (1) Preparation of urea-formaldehyde glue: Put 2,500 kg of formaldehyde into the reactor, add polystyrene: melamine: 1,2-dimethylimidazole: sodium alkylbenzene sulfonate according to the ratio of 15:20:3:0.3 Accelerator 15 kilograms and use sodium hydroxide solution to adjust the pH value to 7.2, then stop heating after heating to 86-87 ° C, keep warm for 20 minutes; add 20% formic acid in three times to adjust the pH value to 4, the time interval is 5 minutes, the temperature Automatically rise to 93-96°C. After about 90 minutes, put the glue into 35°C water to detect the fog point. When white fog appears, add 35 kg of the above-mentioned accelerator, and then adjust the pH value to 5 with sodium hydroxide, then start to cool down. After the temperature drops to 60°C, add 550 kg of urea and 350 kg of water, and then cool down to 35°C.

[0022] (...

Embodiment 2

[0029] A production method of scientific and technological ecological impregnated paper, it comprises the following steps:

[0030] (1) Preparation of urea-formaldehyde glue: Put 2,500 kg of formaldehyde into the reactor, add polystyrene: melamine: 1,2-dimethylimidazole: sodium alkylbenzene sulfonate according to the ratio of 15:20:3:0.3 15 kg of the accelerant was prepared and the pH value was adjusted to 8 with sodium hydroxide solution, then heated to 86-87°C, then stopped heating, and kept warm for 20 minutes; 20% formic acid was added three times to adjust the pH value to 4.6, the time interval was 10 minutes, and the temperature Automatically rise to 93-96°C. After about 90 minutes, put the glue into 35°C water to detect the fog point. When white fog appears, add 35 kg of the above-mentioned accelerator, and then adjust the pH value to 8 with sodium hydroxide and start to cool down. After the temperature drops to 60°C, add 550 kg of urea and 350 kg of water, and then coo...

Embodiment 3

[0038] A production method of scientific and technological ecological impregnated paper, it comprises the following steps:

[0039](1) Preparation of urea-formaldehyde glue: Put 2,500 kg of formaldehyde into the reactor, add polystyrene: melamine: 1,2-dimethylimidazole: sodium alkylbenzene sulfonate according to the ratio of 15:20:3:0.3 15 kg of the accelerant was prepared and the pH value was adjusted to 7 with sodium hydroxide solution, then heated to 86-87°C, then stopped heating, and kept warm for 20 minutes; 20% formic acid was added in three times to adjust the pH value to 4.5, the time interval was 8 minutes, and the temperature Automatically rise to 93-96°C. After about 90 minutes, put the glue into 35°C water to detect the fog point. When white fog appears, add 35 kg of the above-mentioned accelerator, and then adjust the pH value to 7 with sodium hydroxide and start to cool down. After the temperature drops to 60°C, add 550 kg of urea and 350 kg of water, and then co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method for scientific and technological ecological impregnated paper. The method is sequentially carried out according to the following steps: preparing urea-formaldehyde glue; preparing triamine glue; carrying out primary impregnation; carrying out primary drying; carrying out coating; carrying out secondary impregnation; carrying out secondary drying; carrying out tailoring; carrying out inspection; carrying out packaging; and putting the paper in storage. The scientific and technological ecological impregnated paper prepared by virtue of the method can fully replace wood veneer for veneer manufacture of an ecological board and eliminate adverse effect caused by wood veneer in a home decoration process, so that the integral quality level of the ecological board is improved. Compared with the impregnated paper prepared from urea-formaldehyde glue and triamine glue, the impregnated paper disclosed by the invention is high in impact resistance and wear resistance, low in content of free formaldehyde, smooth and uniform in distribution of glue, and can fully cover the texture of the board, so that the bottom exposing and carbonizing phenomena are eliminated, the yield of a product is improved and the service life of the product is prolonged.

Description

technical field [0001] The invention relates to a production method, in particular to a production method of scientific and technological ecological impregnated paper. Background technique [0002] At present, the custom-made furniture in the home improvement market mostly uses ecological panels as the main material for processing, while the veneer of the ecological panels uses veneer to improve the flatness and covering effect of the surface. The veneer plays a key role in the overall decorative effect of the panels. Due to the natural characteristics of wood, there are some insurmountable defects in veneer. The wood fibers only have tension in the direction of tree growth (longitudinal), and there is almost no tension in the transverse direction. As a result, the board will crack longitudinally during use. Secondly, the sag on the surface of the wood fiber itself, in the process of pressing, will appear incompletely pressed locally, which is manifested as carbonization of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H23/24D21H25/06D21H17/49D21H19/24C08G12/12C08G12/32
Inventor 孙建林段术林谭富国
Owner DILONG NEW MATERIAL LINYI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products