A kind of bimetallic catalyst for catalytic oxidation VOCs and its preparation method and application

A bimetallic catalyst and catalytic oxidation technology, which is applied in the field of resources and the environment, can solve the problems of transition metal oxide catalysis promotion and development obstacles, high reaction temperature, high energy consumption, etc., and achieve low cost, high catalytic activity and stable conversion rate Effect

Active Publication Date: 2017-12-12
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, studies have shown that supported Pd and Pt catalysts are mostly suitable for the catalytic oxidation of non-chlorinated VOCs, and more toxic high-chlorinated compounds will be generated when oxidizing chlorinated VOCs
Transition metal oxide catalysts have the advantages of low price, good thermal stability, and not easy to deactivate, but in general, due to their lower catalytic activity than noble metal catalysts, high reaction temperature, and high energy consumption, transition metal oxides The promotion and development of catalysis has brought some obstacles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bimetallic catalyst for catalytic oxidation VOCs and its preparation method and application
  • A kind of bimetallic catalyst for catalytic oxidation VOCs and its preparation method and application
  • A kind of bimetallic catalyst for catalytic oxidation VOCs and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] This example prepares a bimetallic catalyst for catalytic oxidation of VOCs, including a carrier, an active agent and a cocatalyst. The carrier is titanium dioxide, the activator is ruthenium, and the cocatalyst is tricobalt tetroxide. The percentage of the total mass is 1.0 wt%, and the atomic molar ratio of the ruthenium element in the active agent to the cobalt element in the cocatalyst is 1:5.

[0061] The preparation method of described catalyst is as follows (flow process is as follows figure 1 shown):

[0062] (1) Dissolve Salen ligand and cobalt acetate in ethanol (the molar ratio of Salen ligand to cobalt acetate is 1:1), and heat and stir at 50°C for 5 hours to obtain the coordinated single metal Organic compound ethanol solution (wherein the concentration of ethanol solution is 0.5g / mL).

[0063] (2) Ruthenium nitrosyl nitrate is added to the ethanol solution of the monometallic organic compound obtained in step (1) (wherein the mol ratio of ruthenium nitro...

Embodiment 2

[0067] In addition to the percentage of ruthenium element accounting for the total mass of the catalyst in the active agent is 0.2wt%, the atomic molar ratio of the ruthenium element in the activator and the cobalt element in the cocatalyst is 1:1, and in the step (1), the Salen ligand and cobalt acetate The mol ratio is 1:3, the concentration of the ethanol solution in the monometallic organic compound ethanol solution is 0.1g / mL, the ruthenium source described in step (2) is ruthenium trichloride, the mol ratio of ruthenium trichloride and cobalt acetate The concentration of titanium dioxide in the titanium dioxide slurry in step (3) is 1:1, except that the concentration of titanium dioxide in the slurry of titanium dioxide is 0.1 g / mL, the dosage of other materials and the preparation steps are the same as in Example 1.

[0068] The particle size of the bimetallic active particles of the obtained catalyst is 10nm, and when it catalyzes the simulated flue gas containing 1000p...

Embodiment 3

[0070] In addition to the percentage of ruthenium element accounting for the total mass of the catalyst in the active agent is 2wt%, the atomic molar ratio of the ruthenium element in the activator and the cobalt element in the cocatalyst is 1:10, the Salen ligand and cobalt acetate in the step (1) The mol ratio is 1:5, and the concentration of the ethanol solution in the monometallic organic compound ethanol solution is 1g / mL, and the mol ratio of ruthenium nitrosyl nitrate and cobalt acetate is 1:10 in the step (2), and titanium dioxide is 1:10 in the step (3). Except that the concentration of titanium dioxide in the slurry is 1g / mL, other material dosages and preparation steps are the same as in Example 1.

[0071]The particle size of the bimetallic active particles of the obtained catalyst is 10nm, and its complete oxidation temperature is 225°C, 210 °C and 215 °C, CO 2 Selectivity ≥ 99%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention provides a bimetallic catalyst for catalyzing and oxidizing VOCs, a preparation method and application thereof. The catalyst uses titanium dioxide as a carrier, the active agent is a simple substance and / or an oxide of any element in ruthenium, palladium or platinum, and the cocatalyst is any one of tricobalt tetroxide, manganese oxide, copper oxide or nickel oxide. Through nano-control means, Salen ligands are used to synthesize nanoparticles uniformly composited with active agents and co-catalysts. There is a strong synergistic catalytic effect between the two, which can improve the catalytic oxidation efficiency of VOCs. The catalyst of the present invention has high activity and strong universality. The complete oxidation temperature for various VOCs is between 160 and 230°C. It has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of resources and environment, and relates to a bimetallic catalyst for catalyzing and oxidizing VOCs and its preparation method and application, in particular to a nanometer-regulated bimetallic catalyst for catalyzing and oxidizing various VOCs, as well as its preparation method and application. Background technique [0002] Volatile organic compounds (VOCs) are a class of flammable and toxic organic compounds with high saturated vapor pressure and low water solubility, including alkanes, alkenes, aromatic hydrocarbons, alcohols, aldehydes, ketones, Halogenated, etc. VOCs come from a wide range of sources, such as petroleum refining, printing and packaging printing, fuel transportation and sales, architectural decoration, and cooking fumes. With the development of global industrialization, the leakage or direct discharge of these pollutants has caused certain harm to the ecological environment and human he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89B01J23/656B01J31/22B01D53/86B01D53/70B01D53/72
Inventor 朱廷钰刘霄龙曾俊淋施文博
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap