Parking lot information display board capable of adjusting brightness and manufacturing method thereof

A production method and technology for adjusting brightness, applied in the field of transportation, can solve the problems of light insensitivity of display boards, unclear display information, poor reading information by users, etc.

Inactive Publication Date: 2016-01-06
肖白玉
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, under outdoor conditions, the general parking lot display board is not sensitive to light. Due to the influence of sunlight, etc., it will cause problems such as unclear display information, resulting in poor reading information for users.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Parking lot information display board capable of adjusting brightness and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Assemble the information display board 10 , the electrochromic device 20 and the control module 30 .

[0068] Making the electrochromic device 20 includes:

[0069] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0070] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 320nm;

[0071] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 220nm; W film is used as WO 3 a growth source for the nanowires;

[0072] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained...

Embodiment 2

[0087] Assemble the information display board 10 , the electrochromic device 20 and the control module 30 .

[0088] Making the electrochromic device 20 includes:

[0089] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0090] a. Magnetron sputtering fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 360nm;

[0091] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 200nm; W film is used as WO 3 a growth source for the nanowires;

[0092] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained pre...

Embodiment 3

[0107] Assemble the information display board 10 , the electrochromic device 20 and the control module 30 .

[0108] Making the electrochromic device 20 includes:

[0109] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0110] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film on the surface of tempered glass 1 with a specific size, with a thickness of about 340nm;

[0111] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 210nm; W film is used as WO 3 a growth source for the nanowires;

[0112] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a parking lot information display board capable of adjusting brightness and a manufacturing method thereof. Structures of electrochromic devices and manufacturing technology are improved, and the display board is characterized by self-energizing, so that the novel parking lot information display board which is short in response time, prolonged in life, and good in freezing tolerance performance is manufactured. The method is simple and easy in operation, and can be easily used in industrialized production.

Description

technical field [0001] The invention belongs to the traffic field, and more specifically relates to a parking lot information display board capable of automatically adjusting brightness and a manufacturing method thereof. Background technique [0002] The information display board is a plate-shaped medium used for information release and display. Specifically, the parking lot information display board can be used to display information such as the location of the parking lot, the number of vacancies, and the charging standard. Display cards generally have paper, metal and so on. [0003] However, under outdoor conditions, general parking lot display signs are not sensitive to light. Due to the influence of sunlight, etc., problems such as unclear display information will be caused, resulting in poor reading information for users. Contents of the invention [0004] Aiming at the problems existing in the background technology, the present invention provides a parking lot in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02F1/15G02F1/155
CPCG02F1/15G02F1/155
Inventor 肖白玉
Owner 肖白玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products