Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A non-stick coating, collagen hydrolyzate technology, applied in the coating field, can solve the problems of large friction coefficient, heat waste, low coating surface energy and so on
Inactive Publication Date: 2016-01-27
郭亚楠
View PDF0 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Now the coating formed by the coating has extremely low surface energy and a large friction coefficient, and is widely used in household appliances. However, the existing non-stick coatings generally have poor thermal insulation, which leads to better energy consumption and waste of heat.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
[0014] Non-stick coating, including collagen hydrolyzate 19g, polypropylene 8g, ethyl acetate 14g, methanol 27g, ethanol 12g, trimethylbenzene 22g, titanium dioxide 9g, sodium aluminosilicate 19g, aluminum oxide 11g, magnesium stearate 8g , 19g of iron oxide, 21g of ferric oxide, 14g of ammonium heptamolybdate and 57g of iron powder.
[0015] Among them, the iron powder is 120 mesh.
Embodiment 3
[0017] Non-stick coating, including collagen hydrolyzate 11g, polypropylene 7g, ethyl acetate 10g, methanol 21g, ethanol 9g, trimethylbenzene 18g, titanium dioxide 7g, sodium aluminosilicate 11g, aluminum oxide 9g, magnesium stearate 6g , 12g of iron oxide, 18g of ferric oxide, 10g of ammonium heptamolybdate and 51g of iron powder.
[0018] Among them, the iron powder is 110 mesh.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides non-stick paint. The non-stick paint is prepared from 5-19 g of collagen hydrolysate, 6-8 g of polypropylene, 9-14 g of ethyl acetate, 16-27 g of methyl alcohol, 8-12 g of ethyl alcohol, 4-22 g of trimethylbenzene, 4-9 g of titanium dioxide, 4-19 g of sodium silicoaluminate, 8-11 g of aluminum oxide, 5-8 g of magnesium stearate, 7-19 g of ferric oxide, 7-21 g of ferroferric oxide, 7-14 g of ammonium heptamolybdate and 6-57 g of iron powder. The size of the iron powder ranges from 50 meshes to 120 meshes. The iron powder is added to the paint, and the heat preservation performance of the paint can be remarkably improved. The iron powder is added to the paint, the heat preservation effect of the non-stick paint can be remarkably improved, energy is saved, consumption is reduced, other indexes of the non-stick paint are not affected, and use is more convenient.
Description
technical field [0001] The invention belongs to the field of coatings, in particular to non-stick coatings. Background technique [0002] Now the coating formed by the coating has extremely low surface energy and a large friction coefficient, and is widely used in household appliances. However, the existing non-stick coatings generally have poor thermal insulation, which leads to better energy consumption and waste of heat. . Contents of the invention [0003] The purpose of the present invention is to provide sticky paint, which has good thermal insulation, uses less materials and saves cost. [0004] Non-stick coating, including collagen hydrolyzate 5-19g, polypropylene 6-8g, ethyl acetate 9-14g, methanol 16-27g, ethanol 8-12g, trimethylbenzene 4-22g, titanium dioxide 4-9g, aluminosilicate Sodium 4-19g, aluminum oxide 8-11g, magnesium stearate 5-8g, iron oxide 7-19g, ferric oxide 7-21g, ammonium heptamolybdate 7-14g and iron powder 6-57g. [0005] Among them, the iron...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more